Synthesis and characterization of monosize magnetic poly(glycidyl methacrylate) beads

Poly(glycidyl methacrylate)-functionalized magnetic nanoparticles as platforms for linking functionalities, bioentities and organocatalysts

Magnetic nanoparticles coated with polyglycidyl methacrylate are ring-opened by nucleophiles containing reactive centers, bioentities, organocatalysts leading to new materials.

A new morphological approach for removing acid dye from leather waste water: preparation and characterization of metal-chelated spherical particulated membranes (SPMs)

In this study, p(HEMA-GMA) poly(hydroxyethyl methacrylate-co-glycidyl methacrylate) spherical particulated membranes (SPMs) were produced by UV-photopolymerization and the synthesized SPMs were coupled with iminodiacetic acid (IDA). Finally the novel SPMs were chelated with Cr(III) ions as ligand and used for removing acid black 210 dye. Characterizations of the metal-chelated SPMs were made by SEM, FTIR and swelling test. The water absorption capacities and acid dye adsorption properties of the SPMs were investigated and the results were 245.0, 50.0, 55.0 and 51.9% for p(HEMA), p(HEMA-GMA), p(HEMA-GMA)-IDA and p(HEMA-GMA)-IDA-Cr(III) SPMs respectively. Adsorption properties of the p(HEMA-GMA)-IDA-Cr(III) SPMs were investigated under different conditions such as different initial dye concentrations and pH. The optimum pH was observed at 4.3 and the maximum adsorption capacity was determined as 885.14 mg/g at about 8000 ppm initial dye concentration. The concentrations of the dyes were determined using a UV/Vis Spectrophotometer at a wavelength of 435 nm. Reusability of p(HEMA-GMA)-IDA-Cr(III) SPMs was also shown for five adsorption-desorption cycles without considerable decrease in its adsorption capacity. Finally, the results showed that the metal-chelated p(HEMA-GMA)-IDA SPMs were effective sorbent systems removing acid dye from leather waste water.

Facile Synthesis of Magnetic Copolymer Microspheres Based on Poly(glycidyl methacrylate-co-N-isopropylacrylamide)/Fe3O4by Suspension Photopolymerization

Magnetic copolymer based on poly(glycidyl methacrylate-co-N-isopropylacrylamide) microspheres was prepared by 2,2-dimethoxy-2-phenylacetophenone- (DMPP-) photo initiated and poly(vinyl alcohol)- (PVA-) stabilized single step suspension photopolymerization. The effect of chemical interaction, morphology, and thermal properties by adding 0.1% w/v Fe3O4in the copolymer was investigated. Infrared analysis (FTIR) showed that (C=C) band disappeared after copolymerization, indicating that the magnetic copolymer microspheres were successfully synthesized and two important bands at 908 cm−1and 1550 cm−1appear. These are associated with the epoxy group stretching of GMA and secondary amide (N–H/C–H) deformation vibration of NIPAAm in magnetic microspheres. The X-ray diffraction (XRD) result proved the incorporation of Fe3O4nanoparticles with copolymer microspheres as peak of Fe3O4was observed. Morphology study revealed that magnetic copolymer exhibited uniform spheres and smoother appearance when entrapped with Fe3O4nanoparticles. The lowest percentage of Fe3O4nanoparticles leached from the copolymer microspheres was obtained at pH 7. Finally, thermal property of the copolymer microspheres was improved by adding a small amount of Fe3O4nanoparticles that has been shown from the thermogram.

Monosize microbeads for pseudo-affinity adsorption of human insulin

Affinity adsorption technique is increasingly used for protein purification, separation and other biochemical applications. Therapeutic molecules such as antibodies, cytokines, therapeutic DNA and plasma proteins must be purified before characterization and utilization. The aim of this study was to prepare micronsized spherical polymeric beads and to investigate the extent of their human insulin adsorption capability. Monosize poly(ethylene glycol dimethacrylate-N-methacryloyl-(L)-histidine) [poly(EDMA-MAH)] beads were prepared by modified suspension copolymerization. Functional monomer (MAH) was synthesized using methacryloyl chloride and L-histidine. The beads were characterized using scanning electron microscopy (SEM), Fourier transform infrared spectroscopy, swelling test and elemental analysis. MAH incorporation into monosize polymeric beads, having an average size around 2-3 μm, was estimated as 55.3 μmol MAH/g bead. Equilibrium swelling ratios of poly(EDMA-MAH) and poly(EDMA) beads were 65% and 55%, respectively. Adsorption experiments were performed under different conditions (i.e., pH, temperature, protein concentration and ionic strength). It was found that adsorption characteristics are strongly depend on these conditions. Maximum insulin adsorption capacity was achieved as 24.7 mg insulin/g poly(EDMA-MAH) beads. Results were well fitted to the Langmuir isotherm model. Compared with poly(EDMA-MAH), nonspecific insulin adsorption onto poly(EDMA) beads was very low (0.61 mg insulin/g bead) and can be negligible. It was observed that insulin could be repeatedly adsorbed and desorbed (at least 10 times) without significant loss in adsorption capacity.