Surface pre-conditioning with bioactive glass air-abrasion can enhance enamel white spot lesion remineralization

Effect of air-abrasion pretreatment with three desensitizing agents on efficacy of in-office tooth bleaching

OBJECTIVE

To evaluate the influence of air-abrasion of enamel with three different desensitizing powders on the whitening effect of a bleaching gel containing 40% H2O2, which was used for in-office tooth bleaching.

MATERIALS AND METHODS

Forty human incisors, extracted and prepared, were acquired for this study and subsequently randomized into four groups (n = 10). The control group specimens underwent no pretreatment prior to the bleaching procedure, whereas the remaining three groups underwent air abrasion using distinct desensitizing powders; (a) Sylc, which contains bioglass 45S5; (b) BioMinF, which contains calcium phospho-fluoro-silicate glass; and (c) MI Pearls, which contains nano-hydroxyapatite, 1 h preceding the Opalescence Boost PF 40% bleaching procedure. Color measurements were conducted using a double-beam UV-Vis spectrophotometer at four distinct time points (prior to bleaching, 24 h, 15 days, and 30 days post-bleaching).

RESULTS

Tooth color change outcomes revealed that there were no statistically significant results with respect to the interaction of the two criteria (treatments and time) (p = 0.990). Additionally, there were no statistically significant results with respect to the main effects of treatments (p = 0.385), while there were statistically significant effects with respect to the time criterion (p = 0.013).

CONCLUSIONS

The use of the tested desensitizing powders prior the bleaching procedure did not affect the tooth color change induced by the tested bleaching agent.

CLINICAL SIGNIFICANCE

Tooth color change and whiteness are not affected by air-abrasion desensitizing treatments when applied prior to in-office bleaching procedures.

Evaluation of incipient enamel-carious-like lesion treated with hydroxyapatite-chitosan nanocomposite hydrogel

BACKGROUND

Non-invasive restoration of tooth enamel is a topic of high relevance in dental material science. Multiple approaches have been proposed to reach optimum reconstruction results. The current study was performed to evaluate the cross-sectional microhardness besides mineral quality and content in artificially induced carious enamel after treatment with hydroxyapatite-chitosan (HAp-CS) nanocomposite gel.

METHODS

Artificially carious lesions were induced by immersion of teeth in acidic carboxymethyl cellulose gel (pH 4.95-5) for 24- and 72-hours periods. Two different compositions of HAp-CS nanocomposite hydrogel were prepared with two different ratios 50/50 (%) and 70/30 (%), respectively. Additionally, sodium fluoride gel (1000 ppm concentration) was prepared and used as reference. Gels were applied to carious lesions twice/day for 3 min/each. After 45 days of application, surface morphology, energy dispersive x-ray spectroscopy, micro-Raman analysis in addition to cross-sectional microhardness were evaluated. Statistical analysis was performed using two-way ANOVA and Tukey's post hoc statistical tests.

RESULTS

Surface morphological evaluation of treated surfaces showed obliteration of surface irregularities. Groups demineralized for 24 hours and treated with 70/30 (HAp-CS) showed highest significant cross-sectional-microhardness (P ≤ 0.05). Evaluated subsurface cross-sectional microhardness showed better mineral quality for groups demineralized for 24 hours and treated with HAp-CS nanocomposite gels.

CONCLUSIONS

Nanocomposite gel with 70/30 (HAp-CS) could efficiently improve cross-sectional microhardness and both minerals composition and quality for lesions demineralized for 24 hours. More severely induced lesions, as demineralized for 72 hours, need more powerful agent compositions and/or prolonged application protocols for improvement.

Biomimetic Self-Maturation Mineralization System for Enamel Repair

Enamel repair is crucial for restoring tooth function and halting dental caries. However, contemporary research often overlooks the retention of organic residues within the repair layer, which hinders the growth of dense crystals and compromises the properties of the repaired enamel. During the maturation of natural enamel, the organic matrix undergoes enzymatic processing to facilitate further crystal growth, resulting in a highly mineralized tissue. Inspired by this process, a biomimetic self-maturation mineralization system is developed, comprising ribonucleic acid-stabilized amorphous calcium phosphate (RNA-ACP) and ribonuclease (RNase). The RNA-ACP induces initial mineralization in the form of epitaxial crystal growth, while the RNase present in saliva automatically triggers a biomimetic self-maturation process. The mechanistic study further indicates that RNA degradation prompts conformational rearrangement of the RNA-ACP, effectively excluding the organic matter introduced earlier. This exclusion process promotes lateral crystal growth, resulting in the generation of denser enamel-like apatite crystals that are devoid of organic residues. This strategy of eliminating organic residues from enamel crystals enhances the mechanical and physiochemical properties of the repaired enamel. The present study introduces a conceptual biomimetic mineralization strategy for effective enamel repair in clinical practice and offers potential insights into the mechanisms of biomineral formation.

Ultrastructural investigation of the effect of toothpastes containing different remineralizing agents on demineralized enamel

OBJECTIVE

The present study aimed to evaluate the effect of remineralizing agents on demineralized enamel intended for use as fluoride substitutes or supplements for oral hygiene applications.

