Titania-supported gold-based nanoparticles efficiently catalyze the hydrodeoxygenation of guaiacol

Selective C(aryl)-O bond cleavage in biorenewable phenolics

Biorefining of lignocellulosic biomass via a lignin first approach delivers a range of products with high oxygen content. Besides pulp, a lignin oil rich in guaiacols and syringols is obtained bearing multiple C(aryl)-OH and C(aryl)-OMe groups, typically named phenolics. Similarly, technical lignin can be used but is generally more difficult to process providing lower yields of monomers. Removal of the hydroxy and methoxy groups in these oxygenated arenes is challenging due to the inherently strong C-O bonds, in addition to the steric and electronic deactivation by adjacent -OH or -OMe groups. Moreover, chemoselective removal of a specific group in the presence of other similar functionalities is non-trivial. Other side-reactions such as ring saturation and transalkylation further complicate the desired reduction process. In this overview, three different selective reduction reactions are considered. Complete hydrodeoxygenation removes both hydroxy and methoxy groups resulting in benzene and alkylated derivatives (BTX type products) which is often complicated by overreduction of the arene ring. Hydrodemethoxylation selectively removes methoxy groups in the presence of hydroxy groups leading to phenol products, while hydrodehydroxylation only removes hydroxy groups without cleavage of methoxy groups giving anisole products. Instead of defunctionalization via reduction transformation of C(aryl)-OH, albeit via an initial derivatization into C(aryl)-OX, into other functionalities is possible and also discussed. In addition to methods applying guaiacols and syringols present in lignin oil as model substrates, special attention is given to methods using mixtures of these compounds obtained from wood/technical lignin. Finally, other important aspects of C-O bond activation with respect to green chemistry are discussed.

Cobalt-Graphene Catalyst for Selective Hydrodeoxygenation of Guaiacol to Cyclohexanol

Herein, cobalt-reduced graphene oxide (rGO) catalyst was synthesized with a practical impregnation-calcination approach for the selective hydrodeoxygenation (HDO) of guaiacol to cyclohexanol. The synthesized Co/rGO was characterized by transmission electron microscopy (TEM), high-angle annular dark-field scanning TEM (HAADF-STEM), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, X-ray diffraction (XRD), and H₂ temperature-programmed reduction (H₂-TPR) analysis. According to the comprehensive characterization results, the catalyst contains single Co atoms in the graphene matrix and Co oxide nanoparticles (CoO_x) on the graphene surface. The isolated Co atoms embedded in the rGO matrix form stable metal carbides (CoC_x), which constitute catalytically active sites for hydrogenation. The rGO material with proper amounts of N heteroatoms and lattice defects becomes a suitable graphene material for fabricating the catalyst. The Co/rGO catalyst without prereduction treatment leads to the complete conversion of guaiacol with 93.2% selectivity to cyclohexanol under mild conditions. The remarkable HDO capability of the Co/rGO catalyst is attributed to the unique metal-acid synergy between the CoC_x sites and the acid sites of the CoO_x nanoparticles. The CoC_x sites provide H while the acid sites of CoO_x nanoparticles bind the C-O group of reactants to the surface, allowing easier C-O scission. The reaction pathways were characterized based on the observed reaction-product distributions. The effects of the process parameters on catalyst preparation and the HDO reaction, as well as the reusability of the catalyst, were systematically investigated.

Chemicals from Lignin: A Review of Catalytic Conversion Involving Hydrogen

Lignin is the most abundant biopolymer with aromatic building blocks and its valorization to sustainable chemicals and fuels has extremely great potential to reduce the excessive dependence on fossil resources, although such conversions remain challenging. The purpose of this Review is to present an insight into the catalytic conversion of lignin involving hydrogen, including reductive depolymerization and the hydrodeoxygenation of lignin-derived monomers to arenes, cycloalkanes and phenols, with a main focus on the catalyst systems and reaction mechanisms. The roles of hydrogenation sites (Ru, Pt, Pd, Rh) and acid sites (Nb, Ti, Mo), as well as their interaction in selective hydrodeoxygenation reactions are emphasized. Furthermore, some inspirational strategies for the production of other value-added chemicals are mentioned. Finally, some personal perspectives are provided to highlight the opportunities within this attractive field.

Product-oriented Direct Cleavage of Chemical Linkages in Lignin

Lignin is one of the most important biomacromolecules in the plant biomass and the largest renewable source of aromatic building blocks in nature. Selectively producing value-added chemicals from the catalytic transformation of renewable lignin is of strategic significance and meet sustainability targets owing to the excessive consumption of non-renewable petroleum resource, but remains a long-term challenge owing to the complexity of lignin structure. This Minireview provides a summary and perspective of the extensive research that provides insight into selectively catalytic transformations of lignin and its derived monomers via directed scissor of chemical linkages (C-O and C-C bonds) with product-oriented targets. Furthermore, some challenges and opportunities of lignin catalytic transformation are provided based on existing problems in this field for readers to discuss future research directions.

Conversion of guaiacol as lignin model component using acid-treated, multi-walled carbon nanotubes supported Ru–MnO bimetallic catalysts

Acid-treated, multi-walled carbon nanotube (AMWCNT) supported Ru and MnO bimetallic catalysts were prepared for liquid phase hydrodeoxygenation of guaiacol. The physicochemical properties of the prepared catalysts were characterized by FTIR, XRD, NH3-TPD, CO2-TPD, TEM, and XPS. MnO species were loaded on the inner surface of carbon nanotubes and were helpful for Ru particle dispersion. The 6%Ru-8%MnO/AMWCNTs with smaller Ru particle size, better dispersion, and more basic sites gave the best catalytic performance of 99.38% conversion of guaiacol and 85.84% selectivity to cyclohexanol. The effects of reaction conditions on liquid phase guaiacol hydrodeoxygenation were discussed and a possible reaction path was proposed.

Structure and Catalytic Behavior of Alumina Supported Bimetallic Au-Rh Nanoparticles in the Reduction of NO by CO

Alumina-supported bimetallic AuRh catalysts, as well as monometallic reference catalysts, were examined with regard to their structural and catalytic properties in the reduction of NO by CO. Depending on the molar ratio of Au:Rh, the nanoparticles prepared by borohydride co-reduction of corresponding metal salt solutions had a size of 3.5–6.7 nm. The particles consisted of well-dispersed noble metal atoms with some enrichment of Rh in their surface region. NO conversion of AuRh/Al2O3 shifted to lower temperatures with increasing Rh content, reaching highest activity and highest N2 selectivity for the monometallic Rh/Al2O3 catalyst. This behavior is attributed to the enhanced adsorption of CO on the bimetallic catalyst resulting in unfavorable cationic Rh clusters Rh+-(CO)2. Doping with ceria of AuRh/Al2O3 and Rh/Al2O3 catalysts increased the surface population of metallic Rh sites, which are considered most active for the reduction of NO by CO and enhancement of the formation of intermediate isocyanate (-NCO) surface species and their reaction with NO to form N2 and CO2.

Modelling free and oxide-supported nanoalloy catalysts: comparison of bulk-immiscible Pd–Ir and Au–Rh systems and influence of a TiO2 support

DFT calculations on free and TiO₂-supported Pd–Ir and Au–Rh nanoalloys reveal that Janus and core–shell configurations compete on oxide supports.