Tailoring the multi-functionalities of one-dimensional ceria nanostructures via oxygen vacancy modulation

Mechanism insight into double S-scheme heterojunctions and atomic vacancies with tunable band structures for notably enhanced light-driven enrofloxacin decomposition

Building narrow band gap semiconductors and fast separation of photogenerated electron-hole (e--h+) structures are of great significance for photocatalytic process. In this contribution, the CeO2-x/C3-yN4/Ce(CO3)(OH) double S-scheme heterojunctions with atomic vacancies tunable band gap (2.54 eV) have been designed and fabricated as a boost photocatalyst for enrofloxacin (ENR) photodegradation. Compared with the control samples, the experimental results indicate that the typical sample (CeO2-x/C3-yN4/Ce(CO3)(OH)-2) achieves the highest ENR photodegradation efficiency (93.6 %) in 240 min under a pH of 6, and the possible photodegradation pathways are also proposed. The superior performance is ascribed to the CeO2-x/C3-yN4/Ce(CO3)(OH) double S-scheme heterojunctions for selective recombination of photogenerated electrons with weak-reduction ability in conduction band (CB) of CeO2-x, C3-yN4 and the photogenerated holes with weak-oxidation nature in valance band (VB) of C3-yN4, Ce(CO3)(OH), which increase the retention rate of photogenerated electrons in CB of Ce(CO3)(OH) and photogenerated holes in VB of CeO2-x to degrade ENR. This is the first systematic study of CeO2-x/C3-yN4/Ce(CO3)(OH) double S-scheme heterojunctions for ENR photodegradation.

Evaluation of Photocatalytic Performance of Nano-Sized Sr0.9La0.1TiO3 and Sr0.25Ca0.25Na0.25Pr0.25TiO3 Ceramic Powders for Water Purification

Water pollution is a significant issue nowadays. Among the many different technologies for water purification, photocatalysis is a very promising and environment-friendly approach. In this study, the photocatalytic activity of Sr_0.9La_0.1TiO₃ (SLTO) and Sr_0.25Ca_0.25Na_0.25Pr_0.25TiO₃ (SCNPTO) nano-sized powders were evaluated by degradation of pindolol in water. Pindolol is almost entirely insoluble in water due to its lipophilic properties. The synthesis of the SCNPTO was performed using the reverse co-precipitation method using nitrate precursors, whereas the SLTO was produced by spray pyrolysis (CerPoTech, Trondheim Norway). The phase purity of the synthesized powders was validated by XRD, while HR-SEM revealed particle sizes between 50 and 70 nm. The obtained SLTO and SCNPTO powders were agglomerated but had relatively similar specific surface areas of about 27.6 m² g^-1 and 34.0 m² g^-1, respectively. The energy band gaps of the SCNPTO and SLTO were calculated (DFT) to be about 2.69 eV and 3.05 eV, respectively. The photocatalytic performances of the materials were examined by removing the pindolol from the polluted water under simulated solar irradiation (SSI), UV-LED irradiation, and UV irradiation. Ultra-fast liquid chromatography was used to monitor the kinetics of the pindolol degradation with diode array detection (UFLC-DAD). The SLTO removed 68%, 94%, and 100% of the pindolol after 240 min under SSI, UV-LED, and UV irradiation, respectively. A similar but slightly lower photocatalytic activity was obtained with the SCNPTO under identical conditions, resulting in 65%, 84%, and 93% degradation of the pindolol, respectively. Chemical oxygen demand measurements showed high mineralization of the investigated mixtures under UV-LED and UV irradiation.

The preparation of ultrastable Al3+ doped CeO2 supported Au catalysts: Strong metal-support interaction for superior catalytic activity towards CO oxidation

The classical strong metal-support interaction (SMSI) plays a key role in improving thermal stability for supported Au catalysts. However, it always decreases the catalytic activity because of the encapsulation of Au species by support. Herein, we demonstrate that Al³⁺ is a functional additive which could effectively improve both catalytic activity and sintering resistant property for H₂ pretreated Al³⁺ doped CeO₂ supported Au (AuCeAl) catalyst at high temperature. The physical characterization and in-situ DRIFTS results provide insight that more oxygen vacancies generated by Al³⁺ doping could be as preferential adsorption sites for CO molecules when the encapsulation of Au species occurred, which is certificated by an accelerated formation of bicarbonate species. In the meantime, smaller Au nanoparticles with higher dispersion (2.8 nm, 85.63%) is achieved in AuCeAl catalysts, compared with that in CeO₂ supported Au (AuCe) catalysts (5.1 nm, 36.17%). Additionally, the as-prepared AuCeAl catalysts also have superior catalytic performance even after calcination at 800 °C in air.

Microwave-assisted synthesis of 3D Bi2MoO6 microspheres with oxygen vacancies for enhanced visible-light photocatalytic activity

Oxygen vacancies (OVs) defects in metal oxide-based photocatalysts play a crucial role in improving the charge carrier separation efficiencies to enhance the photocatalytic performances. In this work, OVs were introduced in 3D Bi₂MoO₆ microspheres through a facile and fast microwave-assisted method via the modulation of tetramethylethylenediamine (TMEDA). EPR, Raman and XPS results demonstrated that large amounts of oxygen vacancies were formed on the surface of BMO microspheres. The photocatalytic properties of the samples were studied by degradation of tetracycline (TC) under visible light. The optimal Bi₂MoO₆ with OVs exhibited optimum photocatalytic activity, and the degradation rate was 7.0 times higher than that of pristine Bi₂MoO₆. This enhancement can be attributed to the 3D structure furnishing more surface active sites and suitable OVs defects favoring the electron-hole separation. Moreover, the defective Bi₂MoO₆ microspheres exhibit high stability because the photocatalytic activity remains almost unchanged after 5 cycles, making them favorable for practical applications. Finally, a possible visible light photocatalysis mechanism for the degradation of TC was tentatively proposed.

Promoting surface oxygen vacancies on ceria via light pretreatment to enhance catalytic ozonation

Oxygen vacancies catalyzed ozone into hydroxyl radicals which accelerated organic mineralization. Light pre-treatment of ceria intensifies its oxygen vacancy defect levels which are central to its performance in catalytic ozonation.

The construction of an electrochemical sensing interface based on nano-CeO2 cubes for highly sensitive detection of bisphenol A

A highly sensitive electrochemical sensor for BPA was established based on the CeO₂ nanocubes with abundant oxygen vacancies in lattice.