Facile solvothermal synthesis of Pt71Co29 lamellar nanoflowers as an efficient catalyst for oxygen reduction and methanol oxidation reactions

NiIr Nanowire Assembles as an Efficient Electrocatalyst Towards Oxygen Evolution Reaction in Both Acid and Alkaline Media

Oxygen evolution reaction (OER) is the rate-limiting step in water electrolysis due to its sluggish kinetic, and it is challenging to develop an OER catalyst that could work efficiently in both acid and alkaline environment. Herein, NiIr nanowire assembles (NAs) with unique nanoflower morphology were prepared by a facile hydrothermal method. As a result, the NiIr NAs exhibited superior OER activity in both acid and alkaline media. Specifically, in 0.1 M HClO4, NiIr NAs presented a superior electrocatalytic performance with a low overpotential of merely 242 mV at 10 mA cm-2 and a Tafel slope of only 58.1 mV dec-1, surpassing that of commercial IrO2 and pure Ir NAs. And it achieved a significantly higher mass activity of 148.40 A/g at -1.5 V versus RHE. In 1.0 M KOH, NiIr NAs has an overpotential of 291 mV at 10 mA cm-2 and a Tafel slope of 42.1 mV dec-1. Such remarkable activity makes the NiIr NAs among the best of recently reported representative Ir-based OER electrocatalysts. Density functional theory (DFT) calculations confirmed alloying effect promotes surface bonding of NiIr with oxygen-containing reactants, resulting in excellent catalytic properties.

Fabrication of Pb-Containing PtAu Nanoflowers via Galvanic Replacement Method for Electrocatalytical Oxidation of Methanol

A Pb-containing PtAu nanoflower electrocatalyst was deposited on the cathode via galvanic replacement reaction in a double-cabin galvanic cell (DCGC) with a Cu plate as the anode, a multiwalled carbon nanotube (MWCNT) modified glassy carbon electrode (GCE) as the cathode, 0.1 M HClO4 aqueous solution as the anolyte, and Pb2+-containing Pt4+ salt and Au3+ salt mixed aqueous solution as the catholyte, respectively, and the electrocatalytic performance of the modified electrode toward methanol oxidation in the alkaline medium was investigated. Electrochemical studies reveal that the stripping of bulk Cu can induce underpotential deposition (UPD) of Pb on Pt during the galvanic replacement reaction, which affects the morphology and composition of Pb-containing PtAu nanoparticles. Under the optimal experimental conditions, a Pb-Pt3Au1/MWCNTs/GCE shows the highest activity and the best stability toward electrocatalytic oxidation of methanol in the alkaline medium, and the Pt active area-normalized specific electrocatalytic activity of Pb-Pt3Au1/MWCNTs/GCE is as high as 59.8 mA cmPt-2. We believe that the method presented here of depositing highly active noble metal nanostructures by galvanic replacement reaction in a DCGC device is expected to be widely applied in the preparation of nanomaterials for their study in fuel cells and electrocatalysis.

Nanostructure engineering of Pt/Pd-based oxygen reduction reaction electrocatalysts

Increasing the atomic utilization of Pt and Pd elements is the key to the advancement and broad dissemination of fuel cells. Central to this task is the design and fabrication of highly active and stable Pt- or Pd-based electrocatalysts for the oxygen reduction reaction (ORR), which requires a comprehensive understanding of the ORR pathways and mechanism. Past endeavors have accumulated a wealth of knowledge about the Pt/Pd-based ORR electrocatalysts based on structure engineering, while a systematic review of the nanostructure engineering of Pt/Pd-based ORR electrocatalysts has been rarely reported. In this review, we provide a systematic discussion about the current status of Pt/Pd-based ORR electrocatalysts from the perspective of nanostructure engineering, and we highlight the ORR pathways, mechanisms and theories in order to understand the ORR in a more complex nanocatalyst. Particularly, the underlying structure-function relationship of Pt/Pd-based ORR electrocatalysts is specifically highlighted, which will guide the future synthesis of more efficient ORR electrocatalysts.

