Effect of N-acetyl cysteine on orthodontic primers cytotoxicity

Short-term "in vivo" study on cellular DNA damage induced by acrylic Andresen activator in oral mucosa cells

OBJECTIVES

To analyse through comet assay and micronucleus test the viability and DNA damage occurred in buccal mucosa epithelial cells after a short-term exposure to Andresen activator resin monomers.

SETTING AND SAMPLE POPULATION

Test group consisting of 26 subjects was treated with Andresen activator; 16 subjects who had never undergone orthodontic treatment were enrolled in the control group.

MATERIAL & METHODS

Buccal mucosa samples were collected before treatment and after 7, 15, 30, 60 and 90 days. The analyses performed on the cells included the following: cellular viability, comet assay and micronucleus test. Mean ± SD were calculated for cellular viability, tail moment, tail intensity, tail length, micronuclei, binuclear and bud cells. Significance (P < 0.05) was evaluated with Dunnett's test.

RESULTS

Cellular viability did not change during observational time, and its trend was similar to the controls. Tail moment and tail intensity significantly increased after 30 and 60 days, respectively, whereas tail length remained unchanged over time in the test group; the same parameters did not change in the control group. In the test group, micronuclei, binuclear and bud cells significantly increased after 30, 60 and 90 days, respectively.

CONCLUSION

The resin monomers of the Andresen activator cause genotoxic effects detectable through comet assay and micronucleus test, but they do not produce clear cytotoxic effects after a 90 days exposure.

Effect of pH on in vitro biocompatibility of orthodontic miniscrew implants

Background

Although the clinical use of miniscrews has been investigated on a large scale, little is known about their biocompatibility. Since low pH can affect corrosion resistance, the aim of this study was to evaluate the cytotoxic effect of orthodontic miniscrews in different pH conditions.

Methods

Four orthodontic miniscrews of stainless steel and grade IV and grade V titanium were immersed in a pH 7 and pH 4 saline solution for 1, 7, 14, 21, 28, and 84 days. Human osteogenic sarcoma cells (U2OS), permanent human keratinocytes (HaCat), and primary human gingival fibroblasts (HGF) were exposed to eluates, and the mitochondrial dehydrogenase activity was measured after 24 h to assess the cytoxicity. The results were analyzed using the Mann-Whitney U test (P < 0.05).

Results

When exposed to pH 7-conditioned eluates, the cell lines showed an even greater viability than untreated cells. On the contrary, the results revealed a statistically significant decrease in U2OS, HaCat, and HGF viability after exposure to eluates obtained at pH 4. Among the cell lines tested, HGF showed the most significant decrease of mitochondrial activity. Interestingly, grade V titanium miniscrews caused highest toxic effects when immersed at pH 4.

Conclusions

The results suggested that at pH 7, all the miniscrews are biocompatible while the eluates obtained at pH 4 showed significant cytotoxicity response. Moreover, different cell lines can produce different responses to miniscrew eluates.