On the nature of Pt-carbon interactions for enhanced hydrogen generation

Aqueous Phase Reforming over Platinum Catalysts on Doped Carbon Supports: Exploring Platinum-Heteroatom Interactions

A series of platinum catalysts supported on carbon nanofibers with various heteroatom dopings were synthesized to investigate the effect of the local platinum environment on the catalytic activity and selectivity in aqueous phase reforming (APR) of ethylene glycol (EG). Typical carbon dopants such as oxygen, nitrogen, sulfur, phosphorus, and boron were chosen based on their ability to bring acidic or basic functional groups to the carbon surface. In situ X-ray absorption spectroscopy (XAS) was used to identify the platinum oxidation state and platinum species formed during APR of EG through multivariate curve resolution alternating least-squares analysis, observing differences in activity, selectivity, and platinum local environment among the catalysts. The platinum-based catalyst on the nitrogen-doped carbon support demonstrated the most favorable properties for H2 production due to high Pt dispersion and basicity (H2 site time yield 22.7 h-1). Direct Pt-N-O coordination was identified by XAS in this catalyst. The sulfur-doped catalyst presented Pt-S contributions with the lowest EG conversion rate and minimal production of the gas phase components. Boron and phosphorus-doped catalysts showed moderate activity, which was affected by low platinum dispersion on the carbon support. The phosphorus-doped catalyst showed preferential selectivity to alcohols in the liquid phase, associated with the presence of acid sites and Pt-P contributions observed under APR conditions.

Defect-Engineered Charge Transfer in a PtCu/PrxCe1-xO2 Carbon-Free Catalyst for Promoting the Methanol Oxidation and Oxygen Reduction Reactions

Platinum (Pt) and Pt-based alloys have been extensively studied as efficient catalysts for both the anode and cathode of direct methanol fuel cells (DMFC). Defect engineering has been revealed to be practicable in tuning the charge transfer between Pt and transition metals/supports, which leads to the charge density rearrangement and facilitates the electrocatalytic performance. Herein, Pr-doped CeO2 nanocubes were used as the noncarbon support of a PtCu catalyst. The concentration and structure of oxygen vacancy (Vo) defects were engineered by Pr doping. Besides the Vo monomer, the oxygen vacancy with a linear structure is also observed, leading to the one-dimensional PtCu. The Vo concentration shows the volcanic scenario as Pr increased. Accordingly, the activities of PtCu/PrxCe1-xO2 toward methanol oxidation and oxygen reduction reactions exhibit the volcanic scenario. PtCu/Pr0.15Ce0.85O2 exhibits the optimal catalytic performance with the specific activity 3.57 times higher than that of Pt/C toward MOR and 1.34 times higher toward ORR. The MOR and ORR mass activities of PtCu/Pr0.15Ce0.85O2 reached 1.05 and 0.12 A·mg-1, which are 3.09 and 0.92 times the values of Pt/C, respectively. The abundant Vo afforded surplus electrons, which tailored the electron transfer between PtCu and PrxCe1-xO2, leading to enhanced catalytic performance of PtCu/PrxCe1-xO2. DFT calculations on PtCu/Pr0.15Ce0.85O2 revealed that Pr doping reduced the band gap of CeO2 and lowered the overpotential.

Ultrafine Pt nanoparticles anchored on core-shell structured zeolite-carbon for efficient catalysis of hydrogen generation

Ammonia borane (AB) is a potential hydrogen storage material with high-efficiency hydrolytic dehydrogenation under a suitable catalyst. Noble metal catalysts have drawn a lot of attention. In this study, a carbon-coated zeolite was obtained by calcination at high temperatures using glucose as a carbon source. Pt nanoparticles were fixed on a core-shell composite support by a simple chemical reduction method. A series of catalysts were prepared with different synthesis parameters. The results show that PSC-2 has excellent catalytic performance for hydrolytic dehydrogenation of AB in alkaline solution at room temperature, and the turnover frequency (TOF) is 593 min-1. The excellent catalytic performance is attributed to the carbon layer on the zeolite surface which inhibits the aggregation or deformation of metals in the catalytic reaction. The metal-support interaction activates the water and accelerates the rate-limiting step of hydrolysis. The activation energy (E a = 44 kJ mol-1) was calculated based on the reaction temperature. In addition, the kinetics of AB hydrolysis was studied, and the effects of catalyst concentration, AB concentration and NaOH concentration on AB hydrolysis rate were further investigated. The high-efficiency catalyst prepared in this work provides a new strategy for the development of chemical hydrogen production in the field of catalysis.

