The effect of a microcarrier suspension cell culture system on polarization measurements from Ni–Cr dental casting alloys

The Effect of Porcelain Firing on Electrochemical Behavior of a Dental Alloy in Hydrogen Peroxide

PURPOSE

The aim of this study was to evaluate changes in electrochemical corrosion properties of porcelain firing simulated nickel-chromium dental casting alloy exposed to a 10% hydrogen peroxide bleaching agent.

MATERIALS AND METHODS

The electrochemical corrosion behavior of a Ni-Cr alloy was evaluated by cyclic polarization test in the aerated electrolyte (pH = 6.5). Test groups were produced in as-cast (group 1, control group) and simulated porcelain firing (group 2: heat-treated/mean value; group 3: heat-treated/cycle) conditions. Scanning electron microscopy (SEM) was also used to examine the alloy surfaces before and after the corrosion test.

RESULTS

The ranking of the groups with respect to Ecorr and Icorr was as follows: 1, 2, 3 and 3, 1, 2, respectively. Group 3 exhibited the greatest and group 2 displayed the least corrosion tendencies. An increase in corrosion rates was observed after heat treatment/cycle state. Post-corrosion SEM photographs were also consistent with the test results.

CONCLUSION

Within the parameters of this study, a single heat treatment is insufficient to cause upheaval in corrosion behavior of a Ni-Cr alloy subjected to 10% hydrogen peroxide.

The concentrations of IL-8 and IL-6 in gingival crevicular fluid during nickel-chromium alloy porcelain crown restoration

We explored gum irritation and cytotoxicity caused by nickel-chromium (Ni-Cr) alloy porcelain by interleukin-8 (IL-8), interleukin-6 (IL-6) and gingival crevicular fluid (GCF) volumes at different time points peri-crown restoration. This prospective study was conducted in 60 young adults. The total amount and concentrations of IL-8 and IL-6 per site, GCF volumes, and blood neutrophil counts were performed prior to and at 1 week, 3 months, and 6 months after Ni-Cr alloy-porcelain crown restoration. Thirty male and 30 female subjects, aged 20-35 years old were enrolled. The total amount and concentrations of IL-8 and IL-6 per site, GCF volumes increased after nickel-chromium (Ni-Cr) alloy-porcelain crown restoration, and reached its peak at the third month as the GCF volume increased by 52.20 %, the total amount and concentrations of IL-8 increased by 112.11 and 22.75 %; the total amount and concentrations of IL-6 increased by 77.66 and 17.17 % when compared to baseline. In particular, the increase of IL-8 concentration was found in female patients at 3 months after restoration; while the neutrophil count of the peripheral blood did not change significantly. The increase in the total amount and the concentrations of IL-8 and IL-6 and GCF volume may be related to the cytotoxicity induced by Ni-Cr alloy. The significant increase of IL-8 concentration in females indicates that more attention should be given to women during Ni-Cr alloy porcelain crown restoration.

Evaluation of the potential cytotoxicity of metals associated with implanted biomaterials (I)

The present assessments of potential toxicity of metal ions (Al, Ni, Cr, V, and Ag) that construct the metallic biomaterials were carried out in vitro. By measurements of cell alkaline phosphatase (ALP) activity and reduction ability of cell methyl tetrazolium (MTT), the cytotoxicity of prevalence metallic biomaterials has been investigated. Furthermore, the poison and erosion of metal ions and atoms on human tissue are discussed. Research results indicated that trace Cr(VI) showed serious cytotoxicity and Ni as well as V are cytotoxic if the ion concentration in culture medium is over 100 micromol x L(-1) and 1 micromol x L(-1), respectively. A strange phenomenon is that Ag also is cytotoxic if the ion concentration is higher than 500 micromol x L(-1). Al ion is biphasic in cytotoxicity. At low ion concentration (< 10 micromol x L(-1)), Al ions can stimulate cell proliferation, whereas at concentrations over 1,000 micromol x L(-1), cytotoxicity increases.

Interactions between stainless steel, shear stress, and monocytes

Angioplasty with stent placement is commonly used to treat coronary atherosclerosis. However, 20-40% of stainless steel stents restenose within 6 months via a prolonged inflammatory response mediated by monocytic infiltration and cytokine secretion. In the current study, we tested a hypothesis that blood flow and monocytes interact to alter stent corrosion. We assessed the effects of THP1 monocytes on the corrosion rate of 316L stainless steel (316LSS) under shear stress (0.5-50 dyn/cm(2)). In addition, THP1 cytokine secretion was determined using cytokine arrays and ELISA analyses. Data were compared using ANOVA and Tukey post hoc analysis (alpha = 0.05). Monocytes significantly lowered 316LSS corrosion rates without limiting current density. However, shear stress alone did not alter the corrosion rate of 316LSS. THP1 cells adhered to the 316LSS surface at all flow rates. Exposure to the 316LSS/corrosion test under high fluid flow rates increased (>twofold) the secretion of 7 of the 42 cytokines tested (angeogenin, GRO, I309, interleukin 8, interleukin 6, interleukin 1beta, and macrophage chemoattractant protein-1). Each of these cytokines play a role in wound healing, macrophage differentiation, and cell proliferation, all hallmarks of in-stent restenosis. Furthermore, only IL8 levels were significantly higher than any of the system controls during the 316LSS/corrosion test conditions. The IL8 levels from the 316LSS/corrosion tests were not significantly different from the +LPS control. Together, these data suggest that monocytic cells maybe activated by exposure to 316LSS stents and could contribute to in-stent restenosis and altered corrosion of the stent.