The effect of two luting agents, pretreatment of the post, and pretreatment of the canal dentin on the retention of fiber-reinforced composite posts

Advanced Material Strategy for Restoring Damaged Endodontically Treated Teeth: A Comprehensive Review

The restoration of endodontically treated teeth (ETT) remains a significant challenge in modern dentistry. These teeth often suffer from substantial structural damage due to both the original pathology and the invasive nature of endodontic procedures. Consequently, ETT are more susceptible to fractures compared to vital teeth, necessitating restorative strategies that can effectively restore both function and aesthetics while minimizing the risk of failure. In recent years, advances in adhesive dentistry and the development of high-strength ceramics have further expanded the restorative options for ETT. Bonded restorations have gained popularity as they preserve more tooth structure and enhance the overall strenght of the tooth-restoration complex. The choice of restorative material and technique is influenced by numerous factors, including the amount of remaining tooth structure, the functional requirements of the tooth, and the aesthetic demands of the patient. Despite the plethora of available materials and techniques, the optimal approach to restoring ETT remains a topic of ongoing research and debate. In this comprehensive review, the current state of and recent advances in restoring damaged endodontically treated teeth are explored. Numerous therapeutic options exist, involving a wide range of materials. This article aims to present the biomaterial advancements of the past decade and their applications, offering alternative approaches to treating damaged ETT with the goal of prolonging their retention on the dental arch and serving as a valuable resource for dental practitioners who face this issue daily.

Influence of customization and light-curing device on the bond strength of glass fiber posts - in vitro study

Abstract Introduction Endodontically treated teeth are usually affected by extensive structure loss requiring the use of intraradicular posts to provide retention and restoration. Objective An in vitro assessment was performed on the bonding of glass fiber posts to the root dentin. Material and method Ninety (n = 10) single bovine roots were used in a 3 x 3 x 3 factorial study with subdivided plots: post customization varying the presence and type of resin (without customization, conventional resin, and Bulk Fill resin), light-curing device (Valo, Radii-Cal, Rainbow), and root third (cervical, middle, and apical). Result For the customization factor, Tukey’s test (5%) showed the superiority of the Bulk Fill (8.16 MPa) and Z350 (7.40 MPa) groups compared to the control group (4.92 MPa), without differing from each other. All light-curing devices differed, showing the superiority of Valo (9.36 MPa), Radii (6.96 MPa) as an intermediate, and the inferiority of Rainbow (4.17 MPa). The cervical root third (7.81 MPa) was superior, the apical third was inferior (5.80 MPa), and the middle third (6.88 MPa) was an intermediate without differing from the others. Conclusion The customization of glass fiber posts increases the bond strength to the root dentin, regardless of the resin used. There was a compromise in the apical third and when using light-curing devices with lower light intensity.

Current perspectives on dental adhesion: (3) Adhesion to intraradicular dentin: Concepts and applications

Adhesion science is one of the greatest contributions to restorative dentistry. Adhesion not only established the current principles of tissue preservation, but also allowed for the production of more hermetic and long-lasting restorations. Although adhesive strategies are routinely used in most clinical situations, adhesion to root dentin is still a major challenge. The presence of humidity together with less intertubular dentin are factors that limit the adhesive potential of root dentin. This situation is more unfavorable in endodontically treated teeth prepared for prefabricated or custom-made intraradicular posts; these procedures may alter the mechanical properties of teeth by modifying the viable dentin surface for adhesion. Also, contaminants deposited on the dentin surface are difficult to remove through conventional techniques. Moreover, root canal morphology has a very unfavorable C-factor, bringing undesirable effects resulting from polymerization contraction of resin-based materials. However, the differences between coronal and root dentin are not a barrier for dentin adhesion. Standardization of procedures and care during clinical steps are fundamental to the success of adhesion to coronal or intraradicular dentin. Thus, it is essential to know the anatomy of the root structure, the factors that interfere with intraradicular adhesion, as well as the current adhesive materials and techniques.

Effect of laser irradiation on push-out bond strength of dental fiber posts to composite resin core buildups: A systematic review and meta-analysis

BACKGROUND

The bonding of fiber posts (FPs) to composite resin core buildups is a challenge due to limited penetration of resin to the polymeric matrix of FPs. This review article tries to answer this question: "What are the effects of laser surface treatment of FPs, compared to other surface roughening methods, on push-out bond strength (PBS) of FPs bonded to composite resin core buildups?"

