Assessing bone quality through mechanical properties in postmenopausal trabecular bone

Dexamethasone and zinc loaded polymeric nanoparticles reinforce and remineralize coronal dentin. A morpho-histological and dynamic-biomechanical study

OBJECTIVE

To investigate the effect of novel polymeric nanoparticles (NPs) doped with dexamethasone (Dex) on viscoelasticity, crystallinity and ultra-nanostructure of the formed hydroxyapatite after NPs dentin infiltration.

METHODS

Undoped-NPs, Dex-doped NPs (Dex-NPs) and zinc-doped-Dex-NPs (Zn-Dex-NPs) were tested at dentin, after 24 h and 21 d. A control group without NPs was included. Coronal dentin surfaces were studied by nano-dynamic mechanical analysis measurements, atomic force microscopy, X-ray diffraction and transmission electron microscopy. Mean and standard deviation were analyzed by ANOVA and Student-Newman-Keuls multiple comparisons (p < 0.05).

RESULTS

At 21 d of storage time, both groups doped with Dex exhibited the highest complex, storage and loss moduli among groups. Zn-Dex-NPs and Dex-NPs promoted the highest and lowest tan delta values, respectively. Dex-NPs contributed to increase the fibril diameters of dentin collagen over time. Dentin surfaces treated with Zn-Dex-NPs attained the lowest nano-roughness values, provoked the highest crystallinity, and produced the longest and shortest crystallite and grain size. These new crystals organized with randomly oriented lattices. Dex-NPs induced the highest microstrain. Crystalline and amorphous matter was present in the mineral precipitates of all groups, but Zn and Dex loaded NPs helped to increase crystallinity.

SIGNIFICANCE

Dentin treated with Zn-Dex-NPs improved crystallographic and atomic order, providing structural stability, high mechanical performance and tissue maturation. Amorphous content was also present, so high hydroxyapatite solubility, bioactivity and remineralizing activity due to the high ion-rich environment took place in the infiltrated dentin.

The PCK2-glycolysis axis assists three-dimensional-stiffness maintaining stem cell osteogenesis

Understanding mechanisms underlying the heterogeneity of multipotent stem cells offers invaluable insights into biogenesis and tissue development. Extracellular matrix (ECM) stiffness has been acknowledged as a crucial factor regulating stem cell fate. However, how cells sense stiffness cues and adapt their metabolism activity is still unknown. Here we report the novel role of mitochondrial phosphoenolpyruvate carboxykinase (PCK2) in enhancing osteogenesis in 3D ECM via glycolysis. We experimentally mimicked the physical characteristics of 3D trabeculae network of normal and osteoporotic bone with different microstructure and stiffness, observing that PCK2 promotes osteogenesis in 3D ECM with tunable stiffness in vitro and in vivo. Mechanistically, PCK2 enhances the rate-limiting metabolic enzyme pallet isoform phosphofructokinase (PFKP) in 3D ECM, and further activates AKT/extracellular signal-regulated kinase 1/2 (ERK1/2) cascades, which directly regulates osteogenic differentiation of MSCs. Collectively, our findings implicate an intricate crosstalk between cell mechanics and metabolism, and provide new perspectives for strategies of osteoporosis.

•

As the key rate-limiting enzyme of gluconeogenesis, PCK2 manipulates osteogenesis in stiff and soft ECM in vitro and in vivo.

•

PCK2 regulates osteogenic capacity of BMMSCs in 3D ECM with different stiffness, via modulating glycolysis and regulating PFKP-AKT/ERK signaling pathways.

Instrumented nanoindentation in musculoskeletal research

Musculoskeletal tissues, such as bone, cartilage, and muscle, are natural composite materials that are constructed with a hierarchical structure ranging from the cell to tissue level. The component differences and structural complexity, together, require comprehensive multiscale mechanical characterization. In this review, we focus on nanoindentation testing, which is used for nanometer to sub-micrometer length scale mechanical characterization. In the following context, we will summarize studies of nanoindentation in musculoskeletal research, examine the critical factors that affect nanoindentation testing results, and briefly summarize other commonly used techniques that can be conjoined with nanoindentation for synchronized imaging and colocalized characterization.

