Inhibitory effect of resin composite containing S-PRG filler on Streptococcus mutans glucose metabolism

Surface prereacted glass-ionomer particles incorporated into resin composites promote biocompatibility for restoration of subgingival dental defects

Subgingival dental defects are common in clinical practice among patients with deep dental caries and dental fractures. These defects commonly accompany lesions involving marginal alveolar bone loss and gingival recession, and their clinical management is challenging. Restoring gingival adhesion and activating the regeneration of periodontal tissue are important for a better prognosis in these cases. However, there is no effective resin material for complex restorations involving the destruction of subgingival tissue. To achieve greater biocompatibility, resins are generally modified with bioactive particles that can release specific components. Surface prereacted glass ionomer (S-PRG) is a novel glass particle characterized by a three-layered structure and the release of multiple ions with bioactive potential. Therefore, in this study, we incorporated S-PRG filler into resin-based composites to investigate their effectiveness in the restoration of subgingival defects. Resin composites containing 0, 10, 30, 50, or 70 wt% S-RPG filler were fabricated and formed into material discs, where a commercial resin composite served as the control group. The microstructure and elemental distribution were characterized by scanning electronic microscopy and energy-dispersive spectroscopy. The resin composites containing 50 or 70 wt% S-PRG fillers exhibited comprehensively better physicochemical properties, including flexural modulus, compressive strength, and water sorption. The ion release profile and environmental pH of the resins were measured with material extracts. Periodontal ligament stem cells were considered as seed cells that harbored great potential for periodontal regeneration. Cellular experiments suggested that S-PRG promotes cell proliferation and adhesion, induces cell migration, and stimulates vascularized osteogenesis. The feasibility of using S-PRG-containing resin composite to rectify subgingival dental defects was confirmed in vivo. After restoration with the S-PRG-filled resin material, intact epithelial tissue adhered to the resin surface with no visible inflammation. In conclusion, S-PRG-filled resin composites showed some biocompatibility as an alternative material for clinical applications.

Evaluation of mechanical properties and ion-releasing of 3D printing resins containing S-PRG filler: A preliminary study

This study aimed to evaluate ionic release, flexural strength and water absorption of UDMA resins containing 0-30 wt% surface pre-reacted glass-ionomer (S-PRG) filler fabricated by a DLP 3D printer. Release of Al, B, Na, Sr and F ions were measured by inductively coupled plasma (ICP) and an ion meter. Flexural strength test and water absorption measurements were performed according to the International Organization for Standardization (ISO) 4049 standard and ISO 1567 standard, respectively. Sr ions were released the most, followed by F, B, Na and Al ions. The highest flexural strength was recorded with the S-PRG filler amount 0 wt%, followed by the S-PRG filler amounts 30, 20 and 10 wt%. Water absorption after one week was below the 32 µg/mm3 mark specified by ISO 1567. The release of ions was confirmed using UDMA-based photopolymerized resin containing S-PRG filler. Furthermore, the results suggest that this resin could be used for provisional restoration.

Resin composite aggregated S-PRG particles are not superior to non-S-PRG under microcosm biofilm

This study assessed the effect of composite resins, aggregated or not with S-PRG particles, and the use of toothpaste in controlling demineralization and bacterial growth. Human molars were distributed into 3 groups: control (CT) - sound teeth, Beautifil Bulk Restorative System (aggregated with S-PRG) (BB), Filtek One Bulk Fill (without S-PRG) (FB). Teeth destined for groups BB and FB previously received Class I preparations (4 × 4 × 4 mm), followed by single-increment restorations. All teeth were sectioned mesiodistally, with all specimens subjected to cariogenic challenge for 5 days, including microcosm biofilm formation. Half of each tooth was exposed to toothpaste (CTF, BBF, FBF). The loss of microhardness was assessed considering the initial microhardness as 100% on enamel, dentin, and composite resin substrates. Colony Forming Units (CFU/mL) were counted in 3 media. Data analysis used one-way ANOVA, Tukey HSD test, and paired t-test (α = 0.05). Toothpaste significantly reduced CFU/mL for total bacteria and genus Streptococcus (p < 0.05), with no significant difference for Streptococcus mutans. Enamel microhardness was positively affected by toothpaste. Both restorative systems controlled enamel demineralization, with FB and FBF outperforming BB and BBF. There was minor degradation of both composite resins, between 10% and 22%. Toothpaste effectively reduced microorganisms, irrespective of the composite resin. Regarding demineralization control, both restorative systems, with and without S-PRG particles, were effective on enamel.