Porous Co-Pt Nanoalloys for Production of Carbon Nanofibers and Composites

The controllable synthesis of carbon nanofibers (CNF) and composites based on CNF (Metals/CNF) is of particular interest. In the present work, the samples of CNF were produced via ethylene decomposition over Co-Pt (0-100 at.% Pt) microdispersed alloys prepared by a reductive thermolysis of multicomponent precursors. XRD analysis showed that the crystal structure of alloys in the composition range of 5-35 at.% Pt corresponds to a fcc lattice based on cobalt (Fm-3m), while the CoPt (50 at.% Pt) and CoPt₃ (75 at.% Pt) samples are intermetallics with the structure P4/mmm and Pm-3m, respectively. The microstructure of the alloys is represented by agglomerates of polycrystalline particles (50-150 nm) interconnected by the filaments. The impact of Pt content in the Co_1-xPt_x samples on their activity in CNF production was revealed. The interaction of alloys with ethylene is accompanied by the generation of active particles on which the growth of nanofibers occurs. Plane Co showed low productivity (~5.5 g/g_cat), while Pt itself exhibited no activity at all. The addition of 15-25 at.% Pt to cobalt catalyst leads to an increase in activity by 3-5 times. The maximum yield of CNF reached 40 g/g_cat for Co_0.75Pt_0.25 sample. The local composition of the active alloyed particles and the structural features of CNF were explored.

Magnetically Isolable Pt0/Co3O4 Nanocatalysts: Outstanding Catalytic Activity and High Reusability in Hydrolytic Dehydrogenation of Ammonia Borane

The development of a new platinum nanocatalyst to maximize the catalytic efficiency of the precious noble metal catalyst in releasing hydrogen from ammonia borane (AB) is reported. Platinum(0) nanoparticles are impregnated on a reducible cobalt(II,III) oxide surface, forming magnetically isolable Pt⁰/Co₃O₄ nanocatalysts, which have (i) superb catalytic activity providing a record turnover frequency (TOF) of 4366 min^-1 for hydrogen evolution from the hydrolysis of AB at room temperature and (ii) excellent reusability, retaining the complete catalytic activity even after the 10th run of hydrolysis reaction. The outstanding activity and stability of the catalyst can be ascribed to the strong interaction between the platinum(0) nanoparticles and reducible cobalt oxide, which is supported by the results of XPS analysis. Pt⁰/Co₃O₄ exhibits the highest TOF among the reported platinum-nanocatalysts developed for hydrogen generation from the hydrolysis of AB.

Cobalt ferrite supported platinum nanoparticles: Superb catalytic activity and outstanding reusability in hydrogen generation from the hydrolysis of ammonia borane

In this work, platinum(0) nanoparticles are deposited on the surface of magnetic cobalt ferrite forming magnetically separable Pt⁰/CoFe₂O₄ nanoparticles, which are efficient catalysts in H₂ generation from the hydrolysis of ammonia borane. Catalytic activity of Pt⁰/CoFe₂O₄ nanoparticles decreases with the increasing platinum loading, parallel to the average particle size. Pt⁰/CoFe₂O₄ (0.23% wt. Pt) nanoparticles have an average diameter of 2.30 ± 0.47 nm and show an extraordinary turnover frequency of 3628 min^-1 in releasing 3.0 equivalent H₂ per mole of ammonia borane from the hydrolysis at 25.0 °C. Moreover, the magnetically separable Pt⁰/CoFe₂O₄ nanoparticles possess high reusability retaining 100% of their initial catalytic activity even after ten runs of hydrolysis. The superb catalytic activity and outstanding reusability make the Pt⁰/CoFe₂O₄ nanoparticles very attractive catalysts for the hydrogen generation systems in portable and stationary fuel cell applications.