Silk fibres grafted with 2-hydroxyethyl methacrylate (HEMA) and 4-hydroxybutyl acrylate (HBA) for biomedical applications

Vibrational Study on the Structure, Bioactivity, and Silver Adsorption of Silk Fibroin Fibers Grafted with Methacrylonitrile

Natural fibers have received increasing attention as starting materials for innovative applications in many research fields, from biomedicine to engineering. Bombyx mori silk fibroin has become a material of choice in the development of many biomedical devices. Grafting represents a good strategy to improve the material properties according to the desired function. In the present study, Bombyx mori silk fibroin fibers were grafted with methacrylonitrile (MAN) with different weight gains. The potential interest in biomedical applications of MAN functionalization relies on the presence of the nitrile group, which is an acceptor of H bonds and can bind metals. IR and Raman spectroscopy were used to characterize the grafted samples and the possible structural changes induced by grafting. Afterward, the same techniques were used to study the bioactivity (i.e., the calcium phosphate nucleation ability) of MAN-grafted silk fibroins after ageing in simulated body fluid (SBF) for possible application in bone tissue engineering, and their interaction with Ag+ ions, for the development of biomaterials with enhanced anti-microbial properties. MAN was found to efficiently polymerize on silk fibroin through polar amino acids (i.e., serine and tryptophan), inducing an enrichment in silk fibroin-ordered domains. IR spectroscopy allowed us to detect the nucleation of a thin calcium phosphate layer and the uptake of Ag+ ions through the nitrile group, which may foster the application of these grafted materials in biomedical applications.

Silk Fibroin Combined with Electrospinning as a Promising Strategy for Tissue Regeneration

The development of tissue engineering scaffolds is of great significance for the repair and regeneration of damaged tissues and organs. Silk fibroin (SF) is a natural protein polymer with good biocompatibility, biodegradability, excellent physical and mechanical properties and processability, making it an ideal universal tissue engineering scaffold material. Nanofibers prepared by electrospinning have attracted extensive attention in the field of tissue engineering due to their excellent mechanical properties, high specific surface area, and similar morphology as to extracellular matrix (ECM). The combination of silk fibroin and electrospinning is a promising strategy for the preparation of tissue engineering scaffolds. In this review, the research progress of electrospun silk fibroin nanofibers in the regeneration of skin, vascular, bone, neural, tendons, cardiac, periodontal, ocular and other tissues is discussed in detail.

Solvent-Free Direct PEGylation of Collagen Fibers

The addition of poly(ethylene glycol) (PEG) to biomolecules and biomaterials is a well-established approach to modify their properties for therapeutic applications. For biomaterials, the approach is typically to blend or electrospray the synthetic polymer with the biomaterial. Effective surface modification approaches such as surface-initiated polymer brushes are challenging since the harsh solvents required for brush synthesis may destroy the biomaterial. Herein, we describe the PEGylation of collagen fibers by surface-initiated PEG brushes using a living anionic grafting-from mechanism. This brush synthesis is done in the absence of solvents to minimize the degradation of the native collagen structure. We quantify the effect the brush synthesis has on the native structure of the collagen fiber using differential scanning calorimetry (DSC) and find that even at long reaction times a significant fraction of the native structure remains. Dynamic mechanical analysis indicates the collagen undergoes only modest structural degradation, while adhesion studies find a significant improvement of antifouling properties. Further, our approach opens the way for further chemistry, as the growing polymer chain is a potassium alkoxy group that can be functionalized by termination or by subsequent reaction by a wide variety of molecules.

Vibrational Study on Structure and Bioactivity of Protein Fibers Grafted with Phosphorylated Methacrylates

In the last decades, silk fibroin and wool keratin have been considered functional materials for biomedical applications. In this study, fabrics containing silk fibers from Bombyx mori and Tussah silk fibers from Antheraea pernyi, as well as wool keratin fabrics, were grafted with phosmer CL and phosmer M (commercial names, i.e., methacrylate monomers containing phosphate groups in the molecular side chain) with different weight gains. Both phosmers were recently proposed as flame retarding agents, and their chemical composition suggested a possible application in bone tissue engineering. IR and Raman spectroscopy were used to disclose the possible structural changes induced by grafting and identify the most reactive amino acids towards the phosmers. The same techniques were used to investigate the nucleation of a calcium phosphate phase on the surface of the samples (i.e., bioactivity) after ageing in simulated body fluid (SBF). The phosmers were found to polymerize onto the biopolymers efficiently, and tyrosine and serine underwent phosphorylation (monitored through the strengthening of the Raman band at 1600 cm-1 and the weakening of the Raman band at 1400 cm-1, respectively). In grafted wool keratin, cysteic acid and other oxidation products of disulphide bridges were detected together with sulphated residues. Only slight conformational changes were observed upon grafting, generally towards an enrichment in ordered domains, suggesting that the amorphous regions were more prone to react (and, sometimes, degrade). All samples were shown to be bioactive, with a weight gain of up to 8%. The most bioactive samples contained the highest phosmers amounts, i.e., the highest amounts of phosphate nucleating sites. The sulphate/sulphonate groups present in grafted wool samples appeared to increase bioactivity, as shown by the five-fold increase of the IR phosphate band at 1040 cm-1.

