Effect of side-group methylation on the performance of methacrylamides and methacrylates for dentin hybridization

In Search of Novel Degradation-Resistant Monomers for Adhesive Dentistry: A Systematic Review and Meta-Analysis

This study aimed to assess whether degradation-resistant monomers included in experimental dental adhesives can improve long-term bond strength compared to conventional monomers. This study followed the latest PRISMA guidance (2020). The search for the systematic review was carried out in four electronic databases: PubMed/Medline, Scopus, SciELO and EMBASE, without restrictions on the year of publication and language. The last screening was conducted in July 2022. Interventions included were in vitro studies on experimental dental adhesives that tested short-term and long-term bond strength, but also water sorption and solubility data when available, in extracted human molars. Meta-analyses were performed using Rstudio v1.4.1106. A summary table analyzing the individual risk of bias was generated using the recent RoBDEMAT tool. Of the 177 potentially eligible studies, a total of 7 studies were included. Experimental monomers with acrylamides or methacrylamide−acrylamide hybrids in their composition showed better results of aged bond strength when compared to methacrylate controls (p < 0.05). The experimental monomers found better sorption and solubility compared to controls and were significantly different (p < 0.001). It is possible to achieve hydrolytically resistant formulations by adding novel experimental monomers, with chemical structures that bring benefit to degradation mechanisms.

Triacrylamide-Based Adhesives Stabilize Bonds in Physiologic Conditions

In this study, an acrylamide-based adhesive was combined with a thiourethane-based composite to improve bond stability and reduce polymerization stress, respectively, of simulated composite restorations. The stability testing was conducted under physiologic conditions, combining mechanical and bacterial challenges. Urethane dimethacrylate was combined with a newly synthesized triacrylamide (TMAAEA) or HEMA (2-hydroxyethyl-methacrylate; control) to produce a 2-step total-etch adhesive system. Methacrylate-based composites (70 wt% silanized filler) were formulated, containing thiourethane oligomers at 0 (control) or 20 wt%. Standardized preparations in human third molars were restored; then, epoxy replicas were obtained from the occlusal surfaces before and after 7-d storage in water or with Streptococcus mutans biofilm, which was tested after storage in an incubator (static) or the bioreactor (mechanical challenge). Images were obtained from the replicas (scanning electron microscopy) and cross sections of the samples (confocal laser scanning microscopy) and then analyzed to obtain measurements of gap, bacterial infiltration, and demineralization. Microtensile bond strength of specimens stored in water or biofilm was assessed in 1-mm2 stick specimens. Data were analyzed with analysis of variance and Tukey's test (α = 0.05). HEMA-based materials had greater initial gap measurements, indicating more efficient bonding for the acrylamide materials. When tested in water, the triacrylamide-based adhesive had smaller gaps in the incubator or bioreactor. In the presence of biofilm, there was less difference among materials, but the acrylamide/thiourethane combination led to statistically lower gap formation in the bioreactor. HEMA and TMAAEA-based adhesives produced statistically similar microtensile bond strengths after being stored in water for 7 d, but after the same period with biofilm-challenged specimens, the TMAAEA-based adhesives were the only ones to retain the initial bond strength values. The use of a stable multiacrylamide-based adhesive led to the preservation of the resin-dentin bonded interface after a physiologically relevant challenge. Future studies will include a multispecies biofilm model.