Effect of water storage on the translucency of silorane-based and dimethacrylate-based composite resins with fibres

Effects of number of firings and veneer thickness on the color and translucency of 2 different zirconia-based ceramic systems

STATEMENT OF PROBLEM

Color matching between a zirconia-based ceramic restoration and a natural tooth is a common clinical challenge.

PURPOSE

The purpose of this in vitro study was to investigate the effects of the number of firings, veneer thickness, and zirconia core translucency on the final color and translucency of zirconia-based ceramic restorations.

MATERIAL AND METHODS

Sixty disk-shaped zirconia specimens (10×1 mm) were prepared in high and low translucencies (n=30 per translucency group). Each zirconia group was subdivided into 3 subgroups (n=10) veneered with ceramic layers of 0.5-, 1-, and 1.5-mm thicknesses. The specimens were then subjected to 1, 3, 5, and 7 firing times. Color and translucency parameters were measured by using a spectrophotometer. Data were analyzed by using multifactorial repeated measures ANOVA and subgroup analysis (α=.05).

RESULTS

The number of firings affected the L*, a*, and b* values and translucency parameter in both zirconia-based systems with different veneer thicknesses (P<.05). Increasing the veneer thickness decreased the translucency parameter and increased the L*, a*, and b* values in both zirconia-based systems (P<.05). The color difference values (ΔE) were the highest between 1 and 3, 1 and 5, and 1 and 7 firings, and the lowest between 5 and 7 firings in both zirconia systems.

CONCLUSIONS

Repeated firings and porcelain veneer thickness affected the final color and translucency of both zirconia systems and, consequently, adversely influenced the esthetic outcomes. Thus, these factors should be considered in the tooth preparation and laboratory phase.

The effect of repetitive firings on the color of an alumina ceramic system with varying ceramic shade and thickness

OBJECTIVE

The color of all-ceramic restorations is one of the main criteria to achieve esthetical success. Many factors such as ceramic thickness, condensation techniques, firing temperature, and numbers can affect the final color of restoration. The purpose of this study was to investigate the color changes in alumina-based ceramic system according to ceramic shade and thickness during the multiple firings.

MATERIALS AND METHODS

Sixty disc-shaped specimens with two different veneering porcelain shades (A1 or A3), and with three different ceramic thicknesses (0.5, 1, or 1.5 mm), were fabricated from an alumina-based ceramic system. Multiple firings (3, 5, 7, or 9 firings) were performed, and color changes (ΔE₀₀ ) were determined using a spectrophotometer. Repeated-measures ANOVA were used to analyze the data. The Duncan test was used for multiple comparisons (α = .05).

RESULTS

The L*a*b* values of the specimens were affected by the number of firings (3, 5, 7, or 9), veneering ceramic shades (A1 or A3) and veneering ceramic thicknesses (0.5, 1, or 1.5 mm). Significant interactions were present between the number of firings, veneering ceramic shade, and veneering ceramic thickness for L* (p < .001), a* (p < .001), and b* (p < .001) values.

CONCLUSIONS

No statistically significant color change was observed between 3rd and 9th firings.

CLINICAL SIGNIFICANCE

Veneering ceramic shade, veneering ceramic thickness, and number of firings should be carefully considered to obtain an acceptable color match of the definitive restorations.

Use of dental adhesives as modeler liquid of resin composites

OBJECTIVES

Resin adhesives (RA) have been applied between resin composite (RC) increments, but there is no consensus on the impact of this technique on the properties of the final restoration. This study evaluated the effect of the presence of RA between RC layers on physical properties, translucency and long-term color stability of the restorative material.

METHODS

Scotchbond™ Multi-Purpose (bond, 3M ESPE) and Adper™ Single Bond 2 (3M ESPE) were used as RA, and Filtek™ Z350 (3M ESPE) as RC. Specimens containing RA were prepared by applying 3 layers of the adhesive between 4 increments of RC; adhesive-free specimens were also used (control). Tests of water sorption and solubility, mechanical performance (microtensile cohesive strength, flexural strength, and flexural modulus, after immediate and long-term water storage), and translucency and color stability (after immediate and 1, 7, 90, and 180 days of water or wine storage) were performed. Scanning electron microscopy (SEM) images were also taken from the fractured specimens (flexural strength test). Data were analyzed using ANOVA and Tukey test (p<0.05).

RESULTS

Scotchbond (SBMP) showed lower water sorption and solubility than the control (p<0.001), and an overall similar (p≥0.198, immediate tests) or higher (p≤0.019, long-term tests) mechanical performance. SBMP exhibited a rougher cross-sectional surface compared to the other groups. Translucency remained unaltered after 180 days of storage (p≥0.313), except for single bond that had increased translucency with wine storage (p<0.045). After 180 days, all groups changed color (p≤0.002), although more intensively when immersed in wine.

SIGNIFICANCE

The presence of RA within RC increments increased the physical stability of the material, being this effect more evident by using the hydrophobic unfilled adhesive resin (SBMP). This study is the first to show positive results from the use of resin adhesives as modeler liquid of resin composite, which is common in clinical practice.