One-pot synthesis of ternary alloy CuFePt nanoparticles anchored on reduced graphene oxide and their enhanced electrocatalytic activity for both methanol and formic acid oxidation reactions

Enhanced Electrocatalytic Performance of the FePt/PPy-C Composite toward Methanol Oxidation

A novel FePt/PPy-C composite nanomaterial has been designed and investigated as a methanol oxidation reaction (MOR) electrocatalyst. The FePt nanoparticles with an average diameter of about 3 nm have been prepared by the co-reduction method and then loaded onto the PPy-C composite support. The electrocatalytic performance is affected by the composition of the FePt nanoparticles. The experimental results indicated that the Fe1.5Pt1/PPy-C catalyst exhibited excellent catalytic activity and stability for MOR, with mass activity and specific activity of 1.76 A mgPt-1 and 2.71 mA cm-2, respectively, which are 5.18 and 4.60 times higher than that of the commercial Pt/C catalyst. Density functional theory (DFT) has been employed to simulate the electrical structures of catalyst supports, and the mechanism of the methanol oxidation process has been further analyzed. The heterojunctions of the PPy-C interface could accelerate the electron migration from the electrocatalytic center to the electrodes. The possibility of methanol oxidation has been improved effectively, which can be confirmed by the d-band center and CO adsorption energy on FePt nanoparticles in the DFT calculation results.

Recent Advances in Anode Electrocatalysts for Direct Formic Acid Fuel Cell-II-Platinum-Based Catalysts

Platinum-based catalysts have a long history of application in formic acid oxidation (FAO). The single metal Pt is active in FAO but expensive, scarce, and rapidly deactivates. Understanding the mechanism of FAO over Pt important for the rational design of catalysts. Pt nanomaterials rapidly deactivate because of the CO poisoning of Pt active sites via the dehydration pathway. Alloying with another transition metal improves the performance of Pt-based catalysts through bifunctional, ensemble, and steric effects. Supporting Pt catalysts on a high-surface-area support material is another technique to improve their overall catalytic activity. This review summarizes recent findings on the mechanism of FAO over Pt and Pt-based alloy catalysts. It also summarizes and analyzes binary and ternary Pt-based catalysts to understand their catalytic activity and structure relationship.

Low-Cost Pt Alloys for Heterogeneous Catalysis Predicted by Density Functional Theory and Active Learning

Pt is a key high-performing catalyst for important chemical conversions, such as biomass conversion and water splitting. Limited Pt reserves, however, demand that we identify more sustainable alternative catalyst materials for these processes. Here, we combine state-of-the-art graph neural networks and crystal graph machine learning representations with active learning to discover new, low-cost Pt alloy catalysts for biomass reforming and hydrogen evolution reactions. We identify 12 Pt-based alloys which have comparable catalytic activity to that of the exemplar Pt(111) surface. Notably, Cu₃Pt and FeCuPt₂ exhibit near identical catalytic performance as that of Pt(111). These results demonstrate the potential of machine learning for predicting new catalytic materials without recourse to expensive DFT geometry optimizations, the current bottleneck impeding high-throughput materials discovery. We also examine the performance of d-band theory in elucidating trends in binary and ternary Pt alloys.

A scalable synthesis of ternary nanocatalysts for a high-efficiency electrooxidation catalysis by microfluidics

Microfluidic synthesis has attracted extensive attention due to the ability for the multistep precise control of the synthesis parameters, continuous and reproducible preparation, and its ease of integration. However, its commercial application is still affected by its low production efficiency. In this case, we report a high-throughput continuous flow synthesis of highly dispersed PtFeCu/C nanocatalysts using a metal microchip setup with four parallel channels. The high flow rate and integrated channels enabled improving the throughput, whereby 1.33 g h^-1 of catalysts could be achieved with the flow rate of 1200 mL h^-1 under the experimental conditions. The as-prepared PtFeCu/C exhibited excellent performance, 1.94 times higher than Pt/C for methanol oxidation. More importantly, the yield of the PtFeCu/C nanocatalysts could be further increased through designing numerous parallel channels, which might provide a promising approach for large-scale commercialization of the catalysts. Such a high-throughput fabrication pathway is significant for the large-scale industrial production of nanomaterials.

Propitious Dendritic Cu2O-Pt Nanostructured Anodes for Direct Formic Acid Fuel Cells

This study introduces a novel competent dendritic copper oxide-platinum nanocatalyst (nano-Cu₂O-Pt) immobilized onto a glassy carbon (GC) substrate for formic acid (FA) electro-oxidation (FAO); the prime reaction in the anodic compartment of direct formic acid fuel cells (DFAFCs). Interestingly, the proposed catalyst exhibited an outstanding improvement for FAO compared to the traditional platinum nanoparticles (nano-Pt) modified GC (nano-Pt/GC) catalyst. This was evaluated from steering the reaction mechanism toward the desired direct route producing carbon dioxide (CO₂); consistently with mitigating the other undesired indirect pathway producing carbon monoxide (CO); the potential poison deteriorating the catalytic activity of typical Pt-based catalysts. Moreover, the developed catalyst showed a reasonable long-term catalytic stability along with a significant lowering in onset potential of direct FAO that ultimately reduces the polarization and amplifies the fuel cell's voltage. The observed catalytic enhancement was believed to originate bifunctionally; while nano-Pt represented the base for the FA adsorption, nanostructured copper oxide (nano-Cu₂O) behaved as a catalytic mediator facilitating the charge transfer during FAO and providing the oxygen atmosphere inspiring the poison's (CO) oxidation at relatively lower potential. Surprisingly, moreover, nano-Cu₂O induced a surface retrieval of nano-Pt active sites by capturing the poisoning CO via "a spillover mechanism" to renovate the Pt surface for the direct FAO. Finally, the catalytic tolerance of the developed catalyst toward halides' poisoning was discussed.

Iron-containing platinum-based catalysts as cathode and anode materials for low-temperature acidic fuel cells: a review

Positive effect of ordering on the specific activity for oxygen reduction of Pt–Fe (1 : 1) catalysts.

A PtPdCu thin-film catalyst based on titanium nitride nanorod arrays with high catalytic performance for methanol electro-oxidation

Here, we present a novel MOR anode catalyst based on TiN nanorod arrays with high performance towards MOR.

A cobalt nanoparticle ion-implantation-modified indium tin oxide electrode for direct electrocatalytic oxidation of methanol in alkaline media

SEM images of the CoNPs/ITO electrode (A), and the CoNPs/ITO electrode exhibits a good electrocatalytic ability and stability towards direct methanol oxidation in alkaline medium (B, C and D).

Anchoring ternary CuFePd nanocatalysts on reduced graphene oxide to improve the electrocatalytic activity for the methanol oxidation reaction

A ternary CuFePd/rGO electrocatalyst was developed facilely, which exhibited improved performance compared to binary CuPd/rGO, FePd/rGO and Pd/rGO.