Fabrication of high-performance poly(vinyl alcohol)/MgAl-layered double hydroxide nanocomposites

MgAl-LDH nanoflowers as a novel sensing material for high-performance humidity sensing

This work details a novel application of MgAl-LDH nanoflowers, applied in the fabrication of humidity sensors using quartz crystal microbalance (QCM). An oscillating circuit approach has been utilized to thoroughly investigate the humidity detection characteristics of QCM sensors that are fabricated using MgAl-LDH nanoflowers. The examination encompassed various parameters such as the sensors' response, humidity hysteresis, repeatability, and stability. Experimental results clearly indicate that these MgAl-LDH nanoflower-based QCM sensors exhibit a distinct logarithmic frequency response to varying moisture levels. Notably, the sensitivity of the sensors is intricately tied to the amount of MgAl-LDH nanoflowers utilized during the deposition process. Moreover, these sensors maintain remarkable stability across a wide humidity range spanning from 11% to 97% RH. Additionally, the MgAl-LDH nanoflower-based QCM sensors possess minimal humidity hysteresis and display swift dynamic response and recovery periods, further highlighting their potential for humidity detection applications.

Effect of Hydrogen Bonding on Dynamic Rheological Behavior of PVA Aqueous Solution

The rheological behavior of polyvinyl alcohol (PVA) aqueous solution is crucial to optimizing the processing technology and performance of PVA products. In this paper, the dynamic rheological behavior of PVA aqueous solution was investigated in detail. PVA solution with a concentration of 10 wt% showed unnormal rheological behaviors, that is, the liquid-like behavior in the high frequency (ω) region and the solid-like behavior in the low ω region. A storage modulus (G′) plateau appears in the relatively low ω region as a gel with a network structure. Different from conventional hydrogel, this plateau has a low modulus, and the corresponding size of the relaxation unit is estimated to be 554 nm, being higher than the size of a whole PVA chain. It is believed that the network mesh is formed by the intermolecular hydrogen bonding interactions among PVA chains. The relaxation time of these meshes is longer than the reptation time of a PVA chain. Based on the relaxation spectrum and calculation analysis, it is found that the destruction of intermolecular hydrogen bonds, such as by heating up, adding sodium dodecyl sulfate, and shear operation, will make the relaxation unit (mesh) larger and lead to the left shift of the intersection of G′ and loss modulus (G″). In a PVA solution with a high concentration, multiple meshes of various sizes could be formed and thus generate multiple relaxation peaks. The large-sized meshes mainly contribute to the left shift of the intersection of G′ and G″, and the small-sized meshes contribute to the high plateau modulus. The results in this paper offer a new angle to analyze polymer solutions with strong intermolecular interaction.

Structure and Mechanical Performance of Poly(vinyl Alcohol) Nanocomposite by Incorporating Graphitic Carbon Nitride Nanosheets

Owing to the high aspect ratio, the two-dimensional (2D) inorganic nanofillers have attracted extensive interest in the field of polymer reinforcement. In this work, graphitic carbon nitride (g-C₃N₄) nanosheets were obtained via thermal condensation of melamine and were then ultrasonically exfoliated in water, which was confirmed by atomic force microscopy (AFM) and TEM. Poly(vinyl alcohol) (PVA)/g-C₃N₄ nanocomposites were achieved by solution casting using water as the solvent. The structure and mechanical performance of PVA/g-C₃N₄ nanocomposites were studied. It was found that the g-C₃N₄ nanosheets were well dispersed in the PVA matrix. The introduction of g-C₃N₄ nanosheets increased the glass transition temperature and crystallinity of the nanocomposites, leading to the improved mechanical performance. Compared with the pure PVA, the PVA/g-C₃N₄ nanocomposite with 0.50 wt% g-C₃N₄ nanosheets showed ~70.7% enhancement in tensile strength, up from 51.2 MPa to 87.4 MPa.

