Preservation in the liquid media produces alterations in enamel surface properties

Dosimetric parameters and radiotherapy simulation methods used in preclinical studies of radiation damage to the dentition: a systematic review

OBJECTIVE

This systematic review investigated the dosimetric parameters used in preclinical studies.

STUDY DESIGN

Searches were performed in 3 databases (PubMed, Scopus, and Embase) and gray literature to identify studies for review. In vitro and ex vivo studies that examined the effect of radiation on human permanent teeth were included. The modified Consolidated Standards Of Reporting Trials checklist of items for reporting preclinical in vitro studies was used to assess the risk of bias.

RESULTS

In total, 32 studies met the inclusion criteria. The average radiation dose of in vitro studies was 53 (±22) Gy and in ex vivo studies was 69 (±1) Gy. Twenty-two studies used 5 different fractionation schemes. Twenty-two of the included studies did not report the radiotherapy modality of those reporting. Twenty studies used linear accelerators, and 7 used Cobalt-60 with the source-surface-distance of radiation ranging from 1.5 to 100 cm. Distilled water was the storage solution for the dental structure used most commonly. Biases were observed, including small sample sizes, lack of randomization, and blinding processes.

CONCLUSION

The dosimetric parameters used in the preclinical studies, including radiation dose, radiotherapy modality, fractionation regime, and the storage solutions used did not support the hypothesis of direct effects of radiation on the dental structure.

Correlation between dental enamel chemical composition and bracket debonding, comparing adhesive systems through a scanning electron microscope

Literature reports indicate that during bracket removal there can be enamel damage. We compare the shear bond strength (SBS) and tooth enamel loss of four adhesive systems and identify the Ca/P ratio. Then a total of 20 premolars were divided into four groups of five each. After prophylaxis, photographs were taken at 35× with a scanning electron microscope (SEM) and analyzed with X-ray spectroscopy (EDS) at 250×. Brackets were bonded with Transbond™ MIP(G1), Transbond™ PLUS SEP(G2), Enlight(G3) and Stylus®(G4) adhesives, 24 h after were debonded with a Instron universal testing machine at 1 mm/min. All the brackets were photographed with the SEM. The amount of lost enamel was measured with AutoCad. All the results were measured with a significance level p < .05. The SBS general average at debonding was 7.94 ± 2.26 MPa, meanwhile the SBS for G1, G2, G3 and G4 was 9.38 ± 1.46, 6.28 ± 0.69, 9.08 ± 2.45 and 7.04 ± 2.64 MPa respectively. 90% of the samples had no enamel loss, 10% had enamel loss. Only two samples in G1 presented an enamel loss area of 0.34mm² and 0.80mm² respectively. From EDS analysis, the Ca/P ratio was 1.6 ± 0.05, 1.61 ± 0.03, 1.64 ± 0.83 and 1.59 ± 0.07 for G1, G2, G3 and G4 respectively; no statistically significant differences were found. We conclude that no association was found between the Ca/P ratio and enamel damage when brackets are removed.

Effect of different doses of radiation on morphogical, mechanical and chemical properties of primary and permanent teeth-an in vitro study

Background

Radiotherapy, applied to the head and neck region, can cause radiation side effects such as reduction of saliva and radiation caries. The aim of this study was to perform an in vitro assessment of the effects of radiation therapy on the morphological, mechanical, and chemical properties of primary and permanent teeth.

Methods

One hundred four extracted human teeth (52 impacted wisdom teeth, 52 primary molar teeth) were used. The teeth were divided into two parts in the mesiodistal direction. Of the 98 teeth, the vestibular sections were used for the vickers analysis and lingual sections were used for the Inductively Coupled Plasma-Optical Emission Spectrometry (ICP-OES) analysis. The teeth in the experimental group were fixed to wax models. Each model had an equal number of teeth (n = 7). The doses were applied to the teeth for 6 weeks; 5 week days and 2Gy daily. After the radiotherapy was conducted weekly, a wax model was taken from radiation reception. Along with the elemental contents (Na, K, Mg, P, and Ca) of the teeth, enamel and dentin microhardness was evaluated, and SEM analyzes were performed on 6 teeth.

Results

Radiation caused a decrease in microhardness of enamel and dentin (p < 0.05). In the elemental analysis by ICP-OES, it was observed that there were decreases in all elements after 60Gy compared to the control group (p < 0.05). In the experimental groups, amorphous structures were encountered in SEM images.

Conclusions

Radiation has negative effects on the teeth structure and additional studies are needed in this regard. This study indicates that radiotherapy patients are at a higher risk for dental caries.

Effect of Storage Medium and Aging Duration on Mechanical Properties of Self-Adhesive Resin-Based Cements

Background

The aim of this study was to investigate the effects of storage medium and aging duration on Martens hardness (HM) and indentation modulus (EIT) of self-adhesive resin-based cements (SARCs).