METHODS

Searches were run in seven electronic databases with a focus on proper key words. Related titles and abstracts, up to February 2019, were screened, selected, read and subjected to quality assessments.

RESULTS

After the initial search, a total of 2635 articles were included in the study. Finally, 6 studies were reliable enough in methodology to be included. All the studies were in vitro with a total of 359 samples. Er:YAG (-0.05, 95% CI: -2.96 to 2.86; P = 0.97) and Er,Cr:YSGG (0.84, 95% CI: -0.12 to 1.81; P = 0.08) treated samples showed no significant overall mean differences in final PBS compared to the control groups. Moreover, pretreatment with Er,Cr:YSGG laser and sandblasting with 50 μm alumina showed an overall mean difference of -0.42 for PBS (95% CI: -1.23 to 0.39) with no significant differences.

CONCLUSIONS

Laser irradiation of FPs seems to provide no significant increase in PBS values of FPs bonded to composite resin core buildups. Effects of surface treatment of FPs with laser irradiation and sandblasting with 50 μm alumina might be similar in increasing the final PBS, either.

Application of a Novel Modification of the Microbond Test for Evaluation of Adhesive Bond Strength Between Fiber Posts and Dual-Cure Dental Resin Cement

BACKGROUND While several tests can be used in the laboratory evaluation of composite resin-based cement materials, the push-out test remains the most prevalent. Due to difficulties in sample preparation, as well as a highly complex procedure, we attempted to develop an alternative method for testing the bond strength of dental resin cement materials. MATERIAL AND METHODS Ninety-six experimental samples of 2 dual-cure resin cements and 1 fiber post system were prepared for the 2 testing procedures: the push-out test and the modified Microbond test. The degree of monomer conversion was measured by Fourier-transform infrared spectroscopy. RESULTS The push-out test results indicated that the bond strength of dual-cure resin cement differs depending on the tooth root region to which it is applied (p<0.05), In addition, our findings show that Variolink II exhibits a much lower bond strength relative to RelyX ARC. These findings were confirmed by the modified Microbond test results. The monomer conversion rate results indicate average conversion rates of 85.81% and 61.35% for RelyX ARC and Variolnik II, respectively. CONCLUSIONS Our study confirms the practical utility of the modified Microbond test in the assessment of bond strength of dental cement resin-based materials. The proposed test method is particularly useful given that, relative to the push-out test, it requires a much smaller number of preparation and execution steps, thus reducing the potential for introducing errors, while increasing the reliability of the obtained findings.

Irrigación del conducto radicular y tratamiento de superficie de pernos de fibra, previo a la cementación: revisión de tema

Introducción: el tratamiento endodóntico es muy solicitado para preservar las piezas dentales, así como la utilización de pernos de fibra cuando el remanente coronario no es el adecuado para recibir una prótesis coronaria, permitiendo de esta manera reconstruir el muñón dental para la posterior colocación de la restauración definitiva. Objetivo: identificar tanto el tratamiento de superficie de pernos de fibra como el irrigante radicular idóneos para conseguir una cementación adecuada; así como conocer cuál es el tratamiento de superficie que produce menos desintegración de las fibras del perno de fibra. Materiales y métodos: se incluyeron 47 artículos publicados en inglés, durante los últimos 20 años, teniendo en cuenta que los mismos se obtuvieron hasta octubre del 2018. Conclusiones: previa la cementación de pernos sean estos de fibra o de cuarzo es indispensable realizar tratamiento de superficie para así mejorar la adhesión, estos pueden ser químicos o físicos, los que ofrecen mejor resultado sin alterar de manera significativa la estructura del mismo es el enarenado con partículas de diamante sintéticas de 1-3 µm seguido de silanización y dentro de los químicos H2O2 al 10% por 1 min seguido de silano. Para obtener mejores resultados se debe accionar el silano a una temperatura de 80°C. En cuanto a protocolos de irrigación depende del sistema de cementación que se vaya a emplear EDTA 18% + Hipoclorito de sodio al 5,25% o EDTA 18% + clorhexidina al 2% cuando se va emplear un cemento autoadhesivoy NaOCl al 11% cuando se utilice el acondicionamiento ácido de lavado y secado.

