Comparative corrosion resistance properties between (Cu, Ce)-DLC and Ti co-doped (Cu, Ce)/Ti-DLC films prepared via magnetron sputtering method

Optimizing gas pressure for enhanced tribological properties of DLC-coated graphite

In this study, for the first time, the optimization of applied pressure for achieving the one of the best tribological properties of diamond-like carbon (DLC) coating on graphite surface using plasma-enhanced chemical vapor deposition (PECVD) method was investigated. Raman spectroscopy and microscopy methods were used to characterize the applied coating. Additionally, the mechanical properties of the coating were investigated through nanoindentation testing. The wear resistance of coating has been tested as functional test. The results indicated that with increasing gas pressure, the sp3 hybridization percentage decreases, while the ID/IG ratio increases. The average roughness values for the uncoated sample and the coated samples at working pressures of 25, 30, and 35 mTorr were obtained as 1.6, 5.1, 3, and 2.4 nm, respectively. The results of hardness and wear tests showed that these properties were optimized by reducing the applied gas pressure. The highest hardness was 11.59 GPa, and the best sample in terms of the mechanical properties of the coating was the sample applied at a gas pressure of 25 mTorr. Results show that the optimal sample in tribological performance is the one applied at a working pressure of 25 mTorr. Because this sample demonstrates the lowest coefficient of friction, and wear depth.

Tribological Characteristics of a-C:H:Si and a-C:H:SiOx Coatings Tested in Simulated Body Fluid and Protein Environment

This paper presents the tribological properties of silicon and oxygen incorporated diamond-like carbon coatings tested in simulated body fluid and bovine serum albumin environments. The tests were performed using a ball-on-disc tribometer with an AISI316L steel counterbody. The wear tracks and wear scars were analyzed using optical microscopy and a nanoindenter. The interaction between the coating and the working environment was analyzed by Fourier transform infrared spectroscopy, whereas changes in the chemical structure before and after the tribological tests were compared with the use of Raman spectroscopy. Our study showed that the tribological parameters are governed by the presence of oxygen rather than the changing concentration of silicon. Both of the spectroscopy results confirm this statement, indicating that coatings with low concentrations of silicon and oxygen appear to be better candidates for biological applications in terms of wear resistance.

Comparative Investigation on Corrosion Resistance of Stainless Steels Coated with Titanium Nitride, Nitrogen Titanium Carbide and Titanium-Diamond-like Carbon Films

In this study, the corrosion resistance of titanium nitride (TiN), nitrogen titanium carbide (TiCN) and titanium-diamond-like carbon (Ti-DLC) films deposited on 316L stainless steel (SS) were compared via differences in the surface and section-cross morphologies, open circuit potential tests, electrochemical impedance spectroscopy and potentiometric tests. The corrosion resistance of the TiCN and Ti-DLC films significantly improved because of the titanium carbide (TiC) crystals that obstruct the corrosive species penetrating the as-deposited film in the electrolyte atmosphere. TiN exhibited the lowest corrosion resistance because of its low thickness and high volume of defects. The Ti-DLC film showed the lowest corrosion current density (approximately 4.577 μA/cm2) and thickness reduction (approximately 0.12 μm) in different electrolytes, particularly those with high Cl− and H+ concentrations, proving to be the most suitable corrosion protection material for 316L SS substrates.