A facile approach for fabrication of TiO2 hierarchical nanostructures and their photocatalytic properties

Biomorphic Fibrous TiO2 Photocatalyst Obtained by Hydrothermal Impregnation of Short Flax Fibers with Titanium Polyhydroxocomplexes

A biomimetic solution technology for producing a photocatalytic material in the form of biomorphic titanium oxide fibers with a hierarchical structure using short flax fiber as a biotemplate is proposed. The impregnation of flax fibers intensified under hydrothermal conditions with a precursor was performed in an autoclave to activate the nucleation of the photoactive TiO2 phases. The interaction between precursor and flax fibers was studied by using infrared spectroscopy (IR) and differential scanning calorimetry/thermogravimetry analysis (DSC/TG). The morphology, structure, and textural properties of the TiO2 fibers obtained at annealing temperatures of 500–700 °C were determined by X-ray diffraction analysis, scanning electron microscopy, and nitrogen adsorption/desorption. It is shown that the annealing temperature of the impregnated biotemplates significantly affects the phase composition, crystallite size, and porous structure of TiO2 fiber samples. The photocatalytic activity of the obtained fibrous TiO2 materials was evaluated by using the decomposition of the cationic dye Rhodamine B in an aqueous solution (concentration 12 mg/L) under the influence of ultraviolet radiation (UV). The maximum photodegradation efficiency of the Rhodamine B was observed for TiO2 fibers annealed at 600 °C and containing 40% anatase and 60% rutile. This sample ensured 100% degradation of the dye in 20 min, and this amount significantly exceeds the photocatalytic activity of the commercial Degussa P25 photocatalyst and TiO2 samples obtained previously under hydrothermal conditions by the sol-gel method.

Photodegradation of some brominated and phenolic micropollutants in raw hospital wastewater with CeO2 and TiO2 nanoparticles

In this study, the degradations of 2,3,4,5,6-pentabromotoluene (PBT), 2,3,4,5,6-pentabromoethyl benzene (PBEB), triclosan (TCS) and gemfibrozil (GFZ) in raw hospital wastewater were investigated with cerium (IV) oxide and titanium (IV) oxide nanoparticles considering the mechanisms of adsorption, photolysis, and photocatalysis with UV-C lamps. The effects of nano-CeO₂ and nano-TiO₂ concentrations, irradiation times, UV light powers and hospital wastewater pH on the photodegradation yields of micropollutants namely PBT, PBEB, TCS and GFZ were investigated throughout photocatalysis. The nano-TiO₂ produced had an anatase phase with crystalline shape with a surface area of 205 m² g^-1 and an average size of 11.50 nm. The CeO₂ nanoparticles had a spherical shape with a higher surface area (302 m² g^-1) than that of TiO₂ and a lower average size (8.11 nm). It was found that the removals of PBT, PBEB, TCS and GFZ with adsorption (5.7%-17.1%) and photolysis (9.0%-15.9%) were not significant for both nanoparticles. The photodegradation of PBT (92%), PBEB (90%), TCS (97%) and GFZ (95%) with nano-CeO₂ gave better results than nano-TiO₂ (90%, 87%, 94% and 93% for PBT, PBEB, TCS and GFZ, respectively) under optimum experimental conditions (0.50 g L^-1 nano-CeO_2, 45 min irradiation time, 25 °C temperature, pH = 8.50, 210 W UV light power). Both nanoparticles were reused effectively after photo-removals of the micropollutants from the hospital wastewater. The lowest photodegradation yields were 80%, 78%, 75% and 74% for TCS, GFZ, PBT and PBEB, respectively, with nano-TiO₂ after six sequential treatments. The lowest photodegradation yields were 86%, 83%, 80% and 79% for the same micropollutants, respectively, with nano-CeO₂ after six sequential treatments. The cost to treat 1 m³ raw hospital wastewater were 8.70 € and 2.28 €, for the photocatalytic treatments with nano-TiO₂ and nano-CeO₂, respectively.