The preparation of polyolefin elastomer functionalized with polysiloxane and its effect in ethylene-propylene-diene monomer/silicon rubber blends

The Contribution of BaTiO3 to the Stability Improvement of Ethylene-Propylene-Diene Rubber: Part I-Pristine Filler

This study presents the functional effects of BaTiO₃ powder loaded in ethylene-propylene-diene rubber (EPDM) in three concentrations: 0, 1, and 2.5 phr. The characterization of mechanical properties, oxidation strength, and biological vulnerability is achieved on these materials subjected to an accelerated degradation stimulated by their γ-irradiation at 50 and 100 kGy. The thermal performances of these materials are improved when the content of filler becomes higher. The results obtained by chemiluminescence, FTIR-ATR, and mechanical testing indicate that the loading of 2.5 phr is the most proper composition that resists for a long time after it is γ-irradiated at a high dose. If the oxidation starts at 176 °C in the pristine polymer, it becomes significant at 188 and 210 °C in the case of composites containing 1 and 2.5 phr of filler, respectively. The radiation treatment induces a significant stability improvement measured by the enlargement of temperature range by more than 1.5 times, which explains the durability growth for the radiation-processed studied composites. The extension of the stability period is also based on the interaction between degrading polymer substrate and particle surface in the composite richest in titanate fraction when the exposure is 100 kGy was analyzed. The mechanical testing as well as the FTIR investigation clearly delimits the positive effects of carbon black on the functionality of EPDM/BaTiO₃ composites. The contribution of carbon black is a defining feature of the studied composites based on the nucleation of the host matrix by which the polymer properties are effectively ameliorated.

Thermally Conductive and Antistatic Properties of Silicone Rubber Reinforced by the Modified Graphene Oxide

Silicone rubber (SR)/vinyl-graphene oxide (vinyl-GO) nanocomposites were prepared through the hydrosilylation reaction of silicon hydrogen polydimethylsiloxane (H-PDMS) with vinyl polydimethylsiloxane (vinyl-PDMS), in which vinyl-GO was used as a nano filler. The thermally conductive and antistatic properties of the nanocomposites, and their tensile strength and thermal stability were evaluated. The thermally conductive and antistatic properties increased naturally when the nanocomposites had eight to nine parts of vinyl-GO. The addition of 9 parts of vinyl-GO increased the thermal conductivity to 0.44 from 0.17 W/m−1·K−1 of neat SR and the surface resistance value to 108 from 1014 Ω of neat SR. Vinyl-GO is effective in improving the tensile strength and toughness of the nanocomposites. The tensile strength and elongation at break of the nanocomposites were much higher than that of neat SR, especially for 10 parts of vinyl-GO in the nanocomposite, and the tensile strength was 1.84 MPa and the elongation at break was 314.1%. Additionally, compared with neat SR, the nanocomposites had a much higher thermal stability. For eight parts of vinyl-GO in the nanocomposites, H-PDMS with the selected silicon hydrogen content and vinyl-PDMS with the selected vinyl content could offer an appropriate cross-linking degree that suits the character of GO. When the nanocomposite had eight parts of vinyl-GO, its scanning electron microscope exhibited a monolayer GO with folded, twisted, and local surface folds. However, there was a certain amount of multilayer aggregation of GO for 10 parts of vinyl-GO in the nanocomposite.