METHODOLOGY

Enamel samples were obtained from 30 bovine teeth. The enamel blocks were stored in 20 mL of demineralization solution for 72 h. They were then brushed with the following toothpaste for the remineralization protocol: NaF, NaF/SnF2 combination, NovaMin, or nano-hydroxyapatite. SEM/EDX examinations and microhardness measurements of the samples were performed to investigate the remineralization efficacy of the studied toothpaste. One-way analysis of variance (ANOVA) with post hoc Tukey's HSD test was used to analyze the change in microhardness values in different remineralization protocols (p < 0.05).

RESULTS

Differences in the mean remineralization (%RP) and hardness recovery (%HR) were determined between the groups (p < 0.05). Groups 1 and 4 showed significant differences in %RP (p < 0.05). In the SEM/EDX examinations, the samples treated with n-HAp showed an accumulation of crystal deposits on the enamel surface, although at a lower density than those treated with NaF and NaF/SnF2 combination.

CONCLUSION

The remineralization strategy in toothpaste plays an important role in enamel remineralization. NovaMin-containing toothpaste showed positive effects on the enamel surface with better Ca/P ratio. Toothpastes containing n-HAp triggered less change in the increase of microhardness values compared to other toothpastes. The use of SnF2 in toothpaste in combination with NaF significantly increased the binding of fluoride to demineralized enamel compared to toothpaste containing NaF alone.

Surface roughness and microhardness of enamel white spot lesions treated with different treatment methods

Objective

To analyse the surface roughness and microhardness of artificial enamel white spot lesions before and after WSL formation, after treatment (Opalsutre™ microabrasion, Sylc® bioactive glass, and ICON® resin infiltration), and after pH cycling with the help of the profilometer surface roughness tester and the digital Vickers microhardness tester.

Materials and methods

Seventy-five extracted molars were used to acquire one hundred specimens. 50 specimens were randomly assigned to five groups (n = 10) for the surface roughness study: 1) Sound group, 2) WSL group, 3) micro abrasion (MA; Opalustre, Ultradent, South Jordan, UT, USA), 4) bioactive glass 45S5 Sylc powder (Sylc; Denfotex Research Ltd, Inverkeithing, UK), and 5) ICON resin infiltration (ICON; DMG, Hamburg, Germany). An additional 25 specimens were used to obtain 50 enamel slabs for the surface microhardness study, which were also assigned to the same groups. All groups underwent a final stage of pH cycling. Surface roughness and surface microhardness measurements were performed at different stages for all groups.

Results

Regarding surface roughness, ICON significantly reduced the surface roughness compared to Opalustre and Sylc, with no significant difference between Opalustre and Sylc. In terms of surface microhardness, ICON showed the highest improvement, followed by Sylc and then Opalustre. Both surface roughness and microhardness were significantly affected by demineralization, partially improved after treatment, and then regressed significantly after pH cycling.

Conclusion

ICON resin infiltrant can be considered as a superior treatment option for improving surface roughness and microhardness, while Opalustre demonstrated relatively the poorest performance compared to the other treatment options. It is noteworthy that the pH cycling procedure had an adverse impact irrespective of the treatment option used.

Comparative analysis of the effect of Bioactive Glass 45S5 on enamel erosion progression in human dentitions (in vitro study)

OBJECTIVES

The aim of the present study was to compare the surface morphology alterations, mineral content, and surface roughness of eroded enamel surface versus eroded enamel surface which was preceded by Bioactive Glass 45S5 (BAG45S5) application in both primary and permanent human dentitions.

MATERIALS AND METHODS

Fifty-two primary teeth and fifty-two permanent teeth were selected. Teeth were randomly divided into 4 groups of twenty-six teeth each. Groups A1 and B1 underwent erosion with 1% citric acid, while groups A2 and B2 were subjected to application of BAG45S5 powder followed by the same erosive conditions as A1 and B1. Measurements were performed by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and surface profilometry. They were used to examine the surface morphology alterations, mineral content, and surface roughness, respectively.

RESULTS

SEM of enamel which received BAG45S5 showed smoother surface in primary teeth post erosion. EDX analysis showed that enamel exhibited crucial resistance to mineral loss in the group which received BAG45S5 prior to inducing erosion as compared to the induced erosion-only group. This was significant (p < 0.005) in both human dentitions. Erosion-only groups showed significantly less surface roughness in permanent teeth (p < 0.045). A marked decrease in surface roughness was observed in surfaces receiving BAG45S5, primary teeth (p < 0.001), and permanent teeth (p < 0.001).

CONCLUSIONS

Bioactive Glass 45S5 proved successful against erosive conditions in both primary and permanent teeth with better performance in the permanent teeth so it can be regarded as a means of prevention.

CLINICAL RELEVANCE

Bioactive Glass 45S5 powder could be used not only to remove stains but also as a prophylactic preventive measure against the multiple episodes of acidic food and beverage consumption in children.

