Realization of tricolor luminescence from novel Sr5Al2O8:Sm3+, Er3+& Dy3+ nanomaterials for advanced photonic applications

Crystal Chemistry and Photoluminescent Aspects of Bright Orange Light Emitting Sm3+- Activated Ba2BiV3O11 Nanomaterials for Advanced Illuminating Applications

In the present system, Sm3+ activated Ba2BiV3O11 nanomaterial series radiating orange-red light was developed via an efficient approach of solution combustion method. The structural examinations using XRD analysis indicate that the sample is crystallized into the monoclinic phase with the P21/a (14) space group. The elemental composition and morphological conduct were studied via energy dispersive spectroscopy (EDS) and scanning electron microscopy (SEM) respectively. Also, the formation of nanoparticles was confirmed by transmission electron microscopy (TEM). Photoluminescent (PL) examinations reveal the orange-red emission from the developed nanocrystals via documenting the emission spectra, which reveals the peak at 606 nm due to the 4G5/2 → 6H7/2 transition. Further, the decay time, non-radiative rates, quantum efficiency, and band gap of the optimal sample were computed as 1.3263 ms, 219.5 s- 1, 70.88%, and 3.41 eV respectively. Finally, the chromatic parameters including color - coordinates (0.5565, 0.4426), 1975 K color correlated temperature (CCT), and color purity (85.58%) reflected their excellent luminous performance. The above-mentioned outcomes endorsed the relevancy of the developed nanomaterials as a propitious agent in the engineering of advanced illuminating optoelectronic appliances.

Synthesis, photoluminescence, Judd-Ofelt analysis, and thermal stability studies of Dy3+-doped BaLa2ZnO5 phosphors for solid-state lighting applications

Here, we report a series of white-emitting Ba(La_2-x Dy _x )ZnO₅ (x = 0-7 mol%) phosphors synthesized via a high-temperature solid-state reaction. The synthesized phosphor's phase purity and tetragonal crystal structure were confirmed by an X-ray powder diffraction (XRPD) pattern. The wide bandgap characteristic feature was assessed through reflectance spectra, and the estimated bandgap was found to be 4.70 eV. Besides analyzing the effect of doping on the surface morphology, the distribution of ions on the surface was observed through the secondary ion mass spectroscopy technique. The synthesized phosphor was found to display bluish (486 nm) and yellowish (576 nm) bands in the emission spectra under the excitation of 325 nm and 352 nm, which together are responsible for producing the white luminescence. The analysis of Judd-Ofelt parameters indicates the symmetric nature of Dy³⁺ substitution in the present host. The thermal stability of the phosphor was assessed by varying the temperature up to 403 K, and it was found that the synthesized phosphor possesses improved thermal stability with an activation energy of 0.29 eV. The photometric evaluations of the present phosphor revealed the CIE coordinates around the near-white regime (0.3448, 0.3836), along with the color-correlated temperature value of 5102 K. All research on this luminescent material's unique features points to the possibility of using it to fabricate white-light-emitting devices for solid-state lighting applications.

Synthesis of cool white light emitting novel dysprosium (Dy3+ ) complexes with tetradentate β-ketoamide and heterocyclic auxiliary ligands

To improve current multiphase white light emitting diodes (WLEDs), a novel series of five complexes consisting of one binary and four ternary complexes that emitted cool white light was successfully synthesized using a chelating tetradentate ligand and auxiliary ligands, i.e. 5,6-dimethyl-1,10-phenanthroline, 1,10-phenanthroline, 4,4'-dimethyl-2,2'-bipyridyl, and 2,2'-bipyridyl. The series was examined structurally using elemental analysis, Fourier transform infrared spectroscopy, energy dispersive X-ray analysis, ultraviolet-visible spectroscopy, and proton nuclear magnetic resonance spectroscopy. These complexes had the appropriate thermal stability required for the generation of white organic LEDs (WOLEDs). Dysprosium (III) (Dy³⁺ ) ion complexes demonstrated the characteristic emission peaks of blue colour at 482 nm and yellow colour at 572 nm, respectively, when excited using near ultraviolet light. Band gap, refractive index, and decay lifetime of the optimized samples were recorded as 2.68 eV, 2.12, and 1.601 ms, respectively. Correlated colour temperature value (7875 K), Commission International de l'Eclairage coordinates (0.300, 0.294), and colour purity (21.04 × 10^-2 ) of the optimized complex were near to those of white illuminants as defined by the National Television System Committee. These complexes had promise as commercial LEDs for the advanced optoelectronics devices, especially as WOLEDs for illumination applications.