Low-Dimensional High-Entropy Alloys for Advanced Electrocatalytic Reactions

Low-dimensional high-entropy alloy (HEA) nanomaterials are widely employed as electrocatalysts for energy conversion reactions, due to their inherent advantages, including high electron mobility, rich catalytically active site, optimal electronic structure. Moreover, the high-entropy, lattice distortion, and sluggish diffusion effects also enable them to be promising electrocatalysts. A thorough understanding on the structure-activity relationships of low-dimensional HEA catalyst play a huge role in the future pursuit of more efficient electrocatalysts. In this review, we summarize the recent progress of low-dimensional HEA nanomaterials for efficient catalytic energy conversion. By systematically discussing the fundamentals of HEA and properties of low-dimensional nanostructures, we highlight the advantages of low-dimensional HEAs. Subsequently, we also present many low-dimensional HEA catalysts for electrocatalytic reactions, aiming to gain a better understanding on the structure-activity relationship. Finally, a series of upcoming challenges and issues are also thoroughly proposed as well as their future directions.

Recent advances in nanoflowers: compositional and structural diversification for potential applications

In recent years, nanoscience and nanotechnology have emerged as promising fields in materials science. Spectroscopic techniques like scanning tunneling microscopy and atomic force microscopy have revolutionized the characterization, manipulation, and size control of nanomaterials, enabling the creation of diverse materials such as fullerenes, graphene, nanotubes, nanofibers, nanorods, nanowires, nanoparticles, nanocones, and nanosheets. Among these nanomaterials, there has been considerable interest in flower-shaped hierarchical 3D nanostructures, known as nanoflowers. These structures offer advantages like a higher surface-to-volume ratio compared to spherical nanoparticles, cost-effectiveness, and environmentally friendly preparation methods. Researchers have explored various applications of 3D nanostructures with unique morphologies derived from different nanoflowers. The nanoflowers are classified as organic, inorganic and hybrid, and the hybrids are a combination thereof, and most research studies of the nanoflowers have been focused on biomedical applications. Intriguingly, among them, inorganic nanoflowers have been studied extensively in various areas, such as electro, photo, and chemical catalysis, sensors, supercapacitors, and batteries, owing to their high catalytic efficiency and optical characteristics, which arise from their composition, crystal structure, and local surface plasmon resonance (LSPR). Despite the significant interest in inorganic nanoflowers, comprehensive reviews on this topic have been scarce until now. This is the first review focusing on inorganic nanoflowers for applications in electro, photo, and chemical catalysts, sensors, supercapacitors, and batteries. Since the early 2000s, more than 350 papers have been published on this topic with many ongoing research projects. This review categorizes the reported inorganic nanoflowers into four groups based on their composition and structure: metal, metal oxide, alloy, and other nanoflowers, including silica, metal-metal oxide, core-shell, doped, coated, nitride, sulfide, phosphide, selenide, and telluride nanoflowers. The review thoroughly discusses the preparation methods, conditions for morphology and size control, mechanisms, characteristics, and potential applications of these nanoflowers, aiming to facilitate future research and promote highly effective and synergistic applications in various fields.

Noble metal nanodendrites: growth mechanisms, synthesis strategies and applications

Inorganic nanodendrites (NDs) have become a kind of advanced nanomaterials with broad application prospects because of their unique branched architecture. The structural characteristics of nanodendrites include highly branched morphology, abundant tips/edges and high-index crystal planes, and a high atomic utilization rate, which give them great potential for usage in the fields of electrocatalysis, sensing, and therapeutics. Therefore, the rational design and controlled synthesis of inorganic (especially noble metals) nanodendrites have attracted widespread attention nowadays. The development of synthesis strategies and characterization methodology provides unprecedented opportunities for the preparation of abundant nanodendrites with interesting crystallographic structures, morphologies, and application performances. In this review, we systematically summarize the formation mechanisms of noble metal nanodendrites reported in recent years, with a special focus on surfactant-mediated mechanisms. Some typical examples obtained by innovative synthetic methods are then highlighted and recent advances in the application of noble metal nanodendrites are carefully discussed. Finally, we conclude and present the prospects for the future development of nanodendrites. This review helps to deeply understand the synthesis and application of noble metal nanodendrites and may provide some inspiration to develop novel functional nanomaterials (especially electrocatalysts) with enhanced performance.

