INVESTIGATION OF THE ELECTROCHEMICAL AGING OF POLY(3-HEXILTIOPHENE) USING IMPEDANCE SPECTROSCOPY

Overoxidation of Intrinsically Conducting Polymers

Intrinsically conducting polymers may undergo significant changes of molecular structure and material properties when exposed to highly oxidizing conditions or very positive electrode potentials, commonly called overoxidation. The type and extent of the changes depend on the experimental conditions and chemical environment. They may proceed already at much lower rates at lower electrode potentials because some of the processes associated with overoxidation are closely related to more or less reversible redox processes employed in electrochemical energy conversion and electrochromism. These changes may be welcome for some applications of these polymers in sensors, extraction, and surface functionalization, but in many cases, the change of properties affects the performance of the material negatively, contributing to material and device degradation. This report presents published examples, experimental observations, and their interpretations in terms of both structural and of material property changes. Options to limit and suppress overoxidation are presented, and useful applications are described extensively.

In Situ Measurement of Voltage-Induced Stress in Conducting Polymers with Redox-Active Dopants

Minimization of stress-induced mechanical rupture and delamination of conducting polymer (CP) films is desirable to prevent failure of devices based on these materials. Thus, precise in situ measurement of voltage-induced stress within these films should provide insight into the cause of these failure mechanisms. The evolution of stress in films of polypyrrole (pPy), doped with indigo carmine (IC), was measured in different electrochemical environments using the multibeam optical stress sensor (MOSS) technique. The stress in these films gradually increases to a constant value during voltage cycling, revealing an initial break-in period for CP films. The nature of the ions involved in charge compensation of pPy[IC] during voltage cycling was determined from electrochemical quartz crystal microbalance (EQCM) data. The magnitude of the voltage-induced stress within pPy[IC] at neutral pH correlated with the radius of the hydrated mobile ion in the order Li(+) > Na(+) > K(+). At acidic pH, the IC dopant in pPy[IC] undergoes reversible oxidation and reduction within the range of potentials investigated, providing a secondary contribution to the observed voltage-induced stress. We report on the novel stress response of these polymers due to the presence of pH-dependent redox-active dopants and how it can affect material performance.