A novel amelogenesis-inspired hydrogel composite for the remineralization of enamel non-cavitated lesions

Enamel non-cavitated lesions (NCLs) are subsurface enamel porosity from carious demineralization. The developed enamel cannot repair itself once NCLs occurs. The regeneration of mineral crystals in a biomimetic environment is an effective way to repair enamel subsurface defects. Previously, an amelogenin-derived peptide named QP5 was proven to repair demineralized enamel. In this work, inspired by amelogenesis, a novel biomimetic hydrogel composite containing the QP5 peptide and bioactive glass (BG) was designed, in which QP5 could promote enamel remineralization by guiding the calcium and phosphorus ions provided by BG. Also, BG could adjust the mineralization micro-environment to alkalinity, simulating the pH regulation of ameloblasts during enamel maturity. The BQ hydrogel composite showed biosafety and possessed capacity for enamel binding, ion release and pH buffering. Enamel NCLs treated with the BQ hydrogel composite showed a higher reduction in lesion depth and mineral loss both in vitro and in vivo. Moreover, compared to the hydrogels containing only BG or QP5, groups treated with the BQ hydrogel composite attained more surface microhardness recovery and color recovery, exhibiting resistance to erosion and abrasion of the remineralization layer. We envision that the BQ hydrogel composite can provide a biomimetic micro-environment to favor enamel remineralization, thus reducing the lesion depth and increasing the mineral content as a promising biomimetic material for enamel NCLs.

EFFICACY OF NOVEL BIOACTIVE GLASS IN THE TREATMENT OF ENAMEL WHITE SPOT LESIONS: A RANDOMIZED CONTROLLED TRIAL✰

OBJECTIVES

to evaluate the efficacy of 2 types of bioactive glass (45S5) compared to casein-phosphopeptide stabilized-amorphous calcium phosphate (CPP-ACP) in the treatment of orthodontically-induced white spot lesions (WSLs).

METHODS

Sixty post-orthodontic WSLs (ICDAS II score 2) were randomly allocated to a double blind randomized controlled trial with 3 parallel arms (n = 20). Test group I (Bio-BAG) received BiominF slurry and toothpaste, and test group II (N-BAG) received Novamin slurry and toothpaste. While the positive control group (CPP-ACP) received Recaldent paste. Products were applied daily in-office during week 1, and boosted by self-administered home application for 4 weeks (week 1-4). Standard oral hygiene care was performed by all participants twice daily during months 2-6. All patients were assessed for change in WSL dimensions using computer assisted analysis based on standardized digital intraoral photographs in addition to laser fluorescence DIAGNOdent assessment before treatment (T0) and at 1 week (T1), 1 month (T2), 3 months (T3,) and 6 months (T4) follow up periods.

RESULTS

Kruskal Wallis test was used (P < .05 for all). At T4, a statistically significant (P < .001) regression of WSL was disclosed in all 3 groups compared to baseline, and a highly significant lesion size percent reduction in Bio-BAG group compared to the control group (P < .001). The mean area of the lesions decreased by 64.8%, 32.2%, and 31.6% for groups I, II and III respectively (P = .001). DIAGNOdent findings largely reflected the clinical scores (Mean scores at baseline/T4 for groups I, II, and III respectively; 16.57/3.62, 16.93/7.90, 21.95/19.27). No adverse effects were reported.

CONCLUSIONS

The combined in-office and home-application of BiominF paste for 4 weeks resulted in greater esthetic improvements of post-orthodontic WSLs compared to Novamin and CPP-ACP. In addition, BiominF showed a significant reduction in fluorescence intensity which indicates potential lesion remineralization.

CLINICAL RELEVANCE

Post-orthodontic WSLs can be diminished using bioactive glass remineralization therapy.

Synthesis and characterization of nano bioactive glass for improving enamel remineralization ability of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP)

OBJECTIVE

Nanomaterials with superior properties such as high surface area over volume ratio are widely used in dentistry and medicine. This in vitro study was performed to synthesize and characterize nano bioactive glass (nBG) and to evaluate the effect of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) containing nBG (CPP-ACP@nBG) on enamel remineralization by its application to pH-cycled, synthetically demineralized enamel surfaces.

MATERIALS AND METHODS

nBG particles were prepared by sol-gel method. X-ray diffraction pattern (XRD), Fourier-transform infrared spectroscopy (FTIR) and transmittance electron microscopy (TEM) were used for nBG characterization. Synthetic CPP-ACP paste was prepared and nBG particles were added to it. To evaluate the degree of remineralization, 32 healthy human premolars were selected. The samples were randomly divided into 4 groups as: Group 1: Commercial CPP-ACFP (MI paste plus), Group 2: Synthetic casein phosphopeptide-amorphous calcium phosphate containing fluoride (CPP-ACP@F), Group 3: Synthetic CPP/ACP containing nBG (CPP-ACP@nBG), and Group 4: Control (received no treatment). The pastes were then applied on the tooth surfaces for 28 days. The Vickers microhardness of enamel surfaces was evaluated, and enamel surface morphology was assessed using scanning electron microscopy (SEM).

RESULTS

X-Ray diffraction pattern (XRD) of the synthesized nBG show its crystalline nature with the Larnite crystalline mode. Transmittance electron microscope (TEM) microimage of the synthesized nBG shows its formation as less that 100 nm spherical nanoparticle with partial agglomeration. Fourier transform infrared spectroscopy (FTIR) confirm the success formation of nBG with high purity. The results of this study showed that microhardness of the experimental groups was significantly higher than the control group (p ≥ 0.05). SEM images showed a layer of hydroxyapatite in the CPP-ACP@nBG, synthetic and commercial CPP-ACP@F remineralized groups.