Pd-Based Metallenes for Fuel Cell Reactions

Pd-based metallenes, atomically thin layers composed primarily of under-coordinated Pd atoms, have emerged as the newest members in the family of two-dimensional (2D) nanomaterials. Moreover, the unique physiochemical properties, high intrinsic activity associated with metallenes coupled with the ease of applying chemical modifications result in great potential in catalyst engineering for fuel cell reactions. Especially in recent years, interest in Pd-based metallenes is growing, as evidenced by surge in available literatures. Herein, we have reviewed the recent findings achieved in Pd-based metallenes in fuel cells by highlighting the technologies available for deriving metallenes and manifesting the modification strategies for designing them to better suit the application demand. Moreover, we also discuss the perspective insights of Pd-based metallenes for fuel cells regarding the surfactant-free synthesis method, strain engineering, constructing high-entropy alloy, and so on.

Advances in platinum-based and platinum-free oxygen reduction reaction catalysts for cathodes in direct methanol fuel cells

Direct methanol fuel cells (DMFCs) have been the focus of future research because of their simple structure, abundant fuel sources, high energy conversion efficiency and low cost. Among the components in DMFC, the activity and stability of the cathode catalyst is the key to the performance and lifetime of the DMFCs. Oxygen reduction reaction (ORR) is an important electrode reaction on DMFC cathode. It is known that Pt is widely used in the fabrication of ORR catalysts, but the limited earth storage of Pt and its high price limit the use of Pt-based commercial catalysts in DMFCs. To overcome these problems, advances have been made on new low Pt-based catalysts and Pt-free catalysts in recent years. In this article, the development of novel ORR catalysts and the carbon supports is reviewed and discussed.

Pt-Co Electrocatalysts: Syntheses, Morphologies, and Applications

Pt-Co electrocatalysts have attracted significant attention because of their excellent performance in many electrochemical reactions. This review focuses on Pt-Co electrocatalysts designed and prepared for electrocatalytic applications. First, the various synthetic methods and synthesis mechanisms are systematically summarized; typical examples and core synthesis parameters are discussed for regulating the morphology and structure. Then, starting with the design and structure-activity relationship of catalysts, the research progress of the morphologies and structures of Pt-Co electrocatalysts obtained based on various strategies, the structure-activity relationship between them, and their properties are summarized. In addition, the important electrocatalytic applications and mechanisms of Pt-Co catalysts, including electrocatalytic oxidation/reduction and bifunctional catalytic reactions, are described and summarized, and their high catalytic activities are discussed on the basis of their mechanism and active sites. Moreover, the advanced electrochemical in situ characterization techniques are summarized, and the challenges and direction concerning the development of high-performance Pt-Co catalysts in electrocatalysis are discussed.

Batch synthesis of high activity and durability carbon supported platinum catalysts for oxygen reduction reaction using a new facile continuous microwave pipeline technology

Traditional synthesis methodologies for fuel cell catalyst production involve long reactions and uncontrollable reaction processes. Synthesis methods for the production of catalysts typically have difficulties to achieve catalysts materials with consistency, high activity, and durability. In this study, a fast, simple, and suitable continuous pipeline microwave method for catalyst mass production was developed, with the carbon carrier being treated at different temperatures simultaneously. The method herein developed resulted in carbon-supported platinum (Pt) catalysts with high activity and high durability. In addition, the half-wave potential of the catalyst exceeded 0.9 V, the electrochemical active surface area reached 85.7 m²-g_Pt^-1, and the mass specific activity reached 171.1 mA-mg^-1. Remarkably, after 30,000 cycles of Pt attenuation tests and 30,000 cycles of carbon carrier attenuation tests, the retention rate of the annealed carbon carrier catalyst reached 80 %. As a membrane electrode, the catalyst generated a single cell maximum power density of 1.4 W-cm^-2, and the Pt content reached 0.286 g_Pt-kW^-1. The work provides an effective and practical method for the mass production of high-performance and high-durability catalysts, which guiding significance for mass production of catalysts.

Label-free electrochemical biosensor for determination of procalcitonin based on graphene-wrapped Co nanoparticles encapsulated in carbon nanobrushes coupled with AuPtCu nanodendrites

A new label-free electrochemical immunosensor was constructed for quantitative detection of procalcitonin (PCT), by employing AuPtCu nanodendrites (AuPtCu NDs, prepared by a one-pot solvothermal method) and graphene-wrapped Co nanoparticles encapsulated in 3D N-doped carbon nanobrushes (G-Co@ NCNBs), obtained by self-catalyzed chemical vapor deposition as immune-sensing platform. Impressively, the home-made nanocomposite enlarged the highly accessible active sites and promoted the mass/electron transport, in turn showing the efficient synergistic catalysis towards H₂O₂ reduction, combined by greatly increasing the loading capacity of the PCT antibody (Ab). The as-constructed sensor displayed a dynamic linear range of 0.0001 ~ 100 ng mL^-1 along with an ultra-low limit of detection (LOD = 0.011 pg mL^-1, S/N = 3) and was further explored for determination of PCT in a diluted serum sample with acceptable results. The sensor provides some valuable guidelines for bioassay and early diagnosis of sepsis.

