Hydrothermal synthesis and electrochemical performance of nanoparticle Li2FeSiO4/C cathode materials for lithium ion batteries

Hollow Hemispherical Lithium Iron Silicate Synthesized by an Ascorbic Acid-Assisted Hydrothermal Method as a Cathode Material for Li Ion Batteries

High-capacity and high-voltage cathode materials are required to meet the increasing demand for energy density in Li ion batteries. Lithium iron silicate (Li2FeSiO4) is a cathode material with a high theoretical capacity of 331 mAh·g-1. However, its poor conductivity and low Li ion diffusion coefficient result in poor capability, hindering practical applications. Morphology has an important influence on the properties of materials, and nanomaterials with hollow structures are widely used in electrochemical devices. Herein, we report a novel hollow hemispherical Li2FeSiO4 synthesized by a template-free hydrothermal method with the addition of ascorbic acid. The hollow hemispherical Li2FeSiO4 consisted of finer particles with a shell thickness of about 80 nm. After carbon coating, the composite was applied as the cathode in Li ion batteries. As a result, the hollow hemispherical Li2FeSiO4/C exhibited a discharge capacity as high as 192 mAh·g-1 at 0.2 C, and the average capacities were 134.5, 115.5 and 93.4 mAh·g-1 at 0.5, 1 and 2 C, respectively. In addition, the capacity increased in the first few cycles and then decayed with further cycling, showing a warm-up like behavior, and after 160 cycles the capacities maintained 114.2, 101.6 and 79.3 mAh·g-1 at 0.5, 1 and 2 C, respectively. Such a method of adding ascorbic acid in the hydrothermal reaction can effectively synthesize hollow hemispherical Li2FeSiO4 with the enhanced electrochemical performance.

Eggshell-Membrane-Derived Carbon Coated on Li2FeSiO4 Cathode Material for Li-Ion Batteries

Lithium iron orthosilicate (LFS) cathode can be prepared via the polyol-assisted ball milling method with the incorporation of carbon derived from eggshell membrane (ESM) for improving inherent poor electronic conduction. The powder X-ray diffraction (XRD) pattern confirmed the diffraction peaks without any presence of further impure phase. Overall, 9 wt.% of carbon was loaded on the LFS, which was identified using thermogravimetric analysis. The nature of carbon was described using parameters such as monolayer, and average surface area was 53.5 and 24 m2 g−1 with the aid of Langmuir and Brunauer–Emmett–Teller (BET) surface area respectively. The binding energy was observed at 285.66 eV for C–N owing to the nitrogen content in eggshell membrane, which provides more charge carriers for conduction. Transmission electron microscopy (TEM) images clearly show the carbon coating on the LFS, the porous nature of carbon, and the atom arrangements. From the cyclic voltammetry (CV) curve, the ratio of the anodic to the cathodic peak current was calculated as 1.03, which reveals that the materials possess good reversibility. Due to the reversibility of the redox mechanism, the material exhibits discharge specific capacity of 194 mAh g−1 for the first cycle, with capacity retention and an average coulombic efficiency of 94.7% and 98.5% up to 50 cycles.