Effect of 830 nm Diode Laser Irradiation of Root Canal on Bond Strength of Metal and Fiber Post

OBJECTIVE AND BACKGROUND

The correct selections of the cementing agent, the endodontic post material and placement protocol are critical to provide an increased longevity of the teeth that went through endodontic treatment. The irradiation with diode laser before post cementation, can promote an antimicrobial effect. However, there is a lack of information about the effect of 830 nm diode laser on the post bond strength. This study analyzed the effect of dentin root canal irradiation with high-intensity diode laser, at 830 nm, operating in continuous or pulsed mode, on the retention of metal or fiber posts, cemented with self-etching resinous composite (Panavia F) and zinc phosphate cement (ZnPO₄).

MATERIALS AND METHODS

Human roots were irradiated with diode laser (continuous and pulsed mode). The fiber posts were luted with Panavia F and the metal posts with Panavia F or ZnPO₄ cement. Specimens were sectioned into three sections (cervical, middle, and apical). The bond strength was measured by a push-out mechanical analysis. For the statistical analysis, a three-way ANOVA test was applied following a Tukey's pairwise comparison with a significance level of p = 0.05.

RESULTS

The irradiated groups presented higher bond strength compared with nonirradiated group (p < 0.05), and the cervical and middle thirds presented higher on bond strength than the apical. The association of metal post and Panavia F presented higher bond strength when irradiated on continuous mode (p < 0.05). Fiber post and Panavia F presented higher bond strength associated to pulsed mode. The mode seems not to make a significant difference.

CONCLUSIONS

These results corroborate the importance of the post bond to dentin and root canal debris removal to increase the tooth longevity. It was shown that the dentin to post bond strength were enhanced by the diode laser irradiation either on continuous or pulsed modes.

Bond strength of fiber posts to the root canal: Effects of anatomic root levels and resin cements

STATEMENT OF PROBLEM

Decementation is one of the most frequent causes of failure in the post-cement system. The bond strength in different parts of the canal may be influenced by technical and anatomic factors.

PURPOSE

The purpose of this in vitro study was to assess the effects of anatomic root levels to reach the canal and different resin cements on the bond strength of fiberglass posts along the canal.

MATERIAL AND METHODS

One hundred thirty-five roots of bovine teeth were endodontically treated, prepared with 15-mm-long post spaces and divided according to the anatomic root level: coronal (with 15-mm post space), middle (with 10-mm post space), and apical (with 5-mm post space). Fiberglass posts were luted with the cements (n=15): conventional resin cement with 3-step etch-and-rinse adhesive system (RelyX ARC/SBMP); self-adhesive resin cement (RelyX U200) and autopolymerizing resin cement with etch-and-rinse adhesive system (C&B/All-Bond 2). After 24 hours, specimens were sectioned and subjected to the push-out test. The maximum extrusion load was recorded (0.5 mm/minute, 200 N). Data were analyzed with analysis of variance (ANOVA) and the Tukey test (α=.05). Failure mode was analyzed by using multinomial logistic regression.

RESULTS

There were no significant effects of resin cements (P>.05). The bond strength at apical third was higher when the canal was reached at the apical level than at the coronal level (P=.022). When each root level was directly reached, the coronal bond strength was lower than apical (P=.001) and middle (P=.021) for all cements.

CONCLUSIONS

When the canal was reached at the coronal, medium, and apical levels, the bond strength of conventional, self-adhesive and autopolymerizing resin cements was lower in the coronal root third.

Evaluation of the Bond Strength and Fracture Resistance of Different Post Systems

AIM

To compare the bond strength and the fracture resistance of different post systems.

MATERIALS AND METHODS

Endodontically treated 60 mandibular incisor and 60 mandibular premolar teeth were used for the bond strength and fracture resistance test respectively. For each test, three groups (n = 20) were formed according to the posts used zirconia posts (ZR post), individually formed glass fiber reinforced composite posts with an (Interpenetrating Polymer Network-IPN post) and cast metal posts. Then groups were randomly assigned into two subgroups according to the post design: 1-parallel sided and 2-tapered (n = 10/group). All posts were luted with a self-adhesive luting agent. For push-out test two 1 mm thick horizontal root sections were obtained and subjected to push-out test. For fracture resistance test, the specimens were loaded vertically at 1 mm/min crosshead speed. The push out test data were analyzed with Kruskal-Wallis and Dunn's test. Analysis of variance (ANOVA) and Tukey significant difference tests were used to compare the fracture resistance.