Synthesis of PtRu alloy nanofireworks as effective catalysts toward glycerol electro-oxidation in alkaline media

Electro-oxidation of glycerol is a key anodic reaction in direct alcohol fuel cell (DAFCs). Exploring the cost-effective nanocatalysts for glycerol oxidation reaction (GOR) is very important for the development of DAFC, but it is still challenging. In this paper, nanofirework-like PtRu alloy catalyst was successfully synthesized and used for GOR in alkaline medium. Thanks to the unique nanofirework-like structure and synergetic effects, the activity and stability of the as-prepared PtRu alloy nanofireworks (NFs) toward GOR were significantly improved relative to Pt NFs. In particular, the peak current density of GOR catalyzed by the optimized Pt₁Ru₃ NFs catalyst reached 2412.0 mA mg^-1, surpassing that of commercial Pt/C catalyst. This work has important guidance for the design of advanced anode electrocatalysts for fuel cells.

Preparation of Reduced-Graphene-Oxide-Supported CoPt and Ag Nanoparticles for the Catalytic Reduction of 4-Nitrophenol

Composite nanostructure materials are widely used in catalysis. They exhibit several characteristics, such as the unique structural advantage and the synergism among their components, which significantly enhances their catalytic performance. In this work, CoPt nanoparticles and reduced-graphene-oxide-based nanocomposite catalysts (rGO/CoPt, rGO/CoPt/Ag) were prepared by using a facile co-reduction strategy. The crystalline structure, morphology, composition, and optical characteristics of the CoPt nanoparticles, rGO/CoPt nanocomposite, and rGO/CoPt/Ag nanocomposite catalysts were investigated by a set of techniques. The ID/IG value of the rGO/CoPt/Ag nanocomposite is 1.158, higher than that of rGO/CoPt (1.042). The kinetic apparent rate constant, k, of the rGO/CoPt/Ag nanocomposite against 4-nitrophenol (4-NP) reduction is 5.306 min−1, which is higher than that of CoPt (0.495 min−1) and rGO/CoPt (1.283 min−1). The normalized rate constant, knor, of the rGO/CoPt/Ag nanocomposite is 56.76 min−1mg−1, which is higher than some other catalytic materials. The rGO/CoPt/Ag nanocomposite shows a significantly enhanced catalytic performance when compared to CoPt nanoparticles and the rGO/CoPt nanocomposite, which may confirm that the novel rGO/CoPt/Ag nanocomposite is a promising catalyst for the application of catalytic fields.

Alternative Aqueous Phase Synthesis of a PtRu/C Electrocatalyst for Direct Methanol Fuel Cells

Carbon-supported PtRu nanoalloy (PtRu/C) is widely used as the anode catalyst for direct methanol fuel cells (DMFC), and an aqueous phase synthesis of PtRu/C is in high demand due to for energy-saving and environmentally-benign considerations, however, it is very challenging to attain stoichiometric reduction, good dispersion and a high alloying degree. Herein, we report a facile aqueous phase approach with dimethylamine borane (DMAB) as the reducing agent to synthesize a PtRu/C(DMAB). TEM, XRD, XPS and ICP-AES characterizations indicate that the structural parameters in the PtRu/C(DMAB) are improved significantly as compared to those obtained in a PtRu/C(NaBH4) and a commercial PtRu/C, contributing to an enhanced electrocatalytic performance. It turns out that the PtRu/C(DMAB) exhibits the highest methanol electro-oxidation (MOR) performance among all of the tested samples, with the peak current up to 1.8 times as much as that of the state-of-the-art commercial PtRu/C, corroborating the highest output power density in comparative DMFC tests. In-situ attenuated total reflection infrared (ATR-IR) spectroscopy correlates the higher methanol electro-oxidation performance of the PtRu/C(DMAB) with its enhanced CO resistance and CO2 generation. This simple aqueous synthetic approach may provide an alternative route for developing efficient anode electrocatalysts of DMFCs.

