Electropolymerization of [2 × 2] grid-type cobalt(II) complex with thiophene substituted dihydrazone ligand

Investigation of electrochemistry and electrochromic performance of metallopolymer formed by electropolymerization of Fe(II) complex with triphenylamine-hydrazone ligand

The complex of Fe(II) ions of general formula [FeL2](BF4)2 with triphenylamine-hydrazone ligand L has been synthesized and characterized. Oxidative electropolymerization of the complex proceeded smoothly on the working electrode producing homogenous thin film of metallopolymer. The film thickness and morphology of the layer was investigated by microscopy techniques such as SEM and AFM, and the composition of the film was confirmed by XPS analysis. It was found that after fifty successive oxidation/reduction cycles the film of thickness 120 nm was formed on the electrode surface. The metallopolymer was also characterized using cyclic voltammetry and spectroelectrochemical methods. The film was found to change its color from yellow to green-blue, high change in transmittance of 60% at 770 nm and good electrochemical stability during 375 cycles of switching of the potential between -0.1 V and +1.5 V, due to the presence of metal ions that link two ligand molecules resulting in formation of highly cross-linked film. The switching times (coloration and bleaching) were calculated to be 34.2 s and 7.3 s, respectively. Coloration efficiency of the formed film of polymeric complex was found to be 144 cm 2 /C.

New Cu(i) square grid-type and Ni(ii) triangle-type complexes: synthesis and characterization of effective binders of DNA and serum albumins

Metallosupramolecular square grid-type complex [Cu4L4]4+ and triangle-type complex [Ni3L3]6+ as a potential strategy for obtaining versatile metal-based DNA, Serum Albumin (SA) and DNA binders.

Toward Electrochromic Metallopolymers: Synthesis and Properties of Polyazomethines Based on Complexes of Transition-Metal Ions

The tridentate ligand L and its complexes with transition-metal ions have been prepared and characterized. The polycondensation reactions of transition-metal complexes with different dialdehydes led to the formation of transition-metal-complex-based polyazomethines, which have been obtained by on-substrate polymerization, and their electrochemical and electrochromic performance have been investigated. The most interesting properties are exhibited by polymers of Fe(II) and Cu(II) ions obtained by the reaction of the appropriate complexes with a triphenylamine-based dialdehyde. Fe(II) polymer P1 undergoes a reversible oxidation/reduction process and a color change from orange to gray due to the oxidation of Fe(II) to Fe(III) ions concomitant with the oxidation of the triphenylamine group. Its electrochromic properties such as long-term stability, switching times, and coloration efficiencies have been investigated, providing evidence of the utility of the on-substrate polycondensation reaction in the formation of thin films of electrochromic metallopolymers.

Reductive Electropolymerization and Electrochromism of Iron(II) Complex with Styrene-Based Ligand

The benzimidazole-based ligand containing polymerizable styrene group has been prepared via condensation of picolinaldehyde derivative containing styrene moiety and benzimidazole-based hydrazine. The ligand reacted with iron(II) tetrafluoroborate and iron(II) trifluoromethanesulfonate giving red-brown complexes of Fe(II) ions of formula [FeL₂]X₂, where X = CF₃SO₃⁻ (1) or BF₄⁻ (2). Reductive electropolymerization was used to obtain a thin layer of the polymeric complex, poly-1. Further investigation of electrochemical properties of the compound by cyclic voltammetry showed two quasi-reversible redox processes assigned to electrooxidation and electroreduction of the polymer. Spectroelectrochemical measurements confirmed that the polymer undergoes the color changes during oxidation and reduction process. The polymer in its neutral state (Fe(II)) is yellow and it exhibits absorption band at 370 nm, after oxidation to Fe(III) state absorption band shifts to 350 nm and the polymer is almost colorless. While the metal ions are reduced to Fe(I) absorption band at around 410 nm has been observed and the polymer changed its color to intense yellow. The stability of the polymer during multiple oxidation/reduction cycles has also been investigated.

Transmissive to blackish-green NIR electrochromism in a Co(II)-based interfacial co-ordination thin film

Herein, a Co(ii)-based metallo-polymer (Co-tpy-L) with a three armed non-conjugated terpyridine ligand is synthesized using solvent-solvent interfacial polymerization. The thin film exhibits durable transmissive-to-blackish green electrochromism, selectively covering both the visible and NIR regions with a moderate voltage range of -1.4 to 0 V.