Constructing SrCO3/SrTiO3 nanocomposites with highly selective photocatalytic CO2-to-CO reduction

In Situ Reconstruction of Active Heterointerface for Hydrocarbon Combustion through Thermal Aging over Strontium-Modified Co3O4 Nanocatalyst with Good Sintering Resistance

The issue of catalyst deactivation due to sintering has gained significant attention alongside the rapid advancement of thermal catalysts. In this work, a simple Sr modification strategy was applied to achieve highly active Co3O4-based nanocatalyst for catalytic combustion of hydrocarbons with excellent antisintering feature. With the Co1Sr0.3 catalyst achieving a 90% propane conversion temperature (T90) of only 289 °C at a w8 hly space velocity of 60,000 mL·g-1·h-1, 24 °C lower than that of pure Co3O4. Moreover, the sintering resistance of Co3O4 catalysts was greatly improved by SrCO3 modification, and the T90 over Co1Sr0.3 just increased from 289 to 337 °C after thermal aging at 750 °C for 100 h, while that over pure Co3O4 catalysts increased from 313 to 412 °C. Through strontium modification, a certain amount of SrCO3 was introduced on the Co3O4 catalyst, which can serve as a physical barrier during the thermal aging process and further formation of Sr-Co perovskite nanocrystals, thus preventing the aggregation growth of Co3O4 nanocrystals and generating new active SrCoO2.52-Co3O4 heterointerface. In addition, propane durability tests of the Co1Sr0.3 catalysts showed strong water vapor resistance and stability, as well as excellent low-temperature activity and resistance to sintering in the oxidation reactions of other typical hydrocarbons such as toluene and propylene. This study provides a general strategy for achieving thermal catalysts by perfectly combining both highly low-temperature activity and sintering resistance, which will have great significance in practical applications for replacing precious materials with comparative features.

Research Progress on Photocatalytic CO2 Reduction Based on Perovskite Oxides

Photocatalytic CO2 reduction to valuable fuels is a promising way to alleviate anthropogenic CO2 emissions and energy crises. Perovskite oxides have attracted widespread attention as photocatalysts for CO2 reduction by virtue of their high catalytic activity, compositional flexibility, bandgap adjustability, and good stability. In this review, the basic theory of photocatalysis and the mechanism of CO2 reduction over perovskite oxide are first introduced. Then, perovskite oxides' structures, properties, and preparations are presented. In detail, the research progress on perovskite oxides for photocatalytic CO2 reduction is discussed from five aspects: as a photocatalyst in its own right, metal cation doping at A and B sites of perovskite oxides, anion doping at O sites of perovskite oxides and oxygen vacancies, loading cocatalyst on perovskite oxides, and constructing heterojunction with other semiconductors. Finally, the development prospects of perovskite oxides for photocatalytic CO2 reduction are put forward. This article should serve as a useful guide for creating perovskite oxide-based photocatalysts that are more effective and reasonable.

Construction of N-Doped Carbon-Modified Ni/SiO2 Catalyst Promoting Cinnamaldehyde Selective Hydrogenation

At present, the selective hydrogenation of α, β-unsaturated aldehydes remains a challenge due to competition between unsaturated functional groups (C=C and C=O). In this study, N-doped carbon deposited on silica-supported nickel Mott-Schottky type catalysts (Ni/SiO₂@N_xC) was prepared for the selective hydrogenation of cinnamaldehyde (CAL) by using the respective hydrothermal method and high-temperature carbonization method. The prepared optimal Ni/SiO₂@N₇C catalyst achieved 98.9% conversion and 83.1% selectivity for 3-phenylpropionaldehyde (HCAL) in the selective hydrogenation reaction of CAL. By constructing the Mott-Schottky effect, the electron transfer from metallic Ni to N-doped carbon at their contact interface was promoted, and the electron transfer was demonstrated by XPS and UPS. Experimental results indicated that by modulating the electron density of metallic Ni, the catalytic hydrogenation of C=C bonds was preferentially performed to obtain higher HCAL selectivity. Meanwhile, this work also provides an effective way to design electronically adjustable type catalysts for more selective hydrogenation reactions.

Role of SrCO3 on Photocatalytic Performance of SrTiO3-SrCO3 Composites

Perovskites such as SrTiO3 are interesting for photocatalytic applications due to their structure-related and electronic properties. These properties are influenced by the presence of SrCO3 which is often formed simultaneously during the hydrothermal synthesis of SrTiO3. In this study, SrTiO3-SrCO3 composites with different contents of SrCO3 (5–24 wt%) were synthesized. Their morphological, structural, and optical properties were investigated using complementary methods such as scanning electron microscopy (SEM), X-ray diffraction (XRD), nitrogen sorption, and diffuse reflectance spectroscopy (DRS). Their photocatalytic activity was assessed during the degradation of diclofenac (DCFNa) in aqueous solution and CO2 photoreduction under Xe lamp irradiation. Improved photocatalytic efficiency in DCFNa degradation was observed for all the studied composites in comparison with SrTiO3, and the highest mineralization efficiency was obtained for the sample with 21 wt% SrCO3 content. The presence of SrCO3 led to an increased concentration of active species, such as •OH radicals. Otherwise, its presence inhibits CH4 and C2H6 production during CO2 photoreduction compared with pure SrTiO3.