A label-free electrochemical immnunosensor based on signal magnification of oxygen reduction reaction catalyzed by uniform PtCo nanodendrites for highly sensitive detection of carbohydrate antigen 15-3

Developing a highly sensitive immunoassay for tumor biomarkers is particularly important in bioanalysis and early disease diagnosis. In this work, a simple one-pot solvothermal method was developed for controllable synthesis of well-dispersed PtCo alloyed nanodendrites (PtCo NDs) by using l-carnosine as the co-structure-directing agent. The PtCo NDs had a large specific surface area and provided abundant active sites available for electrocatalytic oxygen reduction reaction (ORR). Based on the highly enhanced currents of the ORR, a novel label-free electrochemical immunosensor was fabricated for highly sensitive assay of carbohydrate antigen 15-3 (CA15-3). The sensor showed a wide linear range of 0.1-200 U mL^-1 and a low limit of detection (LOD) down to 0.0114 U mL^-1 (S/N = 3), in turn exploring its application to diluted human serum samples with satisfactory results. This study provides a feasible platform for monitoring other tumor markers in clinical diagnosis.

A mass-producible integrative structure Pt alloy oxygen reduction catalyst synthesized with atomically dispersive metal-organic framework precursors

Oxygen reduction reaction (ORR) catalyst is one of the most significant influential factors for the application of proton exchange membrane fuel cells. This work introduces a mass-producible high-performance PtZn alloy integrative structure ORR catalyst, synthesized with the atomically dispersive metal-organic framework precursors. This PtZn catalyst displays excellent catalytic activity with the onset reduction potential of 1.0 V_RHE@ 0.16 mA cm^-2 (Reversible hydrogen electrode; RHE) and the half-wave potential of 0.934 V_RHE for the ORR catalysis. The calculated specific activity and mass activity at 0.9 V are 9.44 A m^-2 and 544 A g_Pt^-1, respectively, which are 5.62 times and 5.77 times as high as the commercial Pt/C. The mass activity is remarkably higher than the target put forward by the Department of Energy (DOE; 440 A g_Pt^-1). Furthermore, this PtZn catalyst also exhibits outstanding stability after the 10,000 potential cyclic degeneration test. The ORR current is much higher than Pt/C in the whole potential range not only before but also after the 10,000 potential cycles with identical Pt loading. This catalyst has a multifarious active-site catalytic structure with PtZn alloyed particles and atomically dispersive metal-N active sites on the N-doped graphited carbon matrix, exhibiting appealing ORR catalytic activity and sound stability for the application and scalable production of fuel cell catalysts.

Methanol, Ethanol, and Formic Acid Oxidation on New Platinum-Containing Catalysts

Electrooxidation of methanol, ethanol, and formic acid was studied on three platinum-containing electrocatalysts: PtCu/C, Pt/(SnO2/C), and Pt/C, Pt content being about 20 wt%. In all reactions, the integral specific activity of the catalysts, estimated from the results of cyclic voltammetry, grows in the Pt/C < Pt/(SnO2/C) < PtCu/C row. The influence of the reagent nature subjected to electrooxidation is manifested both in the difference of the absolute rate values of the corresponding reactions, decreasing in the order CH3OH > HCOOH > C2H5OH, and in the different ratio of these rates on different catalysts and at different potentials. Pt/(SnO2/C) catalyst containing SnO2 nanoparticles is the most active among the studied catalysts in methanol and formic acid electrooxidation reactions under potentiostatic conditions at the E = 0.60 V. Moreover, in formic acid electrooxidation reaction it is significantly superior to even the PtRu/C commercial catalyst. The reasons for the positive influence of Cu atoms and SnO2 nanoparticles on the catalytic activity of platinum are presumably associated with different effects: Interaction of the d-orbitals of copper and platinum atoms in bimetallic nanoparticles and implementation of the bifunctional catalysis mechanism on the adjacent platinum and tin dioxide nanoparticles.

Cu-Doped Co3O4 microstructure as an efficient non-noble metal electrocatalyst for methanol oxidation in a basic solution

Co₃O₄ doped with copper at different concentrations was used to catalyze methanol oxidation reactions.

