Film formation process of natural rubber latex particles: roles of the particle size and distribution of non-rubber species on film microstructure

Hevea brasiliensis rubber particles' fluid interfaces reveal size impact on early coagulation steps

Natural rubber originates from the coagulation of rubber particles (RP) from Hevea brasiliensis latex. The size distribution of Hevea RP is bimodal with the presence of small rubber particles (SRP) and large rubber particles (LRP). This study aims at getting a better understanding of the early coagulation steps of Hevea RP taking into account the particle size. SRP and LRP were obtained by centrifugation of freshly tapped ammonia-free latex from RRIM600 clone. Size and zeta potential measurements showed that both RP fractions were efficiently separated and stable in basic buffer. SRP and LRP dispersions were placed in a Langmuir trough and RP were let to adsorb at the air-liquid interface to form interfacial films. Surface tension and ellipsometry indicate that the formation kinetics and the stabilization of the film at the air-liquid interface are faster for SRP than LRP. Moreover, the arrangement of RP at the interface differs between SRP and LRP, as shown by Brewster angle microscopy, atomic force microscopy and confocal laser scanning microscopy. First, the RP membrane and cis-1,4-polyisoprene core spread at the air-liquid interface before clustering. Then, while the SRP fuse, the LRP keep their structure in individual particles in floating aggregate. The role of the non-isoprene molecules on the different organization of SRP and LRP films is discussed, the one of the two major RP proteins, SRPP1 (Small Rubber Particle Protein) and Rubber Elongation Factor (REF1) in the early coagulation steps.

Multifunctional Aspects of Mechanical and Electromechanical Properties of Composites Based on Silicone Rubber for Piezoelectric Energy Harvesting Systems

Energy harvesting systems fabricated from rubber composite materials are promising due to their ability to produce green energy with no environmental pollution. Thus, the present work investigated energy harvesting through piezoelectricity using rubber composites. These composites were fabricated by mixing titanium carbide (TiC) and molybdenum disulfide (MoS2) as reinforcing and electrically conductive fillers into a silicone rubber matrix. Excellent mechanical and electromechanical properties were produced by these composites. For example, the compressive modulus was 1.55 ± 0.08 MPa (control) and increased to 1.95 ± 0.07 MPa (6 phr or per hundred parts of rubber of TiC) and 2.02 ± 0.09 MPa (6 phr of MoS2). Similarly, the stretchability was 133 ± 7% (control) and increased to 153 ± 9% (6 phr of TiC) and 165 ± 12% (6 phr of MoS2). The reinforcing efficiency (R.E.) and reinforcing factor (R.F.) were also determined theoretically. These results agree well with those of the mechanical property tests and thus validate the experimental work. Finally, the electromechanical tests showed that at 30% strain, the output voltage was 3.5 mV (6 phr of TiC) and 6.7 mV (6 phr of MoS2). Overall, the results show that TiC and MoS2 added to silicone rubber lead to robust and versatile composite materials. These composite materials can be useful in achieving higher energy generation, high stretchability, and optimum stiffness and are in line with existing theoretical models.

Influence of Clones on Relationship between Natural Rubber and Size of Rubber Particles in Latex

IAN873, Dongfang93114 and Reyan73397, created through vegetative propagation for their high yield and excellent cold resistance, are major clones planted in China. In this work, latexes with rubber particles of the same size from these clones are separated from fresh natural rubber latex, and corresponding rubber films are prepared from each latex. The structure and components of each film are measured. This indicates that the characteristics of the rubbers obtained from latexes with similar particle sizes show some resembling trends among different clones, while for specific samples, those characteristics vary depending on the clone. The molecular weight is generally highest in IAN873 and lowest in Reyan73397. Rubber chains in small rubber particles are longer, and large rubber particles show a wider molecular weight distribution. The gel content of every sample from Reyan73397 is lower than the other two clones. The nitrogen content increases with the size of rubber particles in all clones. The ester content of small rubber particles in IAN873 and Reyan73397 is almost zero. Large rubber particles have more branching points formed via esters. This study provides a new perspective on the influence of clones on the relationship between characteristics of natural rubber and the size of rubber particles in natural rubber latex.