Synthesis and multimethodological characterization of neodymium substituted nickel tungstates and molybdates solid solution Ni Ndx (W,Mo)O4, (0 ≤ x ≤ 0.2)

Sonochemical synthesis of samarium tungstate nanoparticles for the electrochemical detection of nilutamide

This study reports the sonochemical synthesis of samarium tungstate nanoparticles (SWNPs) for applications in electrochemical sensors. The synthesis process is based on a precipitation reaction, which was investigated by ultrasound and compared with the effect of stirring. A bath sonicator operated at a frequency and power of 37/100 kHz and ~60 W, respectively, was employed to prepare the material. The shock waves efficiently irradiated the reaction conditions as much as possible, resulting in the good crystallinity of the monoclinic phase of the SWNPs, which was confirmed by XRD analysis. The surface morphology and structural composition was further evaluated by HRTEM, EDS and XPS. The good crystallinity and uniform distribution of elements in the nanoparticles were confirmed. The performance of the SWNPs to electrochemically sense nilutamide (NLT) was studied, which revealed a good electrochemical signal. As a result, the SWNPs were applied to an electrode material for the detection of NLT. This study revealed the excellent activity of the SWNPs for NLT detection, resulting in a low detection limit (0.0026 µM) and good linear range (0.05-318 µM). Furthermore, the results show appreciable analytical performances, which could be applied to electrochemical anti-androgen drug nilutamide sensors.

Zinc-Layered Hydroxide Salt Intercalated with Molybdate Anions as a New Smart Nanocontainer for Active Corrosion Protection of Carbon Steel

The use of smart nanocontainers to store corrosion inhibitors in coatings significantly increases the efficiency and durability of the coating, providing active corrosion protection. Here we report the synthesis of a zinc-layered hydroxide salt (LHS) and its use as a novel nanocontainer for this purpose, storing the corrosion inhibitor molybdate in the interlayer region of the LHS. Layered zinc hydroxide molybdate (ZHM) was obtained by anion-exchange reactions using layered zinc hydroxide acetate (ZHA) as a precursor, obtained by alkaline coprecipitation. The release behavior of molybdate from the ZHM nanocontainers in aqueous NaCl solution (0.05 mol/L) was evaluated using UV-vis absorption spectroscopy. The molybdate release from the ZHM nanocontainers was realized by the anion-exchange mechanism, where chloride anions replaced intercalated molybdate anions. The release was fast in the first minutes of exposure, followed by a controlled release afterward, reaching about 35% of cumulative amount of released molybdate after 30 days of exposure. The anticorrosion effect provided by the ZHM nanocontainers for carbon steel was investigated by electrochemical impedance spectroscopy. The steel substrate was coated with an epoxy resin loaded with ZHM nanocontainers (5 wt %) and immersed in an NaCl solution (0.05 mol/L) to evaluate the active mechanisms of inhibition and the anticorrosion properties of the loaded coating in comparison with a neat coating (blank). The coating loaded with ZHM nanocontainers presented the best corrosion protection performance, exhibiting an increase of R_C (coating resistance) with the immersion time and superior R_P (polarization resistance) for all the measured periods, compared to the blank. This effect is a consequence of the double mechanism of protection provided by the ZHM nanocontainers: (i) stimulus-response release of molybdate and its active inhibition in the scratched region by the formation of an insoluble protective film, simultaneously with (ii) removal of the corrosive chloride species from the medium.