Synthesis, characterization and degradation of a novel class of fluorescent poly[1,3-bis(p-carboxyphenoxy) propane: p-(carboxyethylformamido)benzoic anhydride] (P(CPP:CEFB))

Preparation, characterization and nasal delivery of alpha-cobrotoxin-loaded poly(lactide-co-glycolide)/polyanhydride microspheres

In this study, alpha-cobrotoxin was incorporated into the microspheres composed of poly(lactide-co-glycolide) (PLGA) and poly[1,3-bis(p-carboxy-phenoxy) propane-co-p-(carboxyethylformamido) benzoic anhydride] (P(CPP:CEFB)) and intranasally delivered to model rats in order to improve its analgesic activity. The microspheres with high entrapment efficiency (>80%) and average diameter of about 25 microm could be prepared by a modified water-in-oil-in-oil (w/o/o) emulsion solvent evaporation method. Scanning electron micrograph (SEM) study indicated that P(CPP:CEFB) content played a considerable role on the morphology and degradation of the microspheres. The presence of P(CPP:CEFB) in the microspheres increased their residence time at the surface of the nasal rat mucosa. The toxicity of the composite microspheres to nasal mucosa was proved to be mild and reversible. A tail flick assay was used to evaluate the antinociceptive activity of the microspheres after nasal administration. Compared with the free alpha-cobrotoxin and PLGA microspheres, PLGA/P(CPP:CEFB) microspheres showed an apparent increase in the strength and duration of the antinociceptive effect at the same dose of alpha-cobrotoxin (80 microg/kg body weight).

Novel Copolyanhydrides Combining Strong Inherent Fluorescence and a Wide Range of Biodegradability: Synthesis, Characterization and in vitro Degradation

In this work, a novel diacid monomer was synthesized in a very convenient scheme. The monomer is derived from naturally occurring products and emits strong fluorescence when polymerized to polyanhydride. The chemical structure of the monomer dCPS is as follows: HOC(O)ArOC(O)(CH2)2C(O)O--Ar--COOH. Copolyanhydrides composed of dCPS and sebacic acid were further prepared by melt copolycondensation, and characterized by IR, NMR, UV-Vis, DSC and fluorometry. The emission wavelength (lambda(em)) of the copolymers could be tuned by the excitation wavelength (lambda(ex)). Fluorescence intensity increased with the increase of dCPS content. The microspheres fabricated from the copolymer with dCPS content as low as 10% could be clearly visualized with fluorescence microscopy. Either blue or green images of the microspheres could be captured with an excitation of UV and visible light. The degradation rate of the copolyanhydrides decreased as the dCPS fraction increased, and the degradation duration could be modulated from several days to more than three months. In addition, it was found that the copolyanhydrides displayed surface degradation characteristics. In view of the advantages of the novel copolyanhydrides, such as easy preparation, unique inherent luminescent properties, and widely adjustable degradation rate, they might be useful for biomedical engineering.