Synthesis of perovskite bismuth ferrite embedded nitrogen-doped Carbon (BiFeO3-NC) nanocomposite for energy storage application

Nickel vanadate nitrogen-doped carbon nanocomposites for high-performance supercapacitor electrode

A nickel-vanadium-based bimetallic precursor was produced using the polymerization process by urea-formaldehyde copolymers. The precursor was then calcined at 800 °C in an argon ambiance to form a Ni3V2O8-NC magnetic nanocomposite. Powerful techniques were used to study the physical characteristics and chemical composition of the fabricated Ni3V2O8-NC electrode. PXRD, Raman, and FTIR analyses proved that the crystal structure of Ni3V2O8-NC included N-doped graphitic carbon. FESEM and TEM analyses imaging showed the distribution of the Ni3V2O8 nanoparticles on the layered graphitic carbon structure. TEM images showed the prepared sample has a particle size of around 10-15 nm with an enhanced active site area of 146 m2/g, as demonstrated by BET analysis. Ni3V2O8-NC nanocomposite exhibits magnetic behaviors and a magnetization saturation value of 35.99 emu/g. The electrochemical (EC) studies of the synthesized Ni3V2O8-NC electrode proceeded in an EC workstation of three-electrode. In a 5 M potassium hydroxide as an electrolyte, the cyclic voltmeter exhibited an enhanced capacitance (CS) of 915 F/g at 50 mV/s. Galvanic charge-discharge (GCD) study also exhibited a superior capacitive improvement of 1045 F/g at a current density (It) of 10 A/g. Moreover, the fabricated Ni3V2O8-NC nanocomposite displays a good power density (Pt) of 356.67 W/kg, improved ion accessibility, and substantial charge storage. At the high energy density (Et) of 67.34 W h/kg, the obtained Pt was 285.17 W/kg. The enhanced GCD rate, cycle stability, and Et of the Ni3V2O8-NC magnetic nanocomposite nominate the sample as an excellent supercapacitor electrode. This study paves the way for developing effective, efficient, affordable, and ecologically friendly electrode materials.

Magnesium Bismuth Ferrite Nitrogen-Doped Carbon Nanomagnetic Perovskite: Synthesis and Characterization as a High-Performance Electrode in a Supercapacitor for Energy Storage

Bismuth ferrite (BiFeO₃) is regarded as an important ABO₃ perovskite in the areas of energy storage and electronics. A high-performance novel MgBiFeO₃-NC nanomagnetic composite (MBFO-NC) electrode was prepared using a perovskite ABO₃-inspired method as a supercapacitor for energy storage. The electrochemical behavior of the perovskite BiFeO₃ has been enhanced by magnesium ion doping in the basic aquatic electrolyte as the A-site. H₂-TPR revealed that the doping of Mg²⁺ ions at the Bi³⁺ sites minimizes the oxygen vacancy content and improves the electrochemical characteristics of MgBiFeO₃-NC. Various techniques were used to confirm the phase, structure, surface, and magnetic properties of the MBFO-NC electrode. The prepared sample showed an enhanced mantic performance and specific area with an average nanoparticle size of ∼15 nm. The electrochemical behavior of the three-electrode system was shown by cyclic voltammetry to have a significant specific capacity of 2079.44 F/g at 30 mV/s in 5 M KOH electrolyte. GCD analysis at a 5 A/g current density also showed an enhanced capacity improvement of 2159.88 F/g, which is 3.4× higher than that of pristine BiFeO₃. At the power density of 5284.83 W/kg, the constructed MBFO-NC//MBFO-NC symmetric cell showed an exceptional energy density of 730.04 W h/kg. The MBFO-NC//MBFO-NC symmetric cell was employed as a direct practical application of the electrode material to entirely brighten the laboratory panel, which had 31 LEDs. This work proposes the utilization of duplicate cell electrodes made of MBFO-NC//MBFO-NC in portable devices for daily use.

Recent Development Strategies for Bismuth-Driven Materials in Sustainable Energy Systems and Environmental Restoration

Bismuth(Bi)-based materials have gained considerable attention in recent decades for use in a diverse range of sustainable energy and environmental applications due to their low toxicity and eco-friendliness. Bi materials are widely employed in electrochemical energy storage and conversion devices, exhibiting excellent catalytic and non-catalytic performance, as well as CO₂ /N₂ reduction and water treatment systems. A variety of Bi materials, including its oxides, chalcogenides, oxyhalides, bismuthates, and other composites, have been developed for understanding their physicochemical properties. In this review, a comprehensive overview of the properties of individual Bi material systems and their use in a range of applications is provided. This review highlights the implementation of novel strategies to modify Bi materials based on morphological and facet control, doping/defect inclusion, and composite/heterojunction formation. The factors affecting the development of different classes of Bi materials and how their control differs between individual Bi compounds are also described. In particular, the development process for these material systems, their mass production, and related challenges are considered. Thus, the key components in Bi compounds are compared in terms of their properties, design, and applications. Finally, the future potential and challenges associated with Bi complexes are presented as a pathway for new innovations.