CONCLUSION

The results of this study demonstrated that CPP-ACP@F and CPP-ACP@nBG remineralize the surface of the demineralized enamel. Microhardness of the remineralized enamel in the CPP-ACP@nBG group was higher than synthetic and commercial CPP-ACP@F groups.

Novel Fluoride- and Chloride-containing Bioactive Glasses for Use in Air Abrasion

OBJECTIVES

To investigate the degradation, fluorapatite formation, biological safety and cutting efficiency on dentine of the mixed fluoride- and chloride-containing bioactive glasses (BGs).

METHODS

Two series of mixed fluoride- and chloride-containing glasses (GPFCl and GPF2.3Cl series) were synthesized using a melt-quench method. Glass transition temperature (T_g) and the bioactivity in term of glass degradation and fluorapatite formation were evaluated in Tris buffer solution. The cutting efficiency of the powdered BGs (GPF2.3Cl series) on dentine via air abrasion was investigated using white light profilometry and scanning electron microscope. The cytotoxicity of GPF2.3Cl series on human periodontal ligament stem cells (hPLSCs) and oral fibroblasts (OFB) were examined by MTT.

RESULTS

These BGs are highly degradable and able to form fluorapatite within 3h of immersion. The formation of CaF₂ was also found in the high fluoride-containing BGs. The faster glass degradation was evidenced in the BGs with higher chloride. A significant reduction of T_g from 790°C to 463°C was seen with increasing in calcium halide content. Air abrasion on dentine using the low and intermediate chloride-containing glasses demonstrates clear depressions, while no depression was found using the high chloride-containing glass. Moreover, the studied BGs showed no cytotoxicity to hPLSCs and OFB.

CONCLUSIONS

The glasses with mixed fluoride and chloride integrate the benefits from the presence of both, showing rapid glass degradation, fast fluorapatite formation, excellent biocompatibility and controllable hardness to provide a selective cutting efficiency on dentine.

CLINICAL SIGNIFICANCE

The developed BGs air abrasive with tunable hardness by varying chloride content can selectively cut different dental tissues. In clinic, a relatively hard BG is of great interest for caries preparation, while a soft glass is attractive for tooth cleaning.

Strategies of Bioceramics, Bioactive Glasses in Endodontics: Future Perspectives of Restorative Dentistry

Prevalently, there is a primary strategy to cure caries using restorative materials notably bioceramics. Existing synthetic materials stimulate natural tooth structure with acceptable interfacial bonding and esthetic and biomechanical qualities with better durability. Several bioceramics have been introduced and investigated for their potentialities as restorative materials. Biomineralization of tooth initiates repair and regeneration of natural dental tissue and reinstating the integrity of periodontium. In the evolution of bioceramics in the aspects of different essential composition for dental application, recent technology and modern strategies revolutionize the restorative dentistry. Bioglass is one among the important bioceramics as a restorative material, and by regulating the properties of the material, it is possible to construct improved formulation towards restoration. This article reviews the current revolution of endodontics, existing restorative materials, and technologies to be achieve for engineering materials with the better design.

Effect of air-abrasion pretreatment with three bioactive materials on enamel susceptibility to erosion by artificial gastric juice

OBJECTIVE

The purpose of the study was to investigate the protective effect of three in-office preventive treatments with bioactive materials against enamel erosion induced by artificial gastric juice similar to that found in gastroesophageal reflux disease (GERD) patients. The treatments included air-abrasion of enamel with a fluoride-containing bioactive glass (BioMinF®), Bioglass 45S5 (ProSylc) and nano-hydroxyapatite (MI Pearls) to test enamel susceptibility following an erosive challenge.

METHODS

Enamel surface loss was evaluated using confocal microscopy, while changes in enamel surface roughness and morphology were also investigated after the treatments. SEM and EDS were used to observe formation of apatite crystals on enamel and to detect alterations in mineral composition. In Group 1 (negative control) the specimens did not receive any treatment; Group 2 specimens (positive control) treated with 0.4 % SnF₂, while in Groups 3-5 enamel was air-abraded with BioMinF®, ProSylc and MI Pearls, respectively.

RESULTS

All the experimental groups reduced significantly enamel surface loss compared to the negative control group (p < 0.05), except for the MI Pearls treatment (p > 0.05). The most protective behavior against erosion presented the treatment with SnF₂. BioMinF induced the larger amount of apatite crystals on the enamel surface, followed by ProSylc.

SIGNIFICANCE

BioMinF and ProSylc treatments may be beneficial against dental erosion induced by gastric juice in GERD patients, while MI Pearls treatment may not suitable for this indication. Both materials promote formation of apatite crystals on enamel in acidic conditions protecting the surface from the erosion. The tested treatments may be useful in GERD patients who cannot comply with at-home therapies with SnF₂.

Efficacy of a Novel Bioactive Glass-Polymer Composite for Enamel Remineralization following Erosive Challenge

Introduction

Dental caries is the most common cause of tooth loss. However, it can be stopped by enhancing remineralization. Fluoride and casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) are among the most important remineralizing agents. Recent studies have used bioactive glass as a remineralizing agent in different forms. This study aimed to assess the efficacy of a composite paste (prepared by mixing urethane polypropylene glycol oligomer with bioactive glass powder for easier application).

