The effect of accelerated aging on crystalline structures and optical properties of different monolithic zirconia: A qualitative systematic review

Advances in zirconia-based dental materials: Properties, classification, applications, and future prospects

OBJECTIVES

Zirconia (ZrO2) ceramics are widely used in dental restorations due to their superior mechanical properties, durability, and ever-improving translucency. This review aims to explore the properties, classification, applications, and recent advancements of zirconia-based dental materials, highlighting their potential to revolutionize dental restoration techniques.

STUDY SELECTION, DATA AND SOURCES

The most recent literature available in scientific databases (PubMed and Web of Science) reporting advances of zirconia-based materials within the dental field is thoroughly examined and summarized, covering the major keywords "dental zirconia, classification, aesthetic, LTD, applications, manufacturing, surface treatments".

CONCLUSIONS

An exhaustive overview of the properties, classifications, and applications of dental zirconia was presented, alongside an exploration of future prospects and potential advances. This review highlighted the importance of addressing challenges such as low-temperature degradation resistance and optimizing the balance between mechanical strength and translucency. Also, innovative approaches to improve the performances of zirconia as dental material was discussed.

CLINICAL SIGNIFICANCE

This review provides a better understanding of zirconia-based dental biomaterials for dentists, helping them to make better choice when choosing a specific material to fabricate the restorations or to place the implant. Moreover, new generations of zirconia are still expected to make progress on key issues such as the long-term applications in dental materials while maintaining both damage resistance and aesthetic appeal, defining the directions for future research.

Fatigue and failure mode analyses of glass infiltrated 5Y-PSZ bonded onto dentin analogues

The purpose of this study was to evaluate the fatigue survival of 5Y-PSZ zirconia infiltrated with an experimental glass and bonded onto dentin analogues. Disc-shaped specimens of a 5Y-PSZ (Katana UTML Kuraray Noritake) were cemented onto dentin analogs (NEMA G10) and divided into four groups (n = 15): Zctrl Group (control, without infiltration); Zglz Group (Glaze, compression surface); Zinf-comp Group (Experimental Glass, compression surface); Zinf-tens Group (Experimental Glass, tension surface). Surface treatments were varied. Cyclic fatigue loading, oblique transillumination, stereomicroscope examination, and scanning electron microscopy were performed. Fatigue data were analyzed (failure load and number of cycles) using survival analysis (Kaplan-Meier and Log-Rank Mantel-Cox). There was no statistically significant difference in fatigue survival between the Zglz, Zctrl, and Zinf-comp groups. The Zinf-tens group presented a significantly higher failure load when compared to the other groups and exhibited a different failure mode. The experimental glass effectively infiltrated the zirconia, enhancing structural reliability, altering the failure mode, and improving load-bearing capacity over more cycles, particularly in the group where the glass was infiltrated into the tensile surface of the zirconia. Glass infiltration into 5Y-PSZ zirconia significantly enhanced structural reliability and the ability to withstand loads over an increased number of cycles. This approach has the potential to increase the durability of zirconia restorations, reducing the need for replacements and save time and resources, promoting efficiency in clinical practice.

Effect of femtosecond laser induced surface patterns on the flexural strength of monolithic zirconia

To investigate how patterns generated by femtosecond (fs) laser and femtosecond laser power affect the surface roughness (Ra) and biaxial flexural strength (BFS) of monolithic zirconia. Eighty disk-shaped zirconia specimens were divided into eight subgroups (n = 10): Control (C), airborne-particle abrasion (APA), 400 mW fs laser (spiral [SP(400)], square [SQ(400)], circular [CI(400)]), and 700 mW fs laser ([SP(700)], [SQ(700)], [CI(700)]). Ra values were calculated by using a surface profilometer. One additional specimen per group was analyzed with scanning electron microscopy and x-ray diffractometry. BFS values were obtained by using the piston-on-3-ball test. One-way ANOVA and either Tukey's HSD (BFS) or Tamhane's T2 (Ra) tests were used to evaluate data (α = 0.05). Regardless of the pattern and power, fs laser groups had higher Ra than C and APA, while SP groups had lower Ra than CI and SQ groups (p ≤ 0.004). For each pattern, Ra increased with higher laser power (p < 0.001), while the laser power did not affect the BFS (p ≥ 0.793). CI and SQ groups had lower BFS than the other groups (p ≤ 0.040), whereas SP groups had similar BFS to C and APA (p ≥ 0.430). Fs laser microstructuring with spiral surface pattern increased the Ra without jeopardizing the BFS of zirconia. Thus, this treatment might be an option to roughen tested zirconia.

Translucency of recent zirconia materials and material-related variables affecting their translucency: a systematic review and meta-analysis

BACKGROUND

Recent forms of translucent zirconia material have been developed, offering a wide range of options and varieties for enhancing aesthetics, making it a preferred choice in the field of prosthetic dentistry. However, there is insufficient understanding regarding the recent types of zirconia materials and their optical behavior. Understanding the variables that influence the translucency of zirconia and identifying strategies to enhance its esthetics are crucial.

