Adsorptive removal of carbon dioxide using polyethyleneimine loaded glass fiber in a fixed bed

CO2 Adsorption Capacity of Organic Alkali Sorbent CPEI from Polyethyleneimine

Support-free cross-linked polyethyleneimine sorbent (CPEI) for CO2 capture was evaluated as the regenerable sorbent. The total amines available for the CO2 capture on CPEI were determined by the polyethyleneimine/glutaraldehyde ratio for the synthesis of CPEI. The CO2 capacity of CPEI in the slurry bubble column reactor reached 4.92 mmol/g, which is 1.97 times higher than that obtained under anhydrous conditions. The adsorption kinetics of CPEI in the reactor were investigated in terms of the CPEI amount, the CO2 fraction, the gas flow rate, temperature, and the total amines available. The experimental breakthrough curves for the sorbent were well-fitted with a fractional-order kinetic model. The modeling analysis found the influence of diffusion resistance on the adsorption is more significant than that of the driving force. The CO2 capacity of CPEI remained almost constant during the temperature swing adsorption/desorption cycles.

The Use of Conductive Polymers Embedded Macro Porous Pei and Ionic Liquid Form of Pei Cryogels for Potential Conductometric Sensor Application to CO2

Polyethyleneimine (PEI) cryogels with interconnected superporous morphology were synthesized via the cryopolymerization technique. Then, conductive polymers, poly(Aniline) (PANi), poly(Pyrrole) (PPy), and poly(Thiophene) (PTh) were prepared within these PEI cryogels. Then, the conductive polymer embedding PEI composites’ characterization was carried morphologically using scanning electron microscope (SEM) by means of Fourier Transform Infrared Radiation (FT-IR) spectrometer, and by means of electrical conductivity measurements using an electrometer. Among all the prepared cryogel conductive polymer composites, the highest value in terms of conductivity was determined for PEI/PANi cryogel composites with 4.80 × 10−3 S.cm−1. Afterward, to prepare polymeric ionic liquid (PIL) forms of PEI and PEI/PANi composites. To assess the effect of anions on the conductivities of the prepared composites, PEI-based cryogels were anion ex-changed after protonation with HCl by treatment of aqueous solutions of sodium dicyanamide (Na+[N(CN)2]−), ammonium hexafluorophosphate (NH4+[PF6]−), sodium tetrafluoroborate (Na+[BF4]−), and potassium thiocyanate (K+[SCN]−), separately. Furthermore, PEI-based cryogel composites and their PIL forms were tested as a sensor for CO2 gas. The higher conductivity changes were observed on bare PEI cryogel and PEI+[BF4]− PIL cryogels with 1000-fold decrease on conductivity upon 240 min CO2 exposure. The sensitivity and recovery percent of bare PEI and PEI+[BF4]− PIL cryogels were shown almost the same with a two-fold decrease in the presence of 0.009 mole of CO2 gas, and approximately 30% recovery after the fifth consecutive reuse.

Fabricating Fibers of a Porous-Polystyrene Shell and Particle-Loaded Core

Polystyrene (PS) polymers have broad applications in protective packaging for food shipping, containers, lids, bottles, trays, tumblers, disposable cutlery and the making of models. Currently, most PS products, such as foams, are not accepted for recycling due to a low density in the porous structure. This poses a challenge for logistics as well as creating a lack of incentive to invest in high-value products. This study, however, demonstrated the use of a dry-jet wet-spinning technique to manufacture continuous PS fibers enabled by an in-house designed and developed spinning apparatus. The manufactured fibers showed porosity in the shell and the capability to load particles in their core, a structure with high potential use in environmentally relevant applications such as water treatment or CO2 collections. A two-phase liquid-state microstructure was first achieved via a co-axial spinneret. Following coagulation procedures and heat treatment, phase-separation-based selective dissolution successfully generated the porous-shell/particle-core fibers. The pore size and density were controlled by the porogen (i.e., PEG) concentrations and examined using scanning electron microscopy (SEM). Fiber formation dynamics were studied via rheology tests and gelation measurements. The shell components were characterized by tensile tests, thermogravimetric analysis, and differential scanning calorimetry for mechanical durability and thermal stability analyses.