Materials and Methods

Enamel disks were cut out of the buccal surface of extracted sound third molars. The samples were randomly divided into 3 groups of 15 and underwent Vickers microhardness test. X-ray diffraction (XRD) and field emission scanning electron microscopy/energy dispersive X-ray spectroscopy (FESEM/EDS) were performed. All samples were immersed in a demineralizing solution for 14 days. The tests were then repeated. Next, bioactive glass paste, fluoride, and CPP-ACP were applied on the surface of the samples and they were then stored in an artificial saliva for 14 days. The tests were repeated again. The microhardness values were analyzed using repeated measures ANOVA followed by one-way ANOVA and Tukey's post hoc test (P < 0.05).

Results

The microhardness of the bioactive glass group was significantly higher than that of other groups (P < 0.05). XRD revealed an enamel structure more similar to sound enamel in the bioactive glass and CPP-ACP groups compared with the fluoride group. FESEM/EDS revealed higher hydroxyapatite deposition in the bioactive glass group than in the other two groups.

Conclusions

All three remineralizing agents caused remineralization, but bioactive glass paste had a greater efficacy.

An investigation into the cutting efficiency of a novel degradable glass as an alternative to alumina powder in air abrasion cutting of enamel

Objectives

To develop and test the cutting efficiency of a novel degradable glass as an alternative media to alumina powder for air abrasion.

Materials and methods

A zinc-based glass (QMZK2) was designed, produced, and evaluated with a multi-modality imaging analysis. The glass dissolution study was carried out in three acids, using ICP-OES (inductively coupled plasma optical emission spectroscopy) at 5 different time points: 2.5, 5, 10, 60, and 240 min. The cutting efficiency of both materials was tested under the same parameters on slabs of elephant enamel. A stained fissure of a molar tooth was air abraded with the glass and evaluated with X-ray micro-tomography before and after air abrasion.

Results

The particle size distribution of the glass was similar to that of alumina 53 µm but with a slightly greater dispersion of particle size. The shape of the particles was angular, appropriate for cutting purposes. The dissolution study showed that the glass dissolved rapidly in acidic conditions at all time points. Between the two variables, pressure and powder flow, pressure was found to influence the cutting speed to a greater extent than powder flow.

Conclusions

Alumina powder was found to perform significantly better in 4 of the 9 conditions tested on elephant enamel, QMZK2 in one, and no significant differences were found for the rest of the 4 conditions. The QMZK2 seems to offer promising results as an alternative material to alumina.

Clinical relevance.

QMZK2 glass has the potential for replacing aluminum oxide as a degradable material in air abrasion technology.

Role of bioglass in enamel remineralization: Existing strategies and future prospects-A narrative review

Enamel, once formed, loses the ability to regenerate due to the loss of the formative ameloblasts. It is subjected to constant damaging events due to exposure to external agents and oral microbiomes. An enamel remineralization process targets to replenish the lost ionic component of the enamel through a multitude of methods. Enamel remineralization is highly challenging as it has a complex organized hierarchical microstructure. Hydroxyapatite nanocrystals of the enamel vary in size and orientation along alignment planes inside the enamel rod. The inability of the enamel to remodel unlike other mineralized tissues is another substantial deterrent. One of the well-known biomaterials, bioglass (BG) induces apatite formation on the external surface of the enamel in the presence of saliva or other physiological fluids. Calcium, sodium, phosphate, and silicate ions in BG become responsive in the presence of body fluids, leading to the precipitation of calcium phosphate. Studies have also demonstrated the bactericidal potential of BG against Streptococcus mutans biofilms. The anticariogenicity and antibacterial activity were found to be enhanced when BG was doped with inorganic ions such as F, Ag, Mg, Sr, and Zn. Due to the versatility of BG, it has been combined with a variety of agents such as chitosan, triclosan, and amelogenin to biomimic remineralization process. Key strategies that can aid in the development of contemporary enamel remineralization agents are also included in this review.

Bioactivity assessment of bioactive glasses for dental applications: A critical review

OBJECTIVE

In the context of minimally invasive dentistry and tissue conservation, bioactive products are valuable. The aim of this review was to identify, clarify, and classify the methodologies used to quantify the bioactive glasses bioactivity.

METHODS

Specific search strategies were performed in electronic databases: PubMed, Embase, Cochrane Library, and Scopus. Papers were selected after a review of their title, abstract, and full text. The following data were then examined for final selection: BAG investigated, objectives, criteria, methods, and outcomes.

RESULTS

Sixty-one studies published from 2001 to 2019, were included. The bioactivity of BAG can be evaluated in vitro in contact with solutions, enamel, dentin, or cells. Other studies have conducted in vivo evaluation by BAG contact with dentin and dental pulp. Studies have used various analysis techniques: evaluation of apatite with or without characterization or assessment of mechanical properties. Reprecipitation mechanisms and pulp cell stimulation are treated together through the term 'bioactivity'.

SIGNIFICANCE

Based on these results, we suggested a classification of methodologies for a better understanding of the bioactive properties of BAG. According to all in vitro studies, BAG appear to be bioactive materials. No consensus has been reached on the results of in vivo studies, and no comparison has been conducted between protocols to assess the bioactivity of other bioactive competitor products.

