Fabrication of TiO2/Pt core–shell particles by electroless metal plating

Au-Ag/TiO2 Thin Films Preparation by Laser Ablation and Sputtering Plasmas for Its Potential Use as Photoanodes in Electrochemical Advanced Oxidation Processes (EAOP)

Titanium dioxide (TiO2) is widely used, studied, and synthesized using different methodologies. By a modification of the material, it can be applied to wastewater treatment. A combined sputtering-laser ablation setup was used to deposit TiO2 thin films modified, individually and simultaneously, with gold (Au) and silver (Ag). To investigate the effect of the metal incorporation in titanium and its impact on the photocatalytic activity, with dye discoloration as a pollutant compound model, the deposited films were characterized by UV–Vis, photoluminescence, and Raman spectroscopies, as well as by parallel beam X-ray diffraction. The results showed that films with different Au and Ag loads, and an 18 nm average crystallite size, were obtained. These metals have an essential effect on the deposited film’s compositional, structural, and optical properties, directly reflected in its photocatalytic activity. The photocatalytic test results using UV-Vis showed that, after 1 h of applying a 4.8 V electric voltage, a discoloration of up to 80% of malachite green (MG) was achieved, using ultraviolet (UV) light.

The pH dependent surface charging and points of zero charge. VII. Update

The pristine points of zero charge (PZC) and isoelectric points (IEP) of metal oxides and IEP of other materials from the recent literature, and a few older results (overlooked in previous searches) are summarized. This study is an update of the previous compilations by the same author [Surface Charging and Points of Zero Charge, CRC, Boca Raton, 2009; J. Colloid Interface Sci. 337 (2009) 439; 353 (2011) 1; 426 (2014) 209]. The field has been very active, but most PZC and IEP are reported for materials, which are very well-documented already (silica, alumina, titania, iron oxides). IEP of (nominally) Gd₂O₃, NaTaO₃, and SrTiO₃ have been reported in the recent literature. Their IEP were not reported in older studies.

Sensitive detection of hydrocarbon gases using electrochemically Pd-modified ZnO chemiresistors

Pristine and electrochemically Pd-modified ZnO nanorods (ZnO NRs) were proposed as active sensing layers in chemiresistive gas sensors for hydrocarbon (HC) gas detection (e.g., CH₄, C₃H_8, C₄H₁₀). The presence of Pd nanoparticles (NPs) on the surface of ZnO NRs, obtained after the thermal treatment at 550 °C, was revealed by morphological and surface chemical analyses, using scanning electron microscopy and X-ray photoelectron spectroscopy, respectively. The effect of the Pd catalyst on the performance of the ZnO-based gas sensor was evaluated by comparing the sensing results with those of pristine ZnO NRs, at an operating temperature of 300 °C and for various HC gas concentrations in the range of 30-1000 ppm. The Pd-modified ZnO NRs showed a higher selectivity and sensitivity compared to pristine ZnO NRs. The mean sensitivity of Pd-modified ZnO NRs towards the analyzed HCs gases increased with the length of the hydrocarbon chain of the target gas molecule. Finally, the evaluation of the selectivity revealed that the presence or the absence of metal nanoparticles on ZnO NRs improves the selectivity in the detection of specific HCs gaseous molecules.