PURPOSE

The current systemic review highlights a comprehensive understanding of different zirconia generations in relation to their optical characteristics and evaluates material-related variables affecting their translucency.

METHODS

The present review studied in-vitro studies that evaluated the optical characteristics of different yttria content of yttria stabilized materials. The topics explored were: (1) the different zirconia material generations and their optical behavior; (2) material-related factors that affect their translucency. The research was restricted to online publication in the English language from July 1, 2010, to July 31, 2023, using PubMed, Scopus, and Science Direct resources. The search key terms and their combinations were "zirconia," "translucent zirconia," "cubic zirconia," "highly translucent zirconia," "yttria partially stabilized zirconia," "monolithic zirconia," "translucency," "optical properties," and "light transmission."

RESULTS

The data obtained from fifty-three studies addressed the optical characteristics of various zirconia generations. They reported that changing yttria content had a significant impact on translucency. Different kinds of zirconia ceramics of the same generation have varying translucencies. Achieving optimum aesthetics with monolithic zirconia is challenging due to factors related to material aspects such as the presence of additives, point defects, microstructure, thickness, phase distribution, and sintering conditions.

CONCLUSIONS

Newly developed monolithic dental zirconia ceramics have improved aesthetics and translucency. However, additional research is necessary to evaluate their performance and long-term durability.

TRIAL REGISTRATION

This systematic review was registered in PROSPERO, under number CRD42023474482.

Effect of low-temperature degradation on the fatigue performance of dental strength-gradient multilayered zirconia restorations

OBJECTIVES

Fatigue and low-temperature degradation (LTD) are the main factors contributing to zirconia restoration failure. This study evaluated the effect of LTD on the fatigue performance of the novel "strength & shade-gradient" multilayered zirconia restorations.

METHODS

Discs (15 mm × 1.2 mm) of each yttria content layer from a newly developed strength-gradient multilayered zirconia were fabricated and under accelerated aging in an autoclave at 134℃ for 0 h, 32 h, and 64 h. Then, the phase transformation, microstructure, and mechanical properties after LTD were assessed. In addition, the crown samples, including the multi-Zir, 3Y-Zir, and 5Y-Zir were fabricated, and their monotonic and fatigue load before and after LTD, percentage of fatigue degradation (Sd) and the fracture morphology were investigated. Statistical analyses were performed using paired samples t-test (α' = α/3 = 0.017), one-way ANOVA and Weibull analysis.

RESULTS

After LTD, the phase transformation, surface roughness, depth of transformed zone, and residual stress were increased and inversely associated with the yttria content. The indentation elastic modulus and hardness after LTD decreased; however, there was no significant difference between the different yttria content layers. The monotonic and fatigue load of multi-Zir restorations decreased, but their Weibull modulus increased, and Sd decreased, similar to 3Y-Zir. The crack origin was associated with the cervical region.

CONCLUSION

These results show that although LTD reduces the absolute fatigue strength of strength-gradient multilayered zirconia restorations, it also reduces the effect of cyclic fatigue itself on the strength of zirconia (relative to monotonic strength), which might be due to the increase of residual stress.

CLINICAL SIGNIFICANCE

The novel "strength & shade-gradient" multilayered zirconia restorations show a promising performance during in vitro LTD and fatigue test and their reliability to some extent is comparable to 3Y-Zir. Yet, further in vivo longitudinal studies are warranted to confirm their precise performance.

Effect of artificial aging on optical properties and crystalline structure of high-translucency zirconia

PURPOSE

To investigate the effect of different in vitro aging protocols on the optical properties and crystalline structure of high-translucency (HT) zirconia.

MATERIALS AND METHODS

Thirty-six specimens of HT and extra-high translucency (XT) zirconia were divided into three groups: control (CO)-no treatment; hydrothermal aging (HA)-autoclave aging for 12.5 h at 134°C, 2 bar; clinically related aging (CRA)-aging in the chewing simulator for 1.2 million cycles, followed by 50,000 thermocycles (5-55°C) and immersion in HCl (pH 1.2) for 15 h. Optical properties, crystalline structure, and surface roughness were analyzed and compared using analysis of variance (5% significance level).

RESULTS

There was no statistically significant effect of aging on translucency (p = 0.10), but CRA promoted the development of a high contrast ratio (p = 0.03). Aging did not cause significant color changes for HT (p = 0.65) or XT (p = 0.36). The proportion of monoclinic crystals increased to 40% for HT-zirconia after HA and 5% after CRA. No monoclinic crystals were detected for XT groups. There was no effect of aging on surface roughness (p = 0.77).

CONCLUSIONS

Although hydrothermal aging has been widely used to verify zirconia crystalline stability, it did not generate an effect similar to clinically related aging on the optical properties and crystalline structure of zirconia. HA affected the crystalline structure of HT-zirconia, and CRA compromised the optical properties of XT zirconia.