Enteromorpha cellulose micro-nanofibrils/poly(vinyl alcohol) based composite films with excellent hydrophilic, mechanical properties and improved thermal stability

Valorization of guinea grass seed (Megathyrsus maximus): Synthesis and utilization of cellulose microfiber to reinforce esterified and cross-linked guinea starch films

The present study extracts starch from guinea grass seed and fiber from the starch extraction residue. The fibrous residue was chemically converted into cellulose microfiber (CMF) and used to reinforce the native, esterified and crosslinked guinea starch films. The films were developed with 5 % starch, 40 % glycerol and 0, 2.5, 5, and 10 % CMF based on the dry matter of starch. SEM images of all film samples showed good compatibility of CMF with starch molecules, and no fractures or pores were observed. Adding filler materials to modified starch films slightly increased the film thickness (0.24 to 0.30 mm) due to the high dimensions of CMF, which comprise a significant amount of the composite's volume. A synergetic effect of starch modification and CMF in films decreased the moisture content (21.98 to 9.21 %), water solubility (25.65 to 15.47 %), water vapor permeability (6.96×10-7 to 1.65×10-7g∙mm2∙day∙Pa), and elongation at the break (33.51 to 16.79 %) while increasing the tensile strength (1.84 to 3.85 MPa) and Young's modulus (5.49 to 22.93 MPa). The L* and a* values of the films decreased, and the b* and opacity values of the films increased with the addition of CMF. The XRD graph showed that all films have semicrystalline structures with peaks at 18°, 20°, and 22°, and the degree of crystallinity increases (32.3 to 55.1 %) with CMF. All film samples showed good thermal stability up to 315 °C. In conclusion, esterified starch-based films exhibited superior barrier properties and flexibility. On the contrary, cross-linked starch films demonstrated higher tensile strength and lower water solubility.

Multifunctional composite coatings with hydrophobic, UV-resistant, anti-oxidative, and photothermal performance for healthcare

Personal protective textiles have attracted extensive interest since Corona Virus Disease 2019 has broken out. Moreover, developing eco-friendly, multifunctional waterproof, and breathable surface is of great importance but still faces enormous challenges. Notably, good hydrophobicity and breathability are necessary for protective textiles, especially protective clothing and face masks for healthcare. Herein, the multifunctional composite coatings with good UV-resistant, anti-oxidative, hydrophobic, breathable, and photothermal performance has been rapidly created to meet protective requirements. First, the gallic acid and chitosan polymer was coated onto the cotton fabric surface. Subsequently, the modified silica sol was anchored on the coated cotton fabric surface. The successful fabrication of composite coatings was verified by RGB values obtained from the smartphone and K/S value. The present work is an advance for realizing textile hydrophobicity by utilizing fluorine-free materials, compared with the surface hydrophobicity fabricated with conventional fluorinated materials. The surface free energy has been reduced from 84.2 to27.6 mJ/m2 so that the modified cotton fabric could repel the ethylene glycol, hydrochloric acid, and sodium hydroxide solutions, respectively. Besides, the composite coatings possesses lower adhesion to deionized water. After 70 cycles of the sandpaper abrasion, the fluorine-free hydrophobic coatings still exhibits good hydrophobicity with WCA of 124.6 ± 0.9°, with overcoming the intrinsic drawback of the poor abrasion resistance of hydrophobic surfaces. Briefly, the present work may provide a universal strategy for rapidly creating advanced protective coatings to meet personal healthcare, and a novel method for detecting RGB values of composite coatings by smartphone.