Effectiveness of polyacrylic acid-bioactive glass air abrasion preconditioning with NovaMin remineralization on the microhardness of incipient enamel-like lesion

Background:

Bioactive glass (BAG) remineralization is a promising method for dental hard tissue regeneration. The aim of this study was to evaluate the microhardness of incipient enamel-like lesions with or without preconditioning by air abrasion using polyacrylic acid (PAA)-BAG before application of NovaMin remineralizing agent.

Materials and Methods:

Forty extracted human molars were selected, sectioned mesiodistally obtaining buccal and lingual halves, and embedded in resin molds. Specimens were randomly assigned to four groups (n = 10) according to the remineralization protocol: G1 (control, artificial saliva), G2 (preconditioning), G3 (NovaMin), and G4 (preconditioning and NovaMin). Enamel windows 4 mm × 4 mm were done on the buccal and lingual surfaces. Specimens were immersed in a daily renewed demineralizing solution to create white spot lesions. Remineralizing agents were applied according to the manufacturer's instructions, and specimens were stored in a daily renewed artificial saliva. Microhardness was assessed using Vickers hardness number (VHN) at baseline (positive control), after demineralization (negative control), and after 24-h and 1-month remineralization.

Results:

The preconditioning/NovaMin group after 1 month showed a statistically significant high VHN, with no statistically significant difference between it and the positive control. This was followed by the NovaMin group after 1 month, while the lowest VHN was found in the demineralized group, with no statistically significant difference between it and the preconditioning group, whether after 24 h or 1 month.

Conclusions:

Enamel preconditioning with PAA-BAG air abrasion play a major role in enhancement of remineralization when it is accompanied with NovaMin. Furthermore, an extended period of time had helped to attain more benefits from NovaMin remineralization.

Clinical Significance:

Enamel remineralization with NovaMin after conditioning by bioactive glass air abrasion, provides the patients with a fast and durable treatment of incipient enamel lesions, which would reduce the possibility of future progression of demineralization and caries occurrence.

Effect of air-abrasion pre-treatment with bioactive glass 45S5 on enamel surface loss after erosion/abrasion challenge

OBJECTIVES

The aim of this in vitro study was to evaluate the effect of air-abrasion surface pre-treatment with bioactive glass (BAG) 45S5 on enamel surface loss after erosion/abrasion challenge.

METHODS

Twenty-four sound bovine incisors were used for this study. Four experimental groups (n=12) were assigned as follows: Group 1 was the negative control group, Group 2 specimens were treated with a SnF₂ gel (positive control group), Group 3 specimens were air-abraded with BAG 45S5 (ProSylc) and Group 4 received both treatments. The specimens were submitted to erosion/abrasion challenge using a common soft drink. Enamel surface loss was evaluated using an optical profilometer. Additionally, surface roughness (VSI method) and surface microhardness (Vickers method) changes were evaluated, as well as SEM and EDS analyses were performed on enamel surface. The data were statistically analyzed using one-way ANOVA and Tukey's post-hoc test at a level of significance a=0.05.

RESULTS

Surface pre-treatment with BAG 45S5 reduced surface loss in comparison with negative control group (p<0.001), which exhibited the highest surface loss of the experimental groups (p<0.05). The positive control group (SnF₂ treatment) and Group 4 specimens, which received both air-abrasion pre-treatment and SnF₂ treatment, presented the lowest surface loss (p<0.05), but did not show significant differences to each other (p=0.65).

SIGNIFICANCE

Air-abrasion pre-treatment with BAG 45S5 may be beneficial as an in-office preventive method for the limitation of enamel erosive wear induced by excessive consumption of soft drinks. The clinical significance of the results regarding this preventive method should be confirmed by clinical studies.

Enamel Remineralization with Novel Bioactive Glass Air Abrasion

Enamel demineralization or white spot lesions (WSLs) are a frequent complication associated with fixed appliance–based orthodontic treatment. The remineralization potential of a novel fluoride-containing bioactive glass (QMAT3) propelled via an air abrasion system was compared with Sylc glass and artificial saliva on artificially induced WSLs. Thirty extracted human premolars were randomly assigned into 3 groups ( n = 10) per method of treatment and scanned with optical coherence tomography and noncontact profilometer in the 4 enamel states: sound, demineralized, after glass propulsion, and after immersion in artificial saliva. Knoop hardness testing was also performed. Twenty additional prepared teeth samples were also randomly selected for examination by scanning electron microscopy and energy-dispersive X-ray spectroscopy (2 teeth per technique) under each of the 4 enamel conditions. 19F MAS-NMR (magic angle spinning–nuclear magnetic resonance) was also used to detect the type of apatite formed on the enamel surface. Significant enamel remineralization with surface roughness and intensity of light backscattering similar to that of sound enamel was observed following treatment with QMAT3. In addition, mineral deposits were detected on the remineralized enamel surfaces, forming a protective layer and improving its hardness. This layer was rich in calcium, phosphate, and fluoride; 19F MAS-NMR confirmed the formation of fluorapatite. This finding is particularly beneficial since fluorapatite is more chemically stable than hydroxyapatite and has greater resistance to acid attack. Hence, a promising fluoride-containing bioactive glass for enamel remineralization has been developed, although further clinical evaluation and refinement is required.

