Study on mechanism of a simple method to regulate salt tolerance of hydrophobically associating water-soluble polymers

An Exceptionally Salt Tolerant Copoly(Maleimide Sulfobetaine) - Structural Requirements for Ultra-Salt Tolerance

Zwitterionic polymers are an important class of polymers with far-ranging applications. In the widely studied poly(meth)acrylate and poly(meth) acrylamide-based zwitterions, properties can be tuned by changing the nature of substituents attached to ammonium ions. However, these changes influenced salt tolerance of zwitterionic polymers only to a limited extent. Upon adding salt these polymers expanded in solution initially. Further increase in salt concentration caused the polymer chains to shrink similar to the common water soluble, uncharged polymers thereby deteriorating the viscosity of aqueous solutions. In contrast to the conventional poly(meth)acrylate and poly(meth)acrylamide-based zwitterions, zwitterionic copolymaleimides showed substituent dependent salt-tolerant nature. In the absence of any substituent on the polymer backbone such as zwitterionic poly(ethylene-alt-maleimide) (ZI-PEMA) the viscosity of salt solutions increased both with the increasing salt concentration as well as the concentration of polymer. This is likely due to the continuous expansion of polymer coil in salt solutions with increasing salt concentration caused primarily by the rigidity of the polymer backbone. ZI-PEMA also enhanced the saturation limit of mono- and divalent salts like sodium chloride and hydrated calcium bromide in water. This property is useful for various applications like fish curing, for making high-density fluids, refrigeration, etc. across various industrial sectors.

Fracturing Fluid Polymer Thickener with Superior Temperature, Salt and Shear Resistance Properties from the Synergistic Effect of Double-Tail Hydrophobic Monomer and Nonionic Polymerizable Surfactant

To develop high-salinity, high-temperature reservoirs, two hydrophobically associating polymers as fracturing fluid thickener were respectively synthesized through aqueous solution polymerization with acrylamide (AM), acrylic acid (AA), 2-acrylamido-2-methylpropanesulfonic acid (AMPS), nonionic polymerizable surfactant (NPS) and double-tail hydrophobic monomer (DHM). The thickener ASDM (AM/AA/AMPS/NPS/DHM) and thickener ASD (AM/AA/AMPS/DHM) were compared in terms of properties of water dissolution, thickening ability, rheological behavior and sand-carrying. The results showed that ASDM could be quickly diluted in water within 6 min, 66.7% less than that of ASD. ASDM exhibited salt-thickening performance, and the apparent viscosity of 0.5 wt% ASDM reached 175.9 mPa·s in 100,000 mg/L brine, 100.6% higher than that of ASD. The viscosity of 0.5 wt% ASDM was 85.9 mPa·s after shearing for 120 min at 120 °C and at 170 s^-1, 46.6% higher than that of ASD. ASDM exhibited better performance in thickening ability, viscoelasticity, shear recovery, thixotropy and sand-carrying than ASD. The synergistic effect of hydrophobic association and linear entanglement greatly enhancing the performance of ASDM and the compactness of the spatial network structure of the ASDM was enhanced. In general, ASDM exhibited great potential for application in extreme environmental conditions with high salt and high temperatures.