Highly active and stable tin-doped perovskite-type oxides as cathode materials for solid oxide fuel cells

A-Site Engineering of the High-Entropy Perovskite Pr0.4La0.4Ba0.4Sr0.4Ca0.4Fe2O5+δ Cathode for Intermediate-Temperature SOFCs

Mixed-oxygen ionic and electronic conduction is crucial for the cathode materials of solid oxide fuel cells, ensuring high efficiency and low-temperature operation. However, the electronic and oxygen ionic conductivity of traditional Fe-based layered perovskite cathode materials is low, resulting in insufficient oxygen reduction reactivity. Herein, a type of high-entropy perovskite oxide consisting of five equimolar metals, Pr0.4La0.4Ba0.4Sr0.4Ca0.4Fe2O5+δ (PLBSCF), a high-performance cobalt-free cathode derived from the PrBaFe2O5+δ (PBF), is proposed. Such A-site engineering could not only increase the oxygen vacancy concentration of PLBSCF but also give higher conductivity than PBF, thus significantly reducing the polarization impedance of the symmetric cell to only 0.052 Ω·cm2 at 750 °C. The good output performance of a single cell is also realized. The peak power density of the single cell with PLBSCF-Ce0.9Gd0.1O2-δ (GDC) as the cathode at 750 °C was 0.853 W·cm-2. Additionally, the single cell with the PLBSCF cathode exhibits a good durable performance of 100 h at 750 °C. Combining the distribution of relaxation time analysis, it can be seen that the enhancement of the oxygen reduction reaction is due to the reduction of intermediate-frequency and low-frequency resistance, indicating an improvement in the charge transfer process and adsorption/dissociation process of molecular oxygen.

Cobalt-Free Double Perovskite Oxide as a Promising Cathode for Solid Oxide Fuel Cells

Double perovskite oxide PrBaFe₂O_5+δ is a potential cathode material for intermediate-temperature solid oxide fuel cells. To improve its electrochemical performance, the trivalent element Ga is investigated to partially replace Fe, forming PrBaFe_2-xGa_xO_5+δ (PBFGx, x = 0.05, 0.1, and 0.15). The doping effects on physicochemical properties and electrochemical properties are analyzed regarding the phase structures, element valence states, amount of oxygen vacancies, content of oxygen species, oxygen surface exchange coefficients (k_chem), electrochemical polarization resistance, and single-cell performance. Specifically, PBFG0.1 exhibits improved k_chem, such as a 19% improvement from 4.09 × 10^-4 to 4.86 × 10^-4 cm s^-1 at 750 °C, due to the increased concentration of reactive oxygen species and oxygen vacancies. Consequently, the interfacial polarization resistance is decreased by 28% from 0.057 to 0.041 Ω cm² at 800 °C. The subreaction steps of the oxygen reduction reaction in the PBFG0.1 cathode are further investigated, which suggests that the oxygen dissociation process is greatly enhanced by doping Ga. Meanwhile, doping Ga increases the peak power density of the anode-supported single cell by 36% from 629 to 856 mW cm^-2 at 800 °C. The single cell with the PBFG0.1 cathode also exhibits good stability in 100 h of long-term operation at 750 °C.