RESULTS

Cast metal posts showed the highest retention (p < 0.05); however, IPN and zirconia posts showed similar results. No significant difference was found between parallel sided or tapered designs of post groups in terms of bond strength (p > 0.05). In terms of fracture resistance, IPN post groups showed lowest fracture resistance (p < 0.05). No significant difference was found between parallel sided or tapered posts in terms of fracture resistance, except zirconia post (p > 0.05). There was no relationship between the bond strength and fracture resistance of the post systems (r = - 0.015, p > 0.700).

CONCLUSION

Post type had effect both on the fracture resistance and retention of the posts used. However, post design had effect only on the fracture resistance of the post systems.

CLINICAL SIGNIFICANCE

Superficial treatment of the post used can improve the retention of post systems.

Effects of heat treating silane and different etching techniques on glass fiber post push-out bond strength

The aims of this study were to compare two pretreatment methods of a fiber post and to evaluate the effect of heat treatment to applied silane on the push-out bond strength for different levels of root. In this in vitro study, 40 glass fiber posts were divided into five groups (n=8) according to the kind of surface treatment applied. They were then inserted into extracted and endodontically treated human canines using a self-etch resin cement (Panavia F2.0, Kuraray, Japan). Group HF+S = hydrofluoric acid (HF) etching and silane (S) application; group HF+S+WP = HF etching and heat-treated silane application and warmed posts (WP); group H2O2+S = hydrogen peroxide etching and silane application; group H2O2+S+WP = hydrogen peroxide and heat-treated-silane application and warmed post; and group C, the control group, received no pretreatment. After completion of thermal cycling (1000 cycles, 5-55°C), all specimens were cut horizontally to obtain three sections. Each section was subjected to a push-out test, and the test results were analyzed using two-way analysis of variance, post-hoc Tukey honestly significant difference test, and a paired sample t-test (α=0.05). It was found that bond strength was not statistically influenced by the kind of etching material used (p=0.224), but was significantly affected by heat treatment of applied silane (p<0.001). The interaction between these two factors was not statistically significant (p=0.142). Group HF+S+WP showed the highest bond strength (12.56±1.73 MPa) (p<0.05). Scanning electron microscopy revealed the effect of the different treatments on the surface characteristics of posts. In the four pretreated groups, the bond strength decreased significantly from the coronal to the apical root canal sections (p≤0.05). The results of this study show that the use of heat-treated silane significantly enhances the push-out bond strength of the fiber posts to root. HF acid etching with heat-treated silane application led to the highest bond strength.

WITHDRAWN: Effect of post space conditioning and luting resin on the retentive strength of fiber-reinforced composite resin posts

This article has been withdrawn at the request of the author(s) and/or editor. The Publisher apologizes for any inconvenience this may cause. The full Elsevier Policy on Article Withdrawal can be found at http://www.elsevier.com/locate/withdrawalpolicy.

The effect of light-curing access and different resin cements on apical bond strength of fiber posts

PURPOSE

This study evaluated the effect of light-curing access on the bond strength of fiber glass posts to the apical area of bovine roots using self-adhesive cement or dual-cured cement with an etch-and-rinse adhesive system.

MATERIALS AND METHODS

The root canals of 60 bovine teeth were endodontically treated and filled. A 15-mm-length post space was prepared and roots were randomly divided into three groups, simulating the levels of light-curing access: coronal (C), with 15-mm post space; middle (M), in which the coronal thirds of roots were cut out, leaving a 10-mm post space; and apical (A), in which the coronal and middle thirds of roots were cut out, leaving a 5-mm post space. Fiber glass posts (Reforpost # 3, Angelus) were cemented with RelyX U100 (3M ESPE) or RelyX ARC/Scotchbond Multi Purpose Plus (SBMP) (3M ESPE) (n=10) and light-cured. After 24 hours, the apical thirds of roots were sectioned perpendicularly to the long axis and submitted to a push-out test (0.5 mm/min, 200 N). The Kruskal-Wallis test compared the three levels of light-curing access, and the Mann-Whitney test compared the cements.

RESULTS

The bond strength was significantly higher in the groups C (p=0.028) and M (p=0.016) when U100 was used, whereas it was similar for both cements in group A. The bond strengths of posts cemented with ARC/SBMP were significantly higher in group A compared to group C (p=0.031).

CONCLUSIONS

The type of cement used and the light-curing access level influenced the bond strength between glass fiber posts and root canals. The bond strength of the RelyX ARC/SBMP cement proved to be more dependent on photoactivation than was the RelyX U100 cement. The light-curing access level did not influence the apical bond strength of RelyX U100.

