Asymmetric in-plane shear behavior of isolated cadaveric lumbar facet capsular ligaments: Implications for subject specific biomechanical models

The Lumbar Facet Capsular Ligament Becomes More Anisotropic and the Fibers Become Stiffer With Intervertebral Disc and Facet Joint Degeneration

Degeneration of the lumbar spine, and especially how that degeneration may lead to pain, remains poorly understood. In particular, the mechanics of the facet capsular ligament may contribute to low back pain, but the mechanical changes that occur in this ligament with spinal degeneration are unknown. Additionally, the highly nonlinear, heterogeneous, and anisotropic nature of the facet capsular ligament makes understanding mechanical changes more difficult. Clinically, magnetic resonance imaging (MRI)-based signs of degeneration in the facet joint and the intervertebral disc (IVD) correlate. Therefore, this study examined how the nonlinear, heterogeneous mechanics of the facet capsular ligament change with degeneration of the lumbar spine as characterized using MRI. Cadaveric human spines were imaged via MRI, and the L2-L5 facet joints and IVDs were scored using the Fujiwara and Pfirrmann grading systems. Then, the facet capsular ligament was isolated and biaxially loaded. The nonlinear mechanical properties of the ligament were obtained using a nonlinear generalized anisotropic inverse mechanics analysis (nGAIM). Then a Holzapfel-Gasser-Ogden (HGO) model was fit to the stress-strain data obtained from nGAIM. The facet capsular ligament is stiffer and more anisotropic at larger Pfirrmann grades and higher Fujiwara scores than at lower grades and scores. Analysis of ligament heterogeneity showed all tissues are highly heterogeneous, but no distinct spatial patterns of heterogeneity were found. These results show that degeneration of the lumbar spine including the facet capsular ligament appears to be occurring as a whole joint phenomenon and advance our understanding of lumbar spine degeneration.

The mechanical behavior of silk-fibroin reinforced alginate hydrogel biocomposites - Toward functional tissue biomimetics

Soft tissues are constructed as fiber-reinforced composites consisting of structural mechanisms and unique mechanical behavior. Biomimetics of their mechanical behavior is currently a significant bioengineering challenge, emphasizing the need to replicate structural and mechanical mechanisms into novel biocomposite designs. Here we present a novel silk-based biocomposite laminate constructed from long natural silk and fibroin fibers embedded in an alginate hydrogel matrix. Controlling the mechanical features of these laminates were studied for different fiber volume fractions (VF) and orientations using unidirectional tensile tests. Three material systems were investigated having different fiber orientations: longitudinal (0°), transverse (90°), and cross-plied (0/90°). The general behavior of the biocomposite laminates was anisotropic hyperelastic with large deformations. Longitudinal fibroin laminates have shown a tensile modulus of 178.55 ± 14.46 MPa and tensile strength of 18.47 ± 2.01 MPa for 0.48 VF. With similar VF, cross-plied fibroin laminates demonstrated structural shielding ability, having a tensile modulus and tensile strength of 101.73 ± 8.04 MPa and 8.29 ± 1.63 MPa for only a third of the VF directed in the stretching direction. The stress-strain behavior was in a similar range to highly stiff native human soft tissues such as ligament and meniscus. These findings demonstrate the potential of the fibroin fiber-reinforced biocomposites to mimic the mechanics of tissues with a quantitatively controlled amount of fibers and designed spatial arrangement. This can lead to new solutions for the repair and replacement of damaged functional and highly stiff soft tissues.

Through-thickness regional variation in the mechanical characteristics of the lumbar facet capsular ligament

The human lumbar facet capsule, with the facet capsular ligament (FCL) that forms its primary constituent, is a common source of lower back pain. Prior studies on the FCL were limited to in-plane tissue behavior, but due to the presence of two distinct yet mechanically different regions, a novel out-of-plane study was conducted to further characterize the roles of the collagen and elastin regions. An experimental technique, called stretch-and-bend, was developed to study the tension-compression asymmetry of the FCL due to varying collagen fiber density throughout the thickness of the tissue. Each healthy excised cadaveric FCL sample was tested in four conditions depending on primary collagen fiber alignment and regional loading. Our results indicate that the FCL is stiffest when the collagen fibers (1) are aligned in the direction of loading, (2) are in tension, and (3) are stretched - 16% from its off-the-bone, undeformed state. An optimization routine was used to fit a four-parameter anisotropic, hyperplastic model to the experimental data. The average elastin modulus, E, and the average collagen fiber modulus, ξ, were 13.15 ± 3.59 kPa and 18.68 ± 13.71 MPa (95% CI), respectively.