Electrochemical reduction of CO2 using Germanium-Sulfide-Indium amorphous glass structures

The research in electrochemical reduction of CO₂ is shifting towards the discovery of new and novel materials. This study shows a new class of material, that of Ge-S-In chalcogenide glass, to be active for reduction of CO₂ in aqueous solutions. Experiments were conducted with bulk and particle form of the material, yielding different product for each structural form. Faradaic efficiency of upto 15% was observed in bulk form for CO production while formic acid with up to 26.1 % faradaic efficiency was measured in powder form. Chalcogenide studies have focused primarily on the photoelectrochemical reduction however these results provide a strong merit for introducing metal in chalcogenide glass structures for electrochemical reduction of CO₂. The activity for CO₂ reduction and the change in product selectivity reflects that further efforts to improve the glass structures can be undertaken in order to increase the faradaic efficiency and selectivity of the products.

Novel Nickel- and Magnesium-Modified Cenospheres as Catalysts for Dry Reforming of Methane at Moderate Temperatures

Cenospheres from coal fly ashes were used as support in the preparation of Ni–Mg catalysts for dry reforming of methane. These materials were characterized by means of XRD, H2-temperature-programmed reduction (H2-TPR), CO2-temperature-programmed desorption (CO2-TPD), and low-temperature nitrogen sorption techniques. The cenosphere-supported catalysts showed relatively high activity and good stability in the dry reforming of methane (DRM) at 700 °C. The catalytic performance of modified cenospheres was found to depend on both Ni and Mg content. The highest activity at 750 °C and 1 atm was observed for the catalyst containing 30 wt % Mg and 10, 20, and 30 wt % Ni, yielding to CO2 and CH4 conversions of around 95%.

Thin NiFeCr-LDHs nanosheets promoted by g-C3N4: a highly active electrocatalyst for oxygen evolution reaction

NiFeCr layered double hydroxides (NiFeCr-LDHs) supported on graphitic carbon nitride (g-C₃N₄) hybrids (NiFeCr-LDHs/g-C₃N₄) are synthesized and used as an electrocatalyst for oxygen evolution reaction (OER) in alkaline media. Effect of g-C₃N₄ on the structure and OER performance of NiFeCr-LDHs are investigated in detail. g-C₃N₄ can promote the formation of thin NiFeCr-LDHs nanosheets, thereby enhancing both the number of active sites and OER activity. X-ray photoelectron spectra measurements confirm the electronic interaction between g-C₃N₄ and NiFeCr-LDHs nanosheets. The OER performance of NiFeCr-LDHs/g-C₃N₄ hybrids highly relates to the weight ratio of g-C₃N₄ to NiFeCr-LDHs. When the weight ratio of g-C₃N₄ to NiFeCr-LDHs is 5%, the corresponding electrocatalyst shows the best OER activity. The component optimized NiFeCr-LDHs/g-C₃N₄ hybrids display the overpotential of ∼223 mV at 10 mA cm^-2 and Tafel slope of 89 mV dec^-1 for OER in 1 M KOH solution, which is better than that of pristine NiFeCr-LDHs, bare g-C₃N₄, and commercial RuO₂.

Rapid Nucleation of Reduced Graphene Oxide-Supported Palladium Electrocatalysts for Methanol Oxidation Reaction

Small sized electrocatalysts, which can be obtained by rapid nucleation and high supersaturation are imperative for outstanding methanol oxidation reaction (MOR). Conventional microwave synthesis processes of electrocatalysts include ultrasonication, stirring, pH adjustment, and microwave irradiation of the precursor mixture. Ethylene glycol (EG), which serves as a reductant and solvent was added during the ultrasonication or stirring stage. However, this step and pH adjustment resulted in unintended multi-stage gradual nucleation. In this study, the microwave reduction approach was used to induce rapid nucleation and high supersaturation in order to fabricate small-sized reduced graphene oxide-supported palladium (Pd/rGO) electrocatalysts via the delayed addition of EG, elimination of the pH adjustment step, addition of sodium carbonate (Na₂CO₃), prior microwave irradiation of the EG mixed with Na₂CO₃, and addition of room temperature precursor mixture. Besides its role as a second reducing agent, the addition of Na₂CO₃ was primarily intended to generate an alkaline condition, which is essential for the high-performance of electrocatalysts. Moreover, the microwave irradiation of the EG and Na₂CO₃ mixture generated highly reactive free radicals that facilitate rapid nucleation. Meanwhile, the room temperature precursor mixture increased supersaturation. Results showed improved electrochemically active surface area (78.97 m² g^-1, 23.79% larger), MOR (434.49 mA mg^-1, 37.96% higher) and stability.

