Enhanced electrochemical performance of Na2/3[Mn0.55Ni0.30Co0.15]O2 positive electrode in sodium-ion batteries by functionalized multi-walled carbon nanotubes

Promoting threshold voltage of P2-Na0.67Ni0.33Mn0.67O2 with Cu2+ cation doping toward high-stability cathode for sodium-ion battery

P2-type Na0.67Ni0.33Mn0.67O2 has attracted considerable attraction as a cathode material for sodium-ion batteries owing to its high operating voltage and theoretical specific capacity. However, when the charging voltage is higher than 4.2 V, the Na0.67Ni0.33Mn0.67O2 cathode undergoes a detrimental irreversible phase transition of P2-O2, leading to a drastic decrease in specific capacity. To address this challenge, we implemented a Cu-doping strategy (Na0.67Ni0.23Cu0.1Mn0.67O2) in this work to stabilize the structure of the transition metal layer. The stabilization strategy involved reinforcing the transition metal-oxygen (TMO) bonds, particularly the MnO bond and inhibiting interlayer slip during deep desodiation. As a result, the irreversible phase transition voltage is delayed, with the threshold voltage increasing from 4.2 to 4.4 V. Ex-situ X-ray diffraction measurements revealed that the Na0.67Ni0.23Cu0.1Mn0.67O2 cathode maintains the P2 phase within the voltage window of 2.5-4.3 V, whereas the P2-Na0.67Ni0.33Mn0.67O2 cathode transforms entirely into O2-type Na0.67Ni0.33Mn0.67O2 when the voltage exceeds 4.3 V. Furthermore, absolute P2-O2 phase transition of the Na0.67Ni0.23Cu0.1Mn0.67O2 cathode occurred at 4.6 V, indicating that Cu2+ doping enhances the stability of the layer structure and increases the threshold voltage. The resulting Na0.67Ni0.23Cu0.1Mn0.67O2 cathode exhibited superior electrochemical properties, demonstrating an initial reversible specific capacity of 89.1 mAh/g at a rate of 2C (360 mA g-1) and retaining more than 78 % of its capacity after 500 cycles.

CeO2-modified P2-Na-Co-Mn-O cathode with enhanced sodium storage characteristics

To improve the cycling stability and dynamic properties of layered oxide cathodes for sodium-ion batteries, surface modified P2-Na_0.67Co_0.25Mn_0.75O₂ with different levels of CeO₂ was successfully synthesized by the solid-state method. X-ray photoelectron spectra, X-ray diffraction and Raman spectra show that the P2-structure and the oxidation state of cobalt and manganese of the pristine oxide are not affected by CeO₂ surface modification, and a small amount of Ce⁴⁺ ions have been reduced to Ce³⁺ ions, and a few Ce ions have entered the crystal lattice of the P2-oxide surface during modification with CeO₂. In a voltage range of 2.0-4.0 V at a current density of 20 mA g^-1, 2.00 wt% CeO₂-modified Na_0.67Co_0.25Mn_0.75O₂ delivers a maximum discharge capacity of 135.93 mA h g^-1, and the capacity retentions are 91.96% and 83.38% after 50 and 100 cycles, respectively. However, the pristine oxide presents a low discharge capacity of 116.14 mA h g^-1, and very low retentions of 39.83% and 25.96% after 50 and 100 cycles, respectively. It is suggested that the CeO₂ modification enhances not only the maximum discharge capacity, but also the electric conductivity and the sodium ion diffusivity, resulting in a significant enhancement of the cycling stability and the kinetic characteristics of the P2-type oxide cathode.

A study on electrochemical properties of P2-type Na–Mn–Co–Cr–O cathodes for sodium-ion batteries

The comprehensive electrochemical properties of P2-type Na–Co–Mn–O cathodes for sodium ion batteries could be significantly enhanced by optimal Cr-doping.