AC and DC studies of the pitting corrosion of Al in perchlorate solutions

Perchlorate reduction during electrochemically induced pitting corrosion of zero-valent titanium (ZVT)

Zero-valent metals and ionic metal species are a popular reagent for the abatement of contaminants in drinking water and groundwater and perchlorate is a contaminant of increasing concern. However, perchlorate degradation using commonly used reductants such as zero-valent metals and soluble reduced metal species is kinetically limited. Titanium in the zero-valent and soluble states has a high thermodynamic potential to reduce perchlorate. Here we show that perchlorate is effectively reduced to chloride by soluble titanium species in a system where the surface oxide film is removed from ZVT and ZVT is oxidized during electrochemically induced pitting corrosion to produce reactive soluble species. The pitting potential of ZVT was measured as 12.77±0.04 V (SHE) for a 100 mM solution of perchlorate. The rate of perchlorate reduction was independent of the imposed potential as long as the potential was maintained above the pitting potential, but it was proportional to the applied current. Solution pH and surface area of ZVT electrodes showed negligible effects on rates of perchlorate reduction. Although perchlorate is effectively reduced during electrochemically induced corrosion of ZVT, this process may not be immediately applicable to perchlorate treatment due to the high potentials needed to produce active reductants, the amount of titanium consumed, the inhibition of perchlorate removal by chloride, and oxidation of chloride to chlorine.

Uniform and Pitting Corrosion Processes of Al, Al-6061, Al-Zn and Al-Cu Alloys Exposed to SCN- Solutions and the Effect of Some Inorganic Anions

The effect of the alloying elements and some inorganic inhibitors (WO4 2-, MoO4 2-, SiO3 2- and CrO4 2- anions) on the uniform and pitting corrosion characteristics of Al-6061, Al-4.5% Cu, Al-7.5% Cu, Al-6% Zn and Al-12% Zn alloys were studied in 0.04M KSCN solution. Susceptibility of the tested alloys towards pitting corrosion was investigated using transient (potentiostatic and galvanostatic) measurements. An independent method of chemical analysis, namely ICP-AES (inductively coupled plasma atomic emission spectroscopy) was also used to study the effect of the alloying elements and the tested inorganic anions on the uniform corrosion of these materials. Results obtained were compared with pure Al. ICP measurements revealed that the alloyed Cu and alloyed Zn enhance uniform corrosion of the Al samples, while WO4 2-, MoO4 2-, SiO3 2- and CrO4 2- anions suppressed it. Transient measurements showed that nucleation of pit takes place after an incubation time (t i). The rate of pit initiation and growth (t i -1 ) increased with increase in SCN- concentration, applied anodic current, applied anodic potential and solution temperature. This rate of pit initiation and growth decreased in presence of inorganic inhibitors to an extent depending on the concentration and type of the introduced inhibitor. Alloyed Zn was found to accelerate pitting attack, while alloyed Cu suppressed it. Among the tested Al alloys, Al-6061 presented the highest resistance towards uniform and pitting corrosion processes. SiO3 2- and CrO4 2- were the most efficient anions in inhibiting uniform and pitting corrosion processes of Al in these solutions.