Trabecular bone porosity and pore size distribution in osteoporotic patients - A low field nuclear magnetic resonance and microcomputed tomography investigation

The study of bone morphology is of great importance as bone morphology is influenced by factors such as age and underlying comorbidities and is associated with bone mechanical properties and fracture risk. Standard diagnostic techniques used in bone disease, such as Dual-Energy X-ray absorptiometry and ultrasonography do not provide qualitative and quantitative morphological information. In recent years, techniques such as High Resolution Computed Tomography (HR-CT), micro- CT, Magnetic Resonance Imaging (MRI), and Low Field Nuclear Magnetic Resonance (LF-NMR) have been developed for the study of bone structure and porosity. Data obtained from these techniques have been used to construct models to predict bone mechanical properties thanks to finite element analysis. Cortical porosity has been extensively studied and successfully correlated with disease progression and mechanical properties. Trabecular porosity and pore size distribution, however, have increasingly been taken into consideration to obtain a comprehensive analysis of bone pathology and mechanic. Therefore, we have decided to evaluate the ability of micro- CT (chosen for its high spatial resolving power) and LF-NMR (chosen to analyze the behavior of water molecules within trabecular bone pores) to characterize the morphology of trabecular bone in osteoporosis. Trabecular bone samples from human femoral heads collected during hip replacement surgery were from osteoporosis (test group) and osteoarthritis (control group) patients. Our data show that both micro- CT and LF-NMR can detect qualitative changes in trabecular bone (i.e., transition from plate-like to rod-like morphology). Micro- CT failed to detect significant differences in trabecular bone morphology parameters between osteoporotic and osteoarthritic specimens, with the exception of Trabecular Number and Connectivity Density, which are markers of osteoporosis progression. In contrast, LF-NMR was able to detect significant differences in porosity and pore size of trabecular bone from osteoporotic versus osteoarthritic (control) samples. However, only the combination of these two techniques allowed the detection of structural morphometric changes (increase in the larger pore fraction and enlargement of the larger pores) in the trabecular bone of osteoporotic specimens compared to osteoarthritic ones. In conclusion, the combined use of LF-NMR and micro- CT provides a valuable tool for characterizing the morphology of trabecular bone and may offer the possibility for a new approach to the study and modeling of bone mechanics in the context of aging and disease.

Doxycycline and Zinc Loaded Silica-Nanofibrous Polymers as Biomaterials for Bone Regeneration

The main target of bone tissue engineering is to design biomaterials that support bone regeneration and vascularization. Nanostructured membranes of (MMA)₁-co-(HEMA)₁/(MA)₃-co-(HEA)₂ loaded with 5% wt of SiO₂-nanoparticles (HOOC-Si-Membrane) were doped with zinc (Zn-HOOC-Si-Membrane) or doxycycline (Dox-HOOC-Si-Membrane). Critical bone defects were effectuated on six New Zealand-bred rabbit skulls and covered with the membranes. After six weeks, the bone architecture was evaluated with micro computed tomography. Three histological analyses were utilized to analyse bone regeneration, including von Kossa silver nitrate, toluidine blue and fluorescence. All membrane-treated defects exhibited higher number of osteocytes and bone perimeter than the control group without the membrane. Zn-HOOC-Si-Membranes induced higher new bone and osteoid area than those treated with HOOC-Si-Membranes, and control group, respectively. Zn-HOOC-Si-Membranes and Dox-HOOC-Si-Membranes attained the lowest ratio M1 macrophages/M2 macrophages. Dox-HOOC-Si-Membranes caused the lowest number of osteoclasts, and bone density. At the trabecular new bone, Zn-HOOC-Si-Membranes produced the highest angiogenesis, bone thickness, connectivity, junctions and branches. Zn-HOOC-Si-Membranes enhanced biological activity, attained a balanced remodeling, and achieved the greatest regenerative efficiency after osteogenesis and angiogenesis assessments. The bone-integrated Zn-HOOC-Si-Membranes can be considered as bioactive modulators provoking a M2 macrophages (pro-healing cells) increase, being a potential biomaterial for promoting bone repair.

Ex vivo investigations on bioinspired electrospun membranes as potential biomaterials for bone regeneration

OBJECTIVES

To assess the surface characteristics and composition that may enhance osteoblasts viability on novel electrospun composite membranes (organic polymer/silicon dioxide nanoparticles).

METHODS

Membranes are composed by a novel polymer blend, the mixture of two hydrophilic copolymers 2-hydroxyethylmethacrylate-co-methylmethacrylate and 2-hydroxyethylacrylate-co-methylacrylate, and they are doped with silicon dioxide nanoparticles. Then the membranes were functionalized with zinc or doxycycline. The membranes were morphologically characterized by atomic force and scanning electron microscopy (FESEM), and mechanically probed using a nanoindenter. Biomimetic calcium phosphate precipitation on polymeric tissues was assessed. Cell viability tests were performed using human osteosarcoma cells. Cells morphology was also studied by FESEM. Data were analyzed by ANOVA, Student-Newman-Keuls and Student t tests (p < 0.05).

RESULTS

Silica doping of membranes enhanced bioactivity and increased mechanical properties. Membranes morphology and mechanical properties were similar to those of trabecular bone. Zinc and doxycycline doping did not exert changes but it increased novel membranes bioactivity. Membranes were found to permit osteoblasts proliferation. Silica-doping favored cells proliferation and spreading. As soon as 24 h after the seeding, cells in silica-doped membranes were firmly attached to experimental tissues trough filopodia, connected to each other. The cells produced collagen and minerals onto the surfaces.