Controlled radical polymerization of hydrophilic and zwitterionic brush-like polymers from silk fibroin surfaces

Bombyx mori silk fibroin is a fibrous protein whose tunable properties and biocompatibility have resulted in its utility in a wide-variety of applications, including as drug delivery vehicles, wound dressings, and tissue engineering scaffolds. Control of protein and cell attachment is vital to the performance of biomaterials, but silk fibroin is mostly hydrophobic and interacts nonspecifically with cells and proteins. Silk functionalised with hydrophilic polymers reduces attachment, but the low number of reactive sites makes achieving a uniform conjugation a persistent challenge. This work presents a new approach to grow brush-like polymers from the surface of degradable silk films, where the films were enriched with hydroxyl groups, functionalised with an initiator, and finally reacted with acrylate monomers using atom transfer radical polymerisation. Two different routes to hydroxyl enrichment were investigated, one involving reaction with ethylene oxide (EO) and the other using a two-step photo-catalysed oxidation reaction. Both routes increased surface hydrophilicity, and hydrophilic monomers containing either uncharged (poly(ethylene glycol), PEG) pendant groups or zwitterionic pendant groups were polymerised from the surfaces. The initial processing of the films to induce beta sheet structures was found to impact the success of the polymerizations. Compared to the EO modified or unmodified silk surfaces, the oxidation reaction resulted in more polymer conjugation and the surfaces appear more uniform. Mesenchymal stem cell and protein attachment were the lowest on polymers grown from oxidised surfaces. PEG-containing brush-like polymers displayed lower protein attachment than surfaces conjugated with PEG using a previously reported "grafting to" method, but polymers containing zwitterionic side chains displayed both the lowest contact angles and the lowest cell and protein attachment. This finding may arise from the interactions of the zwitterionic pendant groups through their permanent dipoles and is an important finding because PEG is susceptible to oxidative damage that can reduce efficacy over time. These modified silk materials with lower cell and protein attachments are envisioned to find utility when enhanced diffusion around surfaces is required, such as in drug delivery implants.

Osteogenic differentiation of hMSCs on semi-interpenetrating polymer networks of polyurethane/poly(2‑hydroxyethyl methacrylate)/cellulose nanowhisker scaffolds

Poly (2‑hydroxyethyl methacrylate) (PHEMA) was crosslinked in the presence of biocompatible and biodegradable poly(caprolactone) (PCL) based polyurethanes (PUs) and cellulose nanowhiskers (CNWs). The CNWs were obtained from wastepaper. In order to crosslink PHEMA (10 wt%), a novel acrylic-urethane cross-linker was produced by a condensation reaction of PHEMA and hexamethylene diisocyanate (HDI). The PU-PHEMA-CNWs scaffolds were prepared by solvent casting/particulate leaching method in different weight percentages of CNWs (i.e., 0, 0.1, 0.5, and 1 wt%). The structural, mechanical, and in vitro biological properties of bio-nanocomposites were evaluated via FTIR, SEM, tensile, and MTT assay. The tensile strength of PU-PHEMA-0, PU-PHEMA-0.1, PU-PHEMA-0.5, and PU-PHEMA-1 were 76.2, 95.8, 98.1, and 89.8 kPa, respectively. Incorporation of CNWs also resulted in improved cell proliferation on PU-PHEMA-CNWs scaffolds. The bone marrow derived human mesenchymal stem cells (hMSCs) were seeded on the prepared porous scaffolds and incubated in osteogenic medium. Based on the results including calcium content assay, alkaline phosphatase assay, and mineralization staining, PU-PHEMA-CNW scaffolds were introduced as a suitable election for imitating the behavior of cellular niche. Bone mineralization and osteogenesis differentiation of hMSCs on PU-PHEMA-CNW scaffolds were significantly more than control after 14 days.