Methods

A total of 416 discs were fabricated from 8 SARCs (n = 52 per SARC): (i) BeautyCem (BEA), (ii) Bifix SE (BIF), (iii) Clearfil SA Cement Automix (CLE), (iv) RelyX Unicem2 Automix (RXU), (v) SeT (SET), (vi) SmartCem 2 (SMC), (vii) SoloCem (SOC) and (viii) SpeedCEM (SPC). The specimens were ground and stored in (a) physiological saliva, (b) artificial saliva, (c) sodium chloride and (d) distilled water, at 37°C for 1, 7, 14, 28, 90 and 180 days. Non-aged specimens (3 hours after photo-initiation) of each SARC acted as control groups. HM and EIT were assessed using a universal hardness testing machine. Data were analyzed using Kolmogorov-Smirnov and Kruskal-Wallis tests and paired t-test, and 3-, 2- and 1-way ANOVA with post hoc Scheffé test (p<0.05).

Results

SARC materials exerted the highest influence on HM and EIT values (p<0.001, partial eta squared [ηP²] = 0.753 and 0.433, respectively), closely followed by aging duration (p<0.001, ηP² = 0.516 and 0.255) and storage medium (p<0.001, ηP² = 0.043 and 0.033). The interaction effect of the combinations of the 3 independent parameters was also significant (p<0.001, ηP² = 0.163 and 0.133). The lowest initial HM and EIT was presented by CLE, followed by SET and SPC; highest HM was for BIF, followed by RXU and SMC. SET gave a greater HM and EIT percentage decrease than SOC, SPC, BEA, SMC, RXU or CLE.

Conclusions

Aging duration is a major factor affecting the micromechanical properties of SARCs, while storage medium was shown to have a significant but minor role.

Radiotherapy effect on nano-mechanical properties and chemical composition of enamel and dentine

OBJECTIVE

To understand radiotherapy-induced dental lesions characterized by enamel loss or delamination near the dentine-enamel junction (DEJ), this study evaluated enamel and dentine nano-mechanical properties and chemical composition before and after simulated oral cancer radiotherapy.

DESIGN

Sections from seven non-carious third molars were exposed to 2 Gy fractions, 5 days/week for 7 weeks for a total of 70 Gy. Nanoindentation was used to evaluate Young's modulus, while Raman microspectroscopy was used to measure protein/mineral ratios, carbonate/phosphate ratios, and phosphate peak width. All measures were completed prior to and following radiation at the same four buccal and lingual sites 500 and 30 μm from the DEJ in enamel and dentine (E-500, E-30, D-30 and D-500).

RESULTS

The elastic modulus of enamel and dentine was significantly increased (P ≤ 0.05) following radiation. Based on Raman spectroscopic analysis, there was a significant decrease in the protein to mineral ratio (2931/430 cm(-1)) following radiation at all sites tested except at D-500, while the carbonate to phosphate ratio (1070/960 cm(-1)) increased at E-30 and decreased at D-500. Finally, phosphate peak width as measured by FWHM at 960 cm(-1) significantly decreased at both D-30 and D-500 following radiation.

CONCLUSIONS

Simulated radiotherapy produced an increase in the stiffness of enamel and dentine near the DEJ. Increased stiffness is speculated to be the result of the radiation-induced decrease in the protein content, with the percent reduction much greater in the enamel sites. Such changes in mechanical properties and chemical composition could potentially contribute to DEJ biomechanical failure leading to enamel delamination that occurs post-radiotherapy. However, other analyses are required for a better understanding of radiotherapy-induced effects on tooth structure to improve preventive and restorative treatments for oral cancer patients.

Effect of 10% sodium ascorbate on bleached bovine enamel surface morphology and microhardness

Sodium ascorbate has recently been suggested to compensate decreased bond strength of composite resin to bleached tooth surfaces. The aim of present study was to evaluate the effect of 10% sodium ascorbate on bleached bovine enamel morphology and microhardness considering the possibility of its effect on enamel surface characteristics. A total of 69 bovine enamel slabs were prepared and mounted in acrylic resin. Subsequent to polishing, they were randomly divided into 3 groups of 23 specimens each; 3 for Scanning Electron Microscopy (SEM) analysis and 20 for hardness test. In group 1 the specimens were immersed in distilled water as control group; in group 2 the specimens were bleached with 35% carbamide peroxide for 30 min a week for 3 consecutive weeks; and in group 3 the specimens were exposed to 10% sodium ascorbate for 30 min subsequent to bleaching similar to group 1. After 3 weeks Vickers hardness of the specimens was measured at 3 points with equal distances from each other under a force of 50 g. The mean of the hardness values of each specimen was calculated and data was analyzed by one-way ANOVA (P < 0.05). The highest and lowest microhardness values were observed in group 1 and group 2, respectively. However, there were no statistically significant differences in microhardness between the groups (P = 0.12). The use of 35% carbamide peroxide alone or with 10% sodium ascorbate does not affect bovine enamel hardness. SEM analysis showed a network of sodium ascorbate adsorbed to the bleached enamel surface.