CONCLUSIONS

Silica nanoparticles enhanced surface properties and osteoblasts viability on electrospun membranes.

CLINICAL SIGNIFICANCE

The ability of silica-doped matrices to promote precipitation of calcium phosphate, together with their mechanical properties, observed non-toxicity, stimulating effect on osteoblasts and its surface chemistry allowing covalent binding of proteins, offer a potential strategy for bone regeneration applications.

Bone Hardness of Different Anatomical Regions of Human Radius and its Impact on the Pullout Strength of Screws

OBJECTIVE

To investigate the bone hardness of different anatomical regions of the human radius and its impact on the pullout strength of screws.

METHODS

Fresh radius bones were obtained from three donated cadavers. They were divided into three parts: proximal metaphysis, shaft, and distal metaphysis. The proximal metaphysis contains the head, neck, and radial tuberosity. The distal metaphysis includes the palmaris radius and the styloid process. The shaft of the radius was divided into nine segments of equal length. The bone hardness of three radiuses, one from each cadaver, was measured by Vickers microindentation hardness tests, and the screw pullout strength was examined in the other three radiuses using a materials testing machine. The trend between radius hardness and pullout strength was analyzed by using an analysis of variance randomized block design. Pearson correlation analysis was performed to evaluate the linear correlation between the bone hardness and the pullout strength of the human radius.

RESULTS

The mean hardness ranged from 33.30 HV (the head) to 43.82 HV (the diaphysis). The hardest part of the radius was the shaft, with a value of 42.54 ± 5.59 HV. The proximal metaphysis had a hardness value of 34.15 ± 6.48 HV, and the distal metaphysis hardness value was 35.24 ± 5.17 HV. The shaft was 23.5% harder than the proximal metaphysis and 20% harder than the distal metaphysis. The microhardness test demonstrated that the bone hardness value of the diaphysis was significantly higher than those of both the proximal and distal metaphysis of the radius (both P < 0.05). The mean pullout strength values ranged from 552 N (the distal metaphysis) to 2296 N (the diaphysis). The greatest pullout strength of the radius was observed for the shaft, with a pullout strength of 1727.96 ± 111.44 N. The pullout strength of the proximal metaphysis was 726.33 ± 236.39 N, and the pullout strength of the distal metaphysis was 590.67 ± 36.30 N. The pullout strength of the shaft was 138% greater than that of the proximal metaphysis and 190% greater than that of the distal metaphysis. The pullout strength was also higher in the diaphysis than at both ends of the radius (both P < 0.05). A positive correlation was found between bone hardness and pullout strength (R = 0.927, P < 0.001).

CONCLUSIONS

Bone hardness and screw pullout strength are higher in the diaphysis of the radius than at either end. The pullout strength is positively related to bone hardness in the human radius.

Silver-loaded nanoparticles affect ex-vivo mechanical behavior and mineralization of dentin

Background

The aim was to evaluate the effect of silver loaded nanoparticles (NPs) application on the triboscopic, crystallographic and viscoelastic properties of demineralized dentin. Polymethylmetacrylate-based NPs and Ag loaded NPs were applied on demineralized dentin.

Material and Methods

Treated and untreated surfaces were probed by a nanoindenter to test viscoelasticity, and by atomic force microscopy to test nanoroughness and collagen fibril diameter. X-ray diffraction and transmission electron microscopy through selected area diffraction and bright-field imaging were also used.

Results

Dentin treated with Ag-NPs attained the lowest complex modulus, and the highest tan delta values after 7 days of storage. Dentin treated with undoped-NPs achieved the lowest nanoroughness and the greatest collagen bandwidths among groups. Crystals were identified as hydroxyapatite with the highest crystallographic maturity and crystallite size in dentin treated with undoped-NPs. Texture increased in all samples from 24 h to 7 d, except in dentin surfaces treated with Ag-NPs at 310 plane. Polyhedral, block-like, hexagonal or plate-like shaped apatite crystals constituted the bulk of minerals in dentin treated with Ag-NPs, after 7 d. Polyhedral or rounded/drop-like, and polymorphic in strata crystal apatite characterized the minerals when undoped-NPs were used, with more crystalline characteristics after 7 d than that found when Ag-NPs were applied. Ag-NPs application did not improve the mechanical performance of dentin and did not produce dentin remineralization. However, energy was dissipated through the dentin without showing stress concentration; contrary was occurring at dentin treated with undoped-NPs, that provoked bridge-like mineral deposits at the dentin surface.

Conclusions

Ag-NPs application did not enhance the mechanical properties of cervical dentin, though the energy dissipation did not damage the dentin structure. Remineralization at dentin was not produced after Ag-NPs application, though improved crystallinity may lead to increase stability of the apatite that was generated at the dentin surface.

Key words:Dentin, mechanical, mineralization, roughness, silver, viscoelastic.