Synergistic effects of flake-like ZnO/SnFe2O4/nitrogen-doped carbon composites on structural stability and electrochemical behavior for lithium-ion batteries

g-C3N4/graphene oxide/SnFe2O4 ternary composite for the effective sunlight-driven photocatalytic degradation of methylene blue

A broadly used dye, methylene blue (MB), adversely impacts human health and water resources, which triggers efficient methods for its elimination. Semiconductor-based heterogeneous photocatalysis is an environmentally friendly approach that effectively degrades organic pollutants. The purpose of the current work is to elucidate and validate the application of a promising g-C3N4/GO/SnFe2O4 (CGS) composite for the environmental remediation of methylene blue dye. The ternary CGS composite has been synthesized using a solvothermal approach. The fabricated composites were analyzed through FTIR, XRD, SEM/EDX, UV-VIS spectroscopy, TEM, and XPS. The photoactivity of composites and affecting parameters (pH, H2O2 dosage, composite amount, initial dye concentration, and irradiation time) were observed in sunlight illumination. The optimal conditions for photocatalytic degradation were pH = 5, photocatalyst dosage = 30 mg/100 mL, H2O2 dosage = 6 mM, and initial dye concentration (IDC) of 10 ppm employing ternary CGS composite, and MB dye was degraded effectively within 1 h. Ninety-eight percent degradation efficacy was attained by employing ternary CGS composite under the optimized conditions. Scavenging analysis suggested that •OH radicals were the key reactive oxygen species (ROS) responsible for the photodegradation of MB dye. Furthermore, the CGS nanocomposite exhibited outstanding recyclability of 84% after five consecutive runs, demonstrating its potential for use in practical applications, particularly pollutant removal.

A Spinel Tin Ferrite with High Lattice-Oxygen Anchored on Graphene-like Porous Carbon Networks for Lithium-Ion Batteries with Super Cycle Stability and Ultra-fast Rate Performances

A new type of nano-SnFe₂O₄ with stable lattice-oxygen and abundant surface defects anchored on ultra-thin graphene-like porous carbon networks (SFO@C) is prepared for the first time by an interesting freezing crystallization salt template method. The functional composite has excellent rate performance and long-term cycle stability for lithium-ion battery (LIB) anodes due to the stable structure, improved conductivity, and shortened migrating distance for lithium-ions, which are derived from the higher lattice-oxygen of SnFe₂O₄, abundant porous carbon networks and surface defects, and smaller nanoparticles. Under the ultra-high current density of 10, 15, and 20 A g^-1 cycling for 1000 times, the SFO@C can provide high reversible capacities of 522.2, 362.5, and 361.1 mAh g^-1, respectively. The lithium-ion storage mechanism of the composite was systematically studied for the first time by in situ X-ray diffraction (XRD), ex situ XRD and scanning electron microscopy (SEM), and density functional theory (DFT) calculations. The results indicate that the existence of Li₂O and metallic Fe during the lithiation/delithiation process is a key reason for reducing the initial lithium-ion storage reversibility but increasing the rate performance and capacity stability in the subsequent cycles. DFT calculations show that lithium-ions are more easily adsorbed on the (111) crystal plane with a much lower adsorption energy of -7.61 eV than other planes, and the Fe element is the main acceptor of electrons. Moreover, the kinetics investigation indicates that the lithium-ion intercalation and deintercalation in SFO@C are mainly controlled by the pseudocapacitance behavior, which is favorable to enhancing the rate performance. The research provides a new strategy for designing LIB electrode materials with a stable structure and outstanding lithium-ion storage performance.