Polyhedron-Assembled Ternary PtCuCo Nanochains: Integrated Functions Enhance the Electrocatalytic Performance of Methanol Oxidation at Elevated Temperature

Recently, the preparation of a high-performance one-dimensional alloy nanostructure for fuel cells has been given increasing attention due to its smart-structure merits and electronic effect triggered by alloying different kinds of metals at the nanoscale. In this study, unique ternary PtCuCo nanochains assembled with small polyhedra are first achieved and used as high-performance anode electrocatalysts toward methanol oxidation at elevated temperature (60 °C) that is closer to the operating temperature of direct methanol fuel cells than room temperature. The specific activity/mass activity of Pt₄₅Cu₃₅Co₂₀ one-dimensional nanochains can reach up to 18.24 mA cm^-2/4.19 A mg^-1_Pt that is 9.25/10.47 times that of commercial Pt black in sulfuric acid medium. After a 3600 s durability test, the remaining current density of Pt₄₅Cu₃₅Co₂₀ one-dimensional nanochains is 73.3 times that of commercial Pt black. The structure characterizations show that the high density of surface active sites, d-band center of the Pt downshift, moderate strain effect, and synergetic effect are jointly responsible for the enhanced electrocatalytic performance of one-dimensional ternary PtCuCo nanochains.

Atomic Carbon Layers Supported Pt Nanoparticles for Minimized CO Poisoning and Maximized Methanol Oxidation

Maximizing activity of Pt catalysts toward methanol oxidation reaction (MOR) together with minimized poisoning of adsorbed CO during MOR still remains a big challenge. In the present work, uniform and well-distributed Pt nanoparticles (NPs) grown on an atomic carbon layer, that is in situ formed by means of dry-etching of silicon carbide nanoparticles (SiC NPs) with CCl₄ gas, are explored as potential catalysts for MOR. Significantly, as-synthesized catalysts exhibit remarkably higher MOR catalytic activity (e.g., 647.63 mA mg^-1 at a peak potential of 0.85 V vs RHE) and much improved anti-CO poisoning ability than the commercial Pt/C catalysts, Pt/carbon nanotubes, and Pt/graphene catalysts. Moreover, the amount of expensive Pt is a few times lower than that of the commercial and reported catalyst systems. As confirmed from density functional theory (DFT) calculations and X-ray absorption fine structure (XAFS) measurements, such high performance is due to reduced adsorption energy of CO on the Pt NPs and an increased amount of adsorbed energy OH species that remove adsorbed CO fast and efficiently. Therefore, these catalysts can be utilized for the development of large-scale and industry-orientated direct methanol fuel cells.

Cyanogel auto-reduction induced synthesis of PdCo nanocubes on carbon nanobowls: a highly active electrocatalyst for ethanol electrooxidation

Direct ethanol fuel cells (DEFCs) with a high conversion efficiency are quite promising candidates for energy conversion devices. Herein, we have successfully synthesized PdCo alloy nanocubes supported on carbon nanobowl (denoted as Pd₂Co₁/CNB) nanohybrids by using the cyanogel auto-reduction method at high temperature. The morphology, composition and structure of Pd₂Co₁/CNB nanohybrids are characterized in detail, revealing that PdCo nanocubes have a high alloying degree and special {110} facets. In cyclic voltammetry measurements, Pd₂Co₁/CNB nanohybrids show a mass activity of 1089.0 A g _Pd^-1 and a specific activity of 40.03 mA cm^-2 for ethanol electrooxidation at peak potential, which are much higher than that of the commercial Pd/C electrocatalyst (278.2 A g_Pd^-1 and 8.22 mA cm^-2). Additionally, chronoamperometry measurements show that Pd₂Co₁/CNB nanohybrids have excellent durability for ethanol electrooxidation. A high alloying degree, special {110} facets and the CNB supporting material contribute to the high activity and durability of Pd₂Co₁/CNB nanohybrids, making them a highly promising Pt-alternative electrocatalyst for ethanol electrooxidation in DEFCs.