Development of a novel bioactive glass for air-abrasion to selectively remove orthodontic adhesives

OBJECTIVES

To develop a novel, bioactive glass for removing residual orthodontic adhesive via air-abrasion, following bracket debonding, and to evaluate its effectiveness against a proprietary bioactive glass 45S5(Sylc™)-air-abrasion, and a slow-speed tungsten carbide (TC) bur.

MATERIALS AND METHODS

Three glasses were prepared and their bioactivity was proved. One novel glass (QMAT3) was selected due to its appropriate hardness, lower than that of enamel/45S5(Sylc™). Sixty extracted human premolars were randomly assigned to adhesive removal using: (a) QMAT3-air-abrasion, (b) 45S5(Sylc™)-air-abrasion, and (c) TC bur, which were further subdivided (n = 10) based on the adhesive used (Transbond XT™ or Fuji Ortho LC™). Enamel roughness was assessed using scanning electron microscopy (SEM) and non-contact profilometry before bracket bonding, after removing residual adhesive following bracket debonding and after polishing.

RESULTS

QMAT3 formed apatite faster (6 h) than 45S5(Sylc™) (24 h) in Tris solution. QMAT3-air-abrasion gave the lowest enamel roughness (Ra) after removing the adhesives. SEM images showed a pitted, roughened enamel surface in the TC bur group and to a lesser extent with 45S5(Sylc™), while a virtually smooth surface without any damage was observed in the QMAT3-air-abrasion group. The time taken for adhesive removal with QMAT3 was comparable to 45S5(Sylc™) but was twice as long with the TC bur.

CONCLUSIONS

QMAT3-air-abrasion is a promising technique for selective removal of adhesives without inducing tangible enamel damage.

CLINICAL RELEVANCE

A novel bioactive glass has been developed as an alternative to the use of TC burs for orthodontic adhesive removal.

The effect of dentine pre-treatment using bioglass and/or polyacrylic acid on the interfacial characteristics of resin-modified glass ionomer cements

OBJECTIVE

To evaluate the effect of load-cycle aging and/or 6 months artificial saliva (AS) storage on bond durability and interfacial ultramorphology of resin-modified glass ionomer cement (RMGIC) applied onto dentine air-abraded using Bioglass 45S5 (BAG) with/without polyacrylic acid (PAA) conditioning.

METHODS

RMGIC (Ionolux, VOCO) was applied onto human dentine specimens prepared with silicon-carbide abrasive paper or air-abraded with BAG with or without the use of PAA conditioning. Half of bonded-teeth were submitted to load cycling (150,000 cycles) and half immersed in deionised water for 24 h. They were cut into matchsticks and submitted immediately to microtensile bond strength (μTBS) testing or 6 months in AS immersion and subsequently μTBS tested. Results were analysed statistically by two-way ANOVA and Student-Newman-Keuls test (α = 0.05). Fractographic analysis was performed using FE-SEM, while further RMGIC-bonded specimens were surveyed for interfacial ultramorphology characterisation (dye-assisted nanoleakage) using confocal microscopy.

RESULTS

RMGIC applied onto dentine air-abraded with BAG regardless PAA showed no significant μTBS reduction after 6 months of AS storage and/or load cycling (p > 0.05). RMGIC-dentine interface showed no sign of degradation/nanoleakage after both aging regimens. Conversely, interfaces created in PAA-conditioned SiC-abraded specimens showed significant reduction in μTBS (p < 0.05) after 6 months of storage and/or load cycling with evident porosities within bonding interface.

CONCLUSIONS

Dentine pre-treatment using BAG air-abrasion might be a suitable strategy to enhance the bonding performance and durability of RMGIC applied to dentine. The use of PAA conditioner in smear layer-covered dentine may increase the risk of degradation at the bonding interface.

CLINICAL SIGNIFICANCE

A combined dentine pre-treatment using bioglass followed by PAA may increase the bond strength and maintain it stable over time. Conversely, the use of PAA conditioning alone may offer no significant contribute to the immediate and prolonged bonding performance.

Cellular differentiation, bioactive and mechanical properties of experimental light-curing pulp protection materials

OBJECTIVE

Materials for pulp protection should have therapeutic properties in order to stimulate remineralization and pulp reparative processes. The aim of this study was to evaluate the mechanical properties, biocompatibility, cell differentiation and bioactivity of experimental light-curable resin-based materials containing bioactive micro-fillers.

METHODS

Four calcium-phosphosilicate micro-fillers were prepared and incorporated into a resin blend: 1) Bioglass 45S5 (BAG); 2) zinc-doped bioglass (BAG-Zn); 3) βTCP-modified calcium silicate (β-CS); 4) zinc-doped β-CS (β-CS-Zn). These experimental resins were tested for flexural strength (FS) and fracture toughness (FT) after 24h and 30-day storage in simulated body fluid (SBF). Cytotoxicity was evaluated using MTT assay, while bioactivity was evaluated using mineralization and gene expression assays (Runx-2 & ALP).