The effect of different adhesive system applications on push-out bond strengths of glass fiber posts

PURPOSE

Over the past years, the adhesion of fiber posts luted with simplified adhesive systems has been a matter of great interest. The aim of this study was to assess the post retentive potential of a self-adhesive resin cement using different adhesive systems to compare the push-out bond strengths of fiber posts.

MATERIALS AND METHODS

The post spaces of 56 mandibular premolar roots were prepared and divided into 4 experimental groups and further divided into 2 subgroups according to testing time (n=7). The fiber posts (Rely X Fiber Post) were luted with a self-adhesive resin cement (RelyX Unicem) and one of the following adhesive systems: no adhesive, a total-etch adhesive resin (Single Bond), a two-step self-etch adhesive resin (Clearfil SE Bond) and a one-step self-etch adhesive resin (Clearfil S3 Bond). Each root was cut horizontally, and 1.5 mm thick six root segments were prepared. Push-out tests were performed after one week or three months (0.5 mm/min). Statistical analysis were performed with three-way ANOVA (α=.05).

RESULTS

Cervical root segments showed higher bond strength values than middle segments. Adhesive application increased the bond strength. For one week group, the total-etch adhesive resin Single Bond showed higher bond strength than the self-adhesive resin cement RelyX Unicem applied without adhesive resin at middle region. For 3 months group, the two-step self-etch adhesive resin Clearfil SE Bond showed the highest bond strength for both regions. Regarding the time considered, Clearfil SE Bond 3 months group showed higher bond strength values than one week group.

CONCLUSION

Using the adhesive resins in combination with the self-adhesive resin cement improves the bond strengths. The bond strength values of two-step self-etch adhesive resin Clearfil SE Bond improved as time passes.

Effect of 2% chlorhexidine digluconate on bond strength of a glass-fibre post to root dentine

AIM

To assess the immediate influence of dentine bonding systems (DBS) associated with 2% chlorhexidine digluconate (CHX) on glass-fibre post-bond strength to root dentine, in terms of coronal, middle and apical thirds.

METHODOLOGY

Sixty bovine roots were root filled and randomly assigned to 1 of 6 groups (n = 10): SBMP (3-step etch-and-rinse system, Scotchbond Multi-Purpose), SB (2-step etch-and-rinse system, Single Bond 2), SE (2-step self-etching system, Clearfil SE Bond) and SBMP-CHX, SB-CHX and SE-CHX, respectively, associated with CHX. For all groups, a glass-fibre post was luted with a dual-cure resin cement, RelyX ARC. After 7-day storage, specimens were subjected to the push-out test. Failure modes were analysed under optical microscopy (40x). Bond strength values were statistically analysed by two-way anova and Bonferroni tests (P < 0.05).

RESULTS

The effect of DBS was significant (P < 0.05), and SE reached higher bond strength in comparison with the other DBS tested. CHX association did not show improvement with any DBS (P > 0.05); rather, it negatively affected SE, which was detected for all thirds. There was no difference between thirds (P > 0.05), except for the SE-CHX, which presented lower values for the apical third (P < 0.05). Adhesive cement/dentine adhesive failure was predominant for all groups. CHX did not influence the failure mode for any DBS (P > 0.05).

CONCLUSIONS

The performance of the dentine bonding systems was material dependent. CHX did not improve immediate bond strength; however, CHX negatively affected the bond strength of the self-etching system, especially in the third apical.

Are implants more reliable than severely compromised endodontically treated teeth as abutments for zirconia-based FPDs? : In vitro results of long-term preclinical load simulation

OBJECTIVES

The aim was to study the impact of the defect size of endodontically treated incisors compared to dental implants as abutments on the survival of zirconia two-unit anterior cantilever-fixed partial dentures (2U-FPDs) during 10-year simulation.

MATERIALS AND METHODS

Human maxillary central incisors were endodontically treated and divided into three groups (n = 24): I, access cavities rebuilt with composite core; II, teeth decoronated and restored with composite; and III as II supported by fiber posts. In group IV, implants with individual zirconia abutments were used. Specimens were restored with zirconia 2U-FPDs and exposed to two sequences of thermal cycling and mechanical loading.

STATISTICS

Kaplan-Meier; log-rank tests.

