Development of anodic and cathodic blisters at a model Zn/epoxy interface studied using local electrochemical impedance

Electrochemical Impedance Measurements in Scanning Ion Conductance Microscopy

Electrochemical impedance spectroscopy (EIS) is a versatile tool for electrochemistry, particularly when applied locally to reveal the properties and dynamics of heterogeneous interfaces. A new method to generate local electrochemical impedance spectra is outlined, by applying a harmonic bias between a quasi-reference counter electrode (QRCE) placed in a nanopipet tip of a scanning ion conductance microscope (SICM) and a conductive (working electrode) substrate (two-electrode setup). The AC frequency can be tuned so that the magnitude of the impedance is sensitive to the tip-to-substrate distance, whereas the phase angle is broadly defined by the local capacitive response of the electrical double layer (EDL) of the working electrode. This development enables the surface topography and the local capacitance to be sensed reliably, and separately, in a single measurement. Further, self-referencing the probe impedance near the surface to that in the bulk solution allows the local capacitive response of the working electrode substrate in the overall AC signal to be determined, establishing a quantitative footing for the methodology. The spatial resolution of AC-SICM is an order of magnitude larger than the tip size (100 nm radius), for the studies herein, due to frequency dispersion. Comprehensive finite element method (FEM) modeling is undertaken to optimize the experimental conditions and minimize the experimental artifacts originating from the frequency dispersion phenomenon, and provides an avenue to explore the means by which the spatial resolution could be further improved.

Corrosion Inhibition at Scribed Locations in Coated AA2024-T3 by Cerium- and DMTD-Loaded Natural Silica Microparticles under Continuous Immersion and Wet/Dry Cyclic Exposure

Earlier studies on cerium-loaded naturally occurring silica microparticles (i.e., diatomaceous earth) demonstrated the potential to efficiently protect small scratches in epoxy-coated AA2024-T3 panels during relatively short immersion times. The current work investigates the potential of such inhibitor-loaded microparticles to protect wide and deep scribes (up to 1 mm wide) in long-time immersion testing and during cyclic (wet/dry) conditions. For this, cerium nitrate and 2,5-dimercaptothiadiazole (DMTD) were used as inorganic and organic corrosion inhibitors. The corrosion protection was evaluated using a hyphenated real-time optics/electrochemistry method and two individual local techniques measuring oxygen concentration and electrochemical impedance (LEIM) inside the scribe. SEM/EDS was used to analyze the samples after exposure. The results show significant levels of corrosion protection at damaged locations at low cerium concentrations (3.7 wt % Ce³⁺ relative to the total coating mass) during 30 days of immersion in salt solution. However, for a given scribe geometry, the protection was found to be dependent on the electrolyte volume with larger electrolyte/exposed metal ratios leading to short protection time. A partial replacement of the Ce³⁺ by DMTD in the microcarriers resulted in a higher degree of passivation than when DMTD was used alone. Wet/dry cyclic exposure tests showed that cyclic conditions can increase the buildup of stable inhibitor-containing layers in the case of cerium-loaded silica microparticles. This underlines the need for more research using wet/dry exposure conditions.