RESULTS

The lowest FS and FT at 24h was attained with β-CS resin, while all the other tested materials exhibited a decrease in FS after prolonged storage in SBF. β-CS-Zn maintained a stable FT after 30-day SBF aging. Incorporation of bioactive micro-fillers had no negative effect on the biocompatibility of the experimental materials tested in this study. The inclusion of zinc-doped fillers significantly increased the cellular remineralization potential and expression of the osteogenic genes Runx2 and ALP (p<0.05).

SIGNIFICANCE

The innovative materials tested in this study, in particular those containing β-CS-Zn and BAG-Zn may promote cell differentiation and mineralization. Thus, these materials might represent suitable therapeutic pulp protection materials for minimally invasive and atraumatic restorative treatments.

The Use of Optical Coherence Tomography in Dental Diagnostics: A State-of-the-Art Review

Optical coherence tomography provides sections of tissues in a noncontact and noninvasive manner. The device measures the time delay and intensity of the light scattered or reflected from biological tissues, which results in tomographic imaging of their internal structure. This is achieved by scanning tissues at a resolution ranging from 1 to 15 μm. OCT enables real-time in situ imaging of tissues without the need for biopsy, histological procedures, or the use of X-rays, so it can be used in many fields of medicine. Its properties are not only particularly used in ophthalmology, in the diagnosis of all layers of the retina, but also increasingly in cardiology, gastroenterology, pulmonology, oncology, and dermatology. The basic properties of OCT, that is, noninvasiveness and low wattage of the used light, have also been appreciated in analytical technology by conservators, who use it to identify the quality and age of paintings, ceramics, or glass. Recently, the OCT technique of visualization is being tested in different fields of dentistry, which is depicted in the article.

Biomineralization: From Material Tactics to Biological Strategy

Biomineralization is an important tactic by which biological organisms produce hierarchically structured minerals with marvellous functions. Biomineralization studies typically focus on the mediation function of organic matrices on inorganic minerals, which helps scientists to design and synthesize bioinspired functional materials. However, the presence of inorganic minerals may also alter the native behaviours of organic matrices and even biological organisms. This progress report discusses the latest achievements relating to biomineralization mechanisms, the manufacturing of biomimetic materials and relevant applications in biological and biomedical fields. In particular, biomineralized vaccines and algae with improved thermostability and photosynthesis, respectively, demonstrate that biomineralization is a strategy for organism evolution via the rational design of organism-material complexes. The successful modification of biological systems using materials is based on the regulatory effect of inorganic materials on organic organisms, which is another aspect of biomineralization control. Unlike previous studies, this study integrates materials and biological science to achieve a more comprehensive view of the mechanisms and applications of biomineralization.

Three-dimensional imaging technologies: a priority for the advancement of tissue engineering and a challenge for the imaging community

Tissue engineering/regenerative medicine (TERM) is an interdisciplinary field that applies the principle of engineering and life sciences to restore/replace damaged tissues/organs with in vitro artificially-created ones. Research on TERM quickly moves forward. Today newest technologies and discoveries, such as 3D-/bio-printing, allow in vitro fabrication of ex-novo made tissues/organs, opening the door to wide and probably never-ending application possibilities, from organ transplant to drug discovery, high content screening and replacement of laboratory animals. Imaging techniques are fundamental tools for the characterization of tissue engineering (TE) products at any stage, from biomaterial/scaffold to construct/organ analysis. Indeed, tissue engineers need versatile imaging methods capable of monitoring not only morphological but also functional and molecular features, allowing three-dimensional (3D) and time-lapse in vivo analysis, in a non-destructive, quantitative, multidimensional analysis of TE constructs, to analyze their pre-implantation quality assessment and their fate after implantation. This review focuses on the newest developments in imaging technologies and applications in the context of requirements of the different steps of the TERM field, describing strengths and weaknesses of the current imaging approaches.

Quantitative characterization and micro-CT mineral mapping of natural fissural enamel lesions

OBJECTIVES

The aim of this study was to characterize the mineral distribution pattern of natural fissural enamel lesions and to quantify structural parameters and mineral density of these lesions in comparison to proximal white spot enamel lesions.

METHODS

Imaging was undertaken using a high-resolution desktop micro-computed tomography system. A calibration equation was used to transform the grey level values of images into true mineral density values. The value of lesion parameters including the mineral density and the thickness of the surface layer of the enamel lesion were extracted from mineral density profiles.

RESULTS

The thickness of the surface layer showed variation among different lesions and it ranged from 0-90 μm in proximal lesions and 0-137 μm in fissural lesions. The average thickness of surface layer in fissural lesions was significantly higher than smooth surface proximal lesions. Sound fissural enamel showed lower mineral density compared to proximal enamel.

CONCLUSION

Micro-CT and the suggested de-noising and visualization method provide an efficient high-resolution approach for non-destructive evaluation of fissural lesions. Using these methods, the current study revealed the exclusive pattern and structure of fissural enamel lesions which may provide a basis for future studies on prevention and remineralization of these lesions.

CLINICAL SIGNIFICANCE

The common demineralization pattern of fissural lesions, which indicates the extension of the lesion in two directions towards the pulp horns, may explain the early inflammation and symptoms of the pulp in fissural lesions even when the lesion base appears far from the pulp roof in normal radiographs. In addition, the presence of the surface layer, indicates that vigorous probing of the occlusal fissures may lead to breakage and cavitation of the enamel lesions.