RESULTS

During TCML in group I two tooth fractures and two debondings with chipping were found. Solely chippings occurred in groups II (2×), IV (2×), and III (1×). No significant different survival was found for the different abutments (p = 0.085) or FPDs (p = 0.526). Load capability differed significantly between groups I (176 N) and III (670 N), and III and IV (324 N) (p < 0.024).

CONCLUSION

Within the limitations of an in vitro study, it can be concluded that zirconia-framework 2U-FPDs on decoronated teeth with/without post showed comparable in vitro reliability as restorations on implants. The results indicated that restorations on teeth with only access cavity perform worse in survival and linear loading.

CLINICAL RELEVANCE

Even severe defects do not justify per se a replacement of this particular tooth by a dental implant from load capability point of view.

An ex vivo comparative study on the retention of custom and prefabricated posts

Aim:

This study was designed to comparatively evaluate the effect of cyclic loading on the retention of custom-fabricated fiber-reinforced composite (CF-FRC), prefabricated metal, and glass fiber posts.

Materials and Methods:

Thirty mandibular first premolars decoronated at the CE junction were divided into three groups (n=10). Groups A, B, and C were restored using Para Post (Whale dent), Reforpost (Angelus), and CF-FRC post (Ribbond-THM), respectively. Five specimens from each group were subjected to cyclic loading. Tensile bond strength (TBS) was evaluated.

Results:

Pre-loading TBS values were statistically, significantly higher for all posts (P<0.05). Before and after loading, there was a significant difference between group C as compared to groups A and B.

Conclusions:

Cyclic loading reduced the retention of all posts but was comparatively lesser for the CF-FRC post. This system provides sufficient retention required for clinical success.

Evaluation of push-out bond strength of two endodontic post systems

INTRODUCTION

The aim of this study was to evaluate the push-out bond strengths of a new polyfiber post system and a fiber post that were adhesively luted with a dual-cure resin cement.

METHODS

Forty single-rooted human maxillary teeth were sectioned below the cementoenamel junction, and the roots were endodontically treated. The roots were randomly divided into 2 groups of 20 specimens each according to the post type used: SpiraPost (group A; DMG, Englewood, NJ) and DT Light-Post Illusion X-RO (group B; Bisco Inc, Schaumburg, IL). All posts were cemented with dual-cure resin cement. Bonded specimens were cut into 1-mm-thick sections, and push-out tests were performed using a universal testing machine. All specimens were loaded until fracture, and the failure modes were evaluated with a stereomicroscope at 50× magnification. Representative specimens were analyzed by scanning electron microscopy.

RESULTS

Push-out bond strength was significantly affected by the type of post (P < .05). In all root sections, the SpiraPost push-out bond strength values were significantly higher than that those of DT Light-Post Illusion X-RO (P < .05). Cohesive failure within the post was the most frequent type of failure for the SpiraPost system.

CONCLUSIONS

In all root segments, the SpiraPost system provided significantly increased post retention compared with the fiber post.

Durability of the bond between resin composite cores and prefabricated posts

OBJECTIVES

This study evaluated the effect of post surface treatment and of storage condition on the bond between resin composite cores (Clearfil Core) and posts of titanium alloy (Fysika), silica-zircon fiber reinforced epoxy resin (SiliciumPost), and zirconia (CosmoPost).

MATERIAL AND METHODS

In the experimental groups, the coronal part of each post received sandblasting or tribochemical silicate-coating (CoJet) treatment. The coronal part of each post was embedded in a cylinder of resin composite core material with the aid of a fixation apparatus. After 15 min, the specimen was freed from the mold and stored in de-ionized water. The axial tensile strength (ATS) of posts was determined in a Universal Testing Machine when extracting the posts from the resin composite cores after: 1) 14 d water storage at 37°C, 2) 14 d water storage at 37°C followed by thermal cycling (6,000 cycles between 5°C and 55°C), or 3) 1 year water storage at 37°C. The results were statistically analyzed by three-way factorial ANOVA and Newman-Keuls' multiple range test.

RESULTS

The ATS values were generally higher for Fysika posts and SiliciumPost posts than for CosmoPost posts. Surface treatment effectively improved the ATS values of Fysika posts and SiliciumPost posts, but not those of CosmoPost posts. Thermal cycling or long-term water storage had only minimal effect on the ATS values of the posts.

CONCLUSION

Bonding of resin composite cores to the posts depended more on the material of the post and the surface treatment of posts than on the storage condition.