Synthesis and characterization of polyaniline/nickel oxide composites for fuel additive and dyes reduction

Chitosan-sunflower meal biochar hydrogel incorporated with green synthesized NiO nanoparticles for enhanced catalytic reduction of anthropogenic water pollutants

Anthropogenic activities have been one of the crucial driving factors for water pollution globally, thereby warranting a sustainable strategy for its redressal. In this study, we have developed a hydrogel-biochar nanocomposite for catalytic reduction of water pollutants. To begin with, green synthesis of nickel oxide nanoparticles (NiO NPs) was accomplished from waste kinnow peel extract via the environmentally benign microwave method. The formation of NiO NPs was affirmed from different analytical techniques namely ultraviolet-visible (UV-Vis), Fourier transform infrared (FTIR), X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and energy-dispersive spectroscopy (EDS). The FESEM images revealed spherical nature of NiO NPs. The average particle size was found to be 15.61 nm from XRD data. A novel hydrogel-biochar nanocomposite comprising the green NiO NPs, sunflower meal biochar and chitosan was prepared (Cs-biochar@ NiO) and explored as a nanocatalyst towards catalytic reduction of pollutants such as 4-nitrophenol, potassium hexacyanoferrate (III) and organic dyes methyl orange (MO), Congo red (CR), methylene blue (MB) in the presence of a reducing agent, i.e. NaBH4. Under optimized conditions, the reduction reactions were completed by 120 s and 60 s for 4-NP and potassium hexacyanoferrate (III) respectively and the rate constants were estimated to be 0.044 s-1 and 0.110 s-1. The rate of reduction was found to be faster for the dyes and the respective rate constants were 0.213 s-1 for MO, 0.213 s-1 for CR and 0.135 s-1 for MB. The assessment of the nanocatalyst in the reduction of binary dye systems depicted its selectivity towards the anionic dyes CR and MO. The nanocatalyst displayed effective reduction of dyes in real-water samples collected from different sources. Taken altogether, this study validates the design of sustainable hydrogel-biochar nanocatalyst for the efficient reduction of hazardous anthropogenic water pollutants.

Rapid catalytic reduction of environmentally toxic azo dye pollutant by Prussian blue analogue nanocatalyst

The release of toxic azo dyes pollutants in the environment from different industries represents a public health concern and a serious environmental problem. Therefore, the conversion of hazardous methyl orange (MO) azo dye to environmentally benign products is a critical demand. In this work, an eco-friendly Prussian blue analogue (PBA) was synthesized and its catalytic activity toward the reduction of MO was investigated. The PBA copper(ii) hexacyanocobaltate(III) (Cu3[Co(CN)6]2) was synthesized by a facile inexpensive chemical coprecipitation method without using hazardous solvents. The nanocatalyst was characterized using XPS, Raman, FTIR spectroscopy, and XRD. The chemical reduction of MO using NaBH4 and the PBA as nanocatalyst was monitored by UV-VIS spectroscopy. Toxic MO was completely reduced in 105 s with a rate constant (k) 0.0386 s-1 using only 10 μg of the PBA nanocatalyst. Besides the powerful catalytic activity, the nanocatalyst also showed excellent stability and recyclability for ten consecutive cycles, with no significant decrease in the catalytic performance. Therefore, the proposed PBA is a promising, stable, cost-effective, and eco-friendly nanocatalyst for the rapid elimination of hazardous azo dyes.

Facile Synthesis of Vanadium Oxide/Carbon Spheres-Doped Nickel Oxide Functioned as a Nanocatalyst and Bactericidal Behavior with Molecular Docking Analysis

Vanadium oxide (V₂O₅) and carbon spheres (Cs)-doped NiO₂ nanostructures (NSs) were prepared using the co-precipitation approach. Several spectroscopic and microscopic techniques, including X-ray diffraction (XRD), UV-vis, FTIR, TEM, and HR-TEM investigations, were used to describe the as-synthesized NSs. The XRD pattern exhibited the hexagonal structure, and the crystallite size of pristine and doped NSs was calculated as 29.3, 32.8, 25.79, and 45.19 nm, respectively. The control sample (NiO₂) showed maximum absorption at 330 nm, and upon doping, a redshift was observed, leading to decreased band gap energy from 3.75 to 3.59 eV. TEM of NiO₂ shows agglomerated nonuniform nanorods exhibited with various nanoparticles without a specific orientation; a higher agglomeration was observed upon doping. The (4 wt %) V₂O₅/Cs-doped NiO₂ NSs served as superior catalysts with a 94.21% MB reduction in acidic media. The significant antibacterial efficacy was estimated against Escherichia coli by measuring the zone of inhibition (3.75 mm). Besides their bactericidal analysis, V₂O₅/Cs-doped NiO₂ was shown to have a binding score of 6.37 for dihydrofolate reductase and a binding score of 4.31 for dihydropteroate synthase in an in silico docking study of E. coli.