Impact of S-PRG/Giomer and Bulk-fill technologies on the hygroscopic profile of resin composites under erosive condition

OBJECTIVE

The emergence of new resin composites (RCs) incorporating bioactive ingredients and/or used as bulk-fill materials aims to enhance restorative potential beyond just the mechanical properties. However, this innovation may affect their performance under clinically simulated conditions, such as erosive challenges (EC). This study evaluated the impact of different technologies on the hygroscopic properties of RCs.

MATERIALS AND METHODS

The evaluated materials were: Gold Label - GL (resin-modified glass-ionomer cement - control); Filtek Z350 - FZ (no bioactive control); Filtek One Bulk - FO (bulk-fill); Beautifil II - BII (bioactive/S-PRG); Beautifil Bulk - BB (bioactive/S-PRG + bulk-fill). Disk-shaped specimens (10 mm x1 mm) were prepared and evaluated by: 1) water sorption - WS and solubility - WSB (n = 10); 2) wettability - W (n = 6); 3) surface microhardness - SM (n = 6); 4) qualitative surface analysis by SEM (n = 3). Except for WS and WSB, tests were performed before and after EC. Data were analyzed by two-factor ANOVA and Tukey tests (p < 0.05).

RESULTS

Positive WS and negative WSB were observed for all materials. In terms of W, GL>BII>FZ>BB>FO. GL and BB exhibited similar/lower SM. EC hampered SM for all materials.

CONCLUSIONS

It may be concluded that the composition and proportion of monomers have a greater influence on the hygroscopic profile of resin composites than the incorporation of bioactive components.

CLINICAL SIGNIFICANCE

While renewed technologies have introduced components to enhance the performance and practicality of resin composites, actual clinical longevity depends on challenges such as erosive conditions. Bioactive ingredients seem to be beneficial without impairing the hygroscopic profile, whereas the monomers can interfere.

Impact of functional monomers, bioactive particles, and HEMA, on the adhesive performance of self-etch adhesive systems applied to simulated altered dentin

OBJECTIVES

This study aimed to evaluate how self-etching/universal dental adhesive systems (DASs) with differing compositions interact with sound (S), post-radiotherapy (irradiated; I), and artificially eroded (E) dentin in terms of bonding properties.

METHODS

The DASs tested were Adper Scotchbond Multipurpose (MP; control), Clearfil SE Bond (SE), FL Bond II (FL), Adper Single Bond Universal (SU) and BeautiBond Xtreme (BX). They were analyzed for initial and 6-month microtensile bond strength (µTBS, n = 12), mode of failure (40 x), scanning electron microscopy (SEM), surface wettability (W, n = 10), and degree of conversion (DC, n = 3) via Fourier-transform infrared spectroscopy (FTIR). Normal and homogeneous distribution of the data allowed their analyses through ANOVA and Tukey tests (p < 0.05).

RESULTS

All DASs except BX exhibited higher µTBS for S decreasing for I and E. BX demonstrated the greatest stability among the altered substrates. FL showed the most hydrophobic properties, likely due to its bioactive components. Universal DASs achieved higher DC, regardless of composition.

CONCLUSIONS

HEMA-free formulation combined with carboxylic and phosphoric acids in BX, achieved the most stable performance for altered substrates.

CLINICAL SIGNIFICANCE

Since radiotherapy and erosion affect dentin, their characteristics compromise adhesive performance and impair the achievement of durable and satisfactory restorations. The use of universal adhesives less dependent on calcium seems less susceptible to hydrolytic degradation and may be a promising option for maintaining adhesive stability over time.

Bioactive Self-Polymerizing Resin with Surface Pre-Reacted Glass Ionomer Fillers for Suppressed Enamel Demineralization

The treatment of damaged enamel surