Enhanced photocatalytic destruction of pollutants by surface W vacancies in VW-Bi2WO6 under visible light

Novel Bi2WO6/ZnSnO3 heterojunction for the ultrasonic-vibration-driven piezocatalytic degradation of RhB

This study designed and prepared a new piezoelectric catalytic nanomaterial, Bi₂WO₆/ZnSnO₃, and applied it in piezocatalytic water purification. Results indicated that the composite had superior piezocatalytic efficiency and stability in rhodamine B (RhB) degradation under ultrasonic vibration. The Bi₂WO₆/ZnSnO₃ sample with 10% Bi₂WO₆ had the optimum activity with a degradation rate of 2.15 h^-1, which was 7.4 and 11.3 times that of ZnSnO₃ and Bi₂WO₆, respectively. Various characterizations were conducted to study the morphology, structure, and piezoelectric properties of the Bi₂WO₆/ZnSnO₃ composites and reveal the reasons for their improved piezocatalytic performance. Results showed that ZnSnO₃ cubes were dispersed throughout the surface of Bi₂WO₆ nanosheets, which enhanced the specific surface area and facilitated the piezocatalytic reaction. Additionally, type-II heterojunction structures formed at the contact interface of Bi₂WO₆ and ZnSnO₃, driving the migration of piezoelectric-induced electrons and holes. Accordingly, the separation efficiency of charge carriers improved, and the piezoelectric catalytic activity was significantly enhanced. This study may provide a potential composite catalyst and a promising idea for the design of highly efficient piezoelectric catalyst.

A prominent dual heterojunction framed CuWO4/Bi2WO6/MnS ternary NCs for para-chlorophenol degradation, Cr(VI) reduction & toxicity studies

In account of environmental remediation, an ideal photocatalyst was fabricated for the effective treatment of water systems. Herein, dual heterojunctions framed CuWO₄/Bi₂WO₆/MnS nanocomposite (NCs) was synthesized via simple co-precipitation method followed by ultra-sonicated assisted route. The prepared NCs were investigated its photocatalytic degradation performance using para-chlorophenol (4-CP) and reduction of chromium VI (Cr (VI)) under visible light irradiation. The photocatalyst were characterized by various analytical techniques including XRD, HR-TEM, XPS, UV-vis DRS, FE-SEM, EIS, PL, ESR, Raman and N₂ adsorption and desorption studies. The excellent photodegradation of 4-CP was observed within 180 min by the NCs. Similarly, the Cr (VI) reduction was about 97% within 140 min. The effect of pH and influence of different dosage of NCs and 4-CP on the photodegradation efficiency was investigated. The reusability and stability of the NCs was examined over 6 consecutive runs where the XRD and XPS confirm the structural stability of the prepared NCs. The scavenging experiment were carried out to elucidate the mechanism and the active species involved were O^2-• and OH• radicals. The TOC analysis affirmed the complete mineralization of the prepared NCs. The ecotoxicity analysis was carried out to determine the toxicity effect of intermediates using ECOSAR software and the end product toxicity was also evaluated against E. coli and S. epidermis. The end product toxicity study also confirmed that the degraded product was less toxic compared to parent compound. Further, the genotoxicity study was done to understand the environmental impact using allium cepa and results confirms that there are no causes of cytotoxicity & genotoxicity by the prepared NCs. Therefore, the prepared NCs can be economical, efficient with excellent photocatalytic performance and environment friendly.

Promoting superoxide generation in Bi2WO6 by less electronegative substitution for enhanced photocatalytic performance: an example of Te doping

Doping with elements with lower electronegativity, like Te, shifts the band potentials of Bi2WO6 to the point that superoxide radical generation is feasible. As a result, an optimum of 2.5 at% Te doping improves the activity of Bi2WO6 by 48 times.