Preparation and characterization of polystyrene-MgAl layered double hydroxide nanocomposites using bulk polymerization

Polymer/mineral filler nanocomposites are more and more used for diverse applications. As mineral fillers, layered double hydroxides (LDHs) present a great advantage as flame retardants from an environmental point a view (reduction of smoke and toxic gases). This article deals with the use of LDH as flame retardants as compared to montmorillonite (MMT). In situ bulk polymerization of styrene was carried out in the presence of MgAl LDH modified with dodecyl sulfate (DDS) and dodecylbenzene sulfonate (DBS) surfactants. LDH concentrations used were lower than 10 wt.%. X-ray diffraction analysis of the LDH-styrene suspensions revealed the monomer intercalation into the DDS-LDH galleries and a slight decrease in the DBS-LDH basal spacing. Transmission electron microscopy analysis showed that the polymerization occurred outside the DBS-LDH galleries, leading to exfoliation of the layers on the outer surface of LDH platelets. DDS-LDH particles were trapped in the PS polymer. The thermal stability effect was observed for all LDH nanocomposites by thermogravimetric analysis. Cone calorimetry measurements revealed that only the DBS-LDH nanofiller resulted in a reduction of the peak heat released rate (PHHR) and a decrease of smoke released. DBS-LDH/PS exhibited fire properties close to those of clay-PS nanocomposite at 7 wt.% montmorillonite. The PHRR reduction remained small and the total heat release rate constant at 7 wt.% DBS-LDH loading.

Multifunctional properties of organic-inorganic hybrid nanocomposites based on chitosan derivatives and layered double hydroxides for ocular drug delivery

To improve the ocular bioavailability of the model drug of pirenoxine sodium (PRN), organic-inorganic hybrid nanocomposites including layered double hydroxides (LDH) and chitosan derivatives (chitosan-glutathione (CG), chitosan-glutathione-valine (CG-V) and chitosan-glutathione-valine-valine (CG-VV)) were designed and characterized. In vivo precorneal retention study on rabbits showed that mean residence time (MRT) and area under the curve (AUC0-6h) of CG-PRN-LDH nanocomposite eye drop was up to 2.1-fold and 6.3-fold higher than those of commercial product, respectively. In vitro corneal penetration on rabbits demonstrated that the cumulative permeation of CG-VV-PRN-LDH nanocomposite dispersion was increased by 5.2 folds compared to that of commercial product, which may be due to the active transport effect of the nanocomposites by peptide transporter-1 (PepT-1). In addition, the ex vivo fluorescence imaging showed that fluorescent intensity of crystalline lens in rabbits was increased after the administration of PRN-LDH, CG-PRN-LDH, CG-V-PRN-LDH and CG-VV-PRN-LDH (in increasing order) nanocomposite eye drop. Finally, in vivo distribution evaluation in ocular tissues of rabbits revealed that AUC0-8h and MRT in crystalline lens exhibited 14.7-fold and 2.2-fold increase in CG-VV-PRN-LDH nanocomposite eye drop group than those of commercial group, respectively. In summary, the organic-inorganic hybrid nanocomposites with multifunctional properties may be a promising ocular drug delivery system to achieve prolonged precorneal retention, better corneal permeability and enhanced ocular bioavailability.

STATEMENT OF SIGNIFICANCE

Due to several structural and physiological intraocular barriers, drug delivery to the ocular mid-posterior segments still faces great challenges. In this manuscript, organic-inorganic hybrid nanocomposites based on chitosan derivatives and layered double hydroxides (LDH) were designed and constructed. Multifunctional properties of these hybrid nanocomposites were due to the possible active targeting to the peptide transporter-1 on the corneal epithelial cells, the bioadhesive ability and permeation enhancement of chitosan derivatives, and the electrostatic adsorption of LDH. Prolonged precorneal retention, better corneal permeability and enhanced ocular bioavailability of the model drug pirenoxine sodium were observed. Chitosan derivatives-LDH hybrid nanocomposites may be a promising ophthalmic drug system for the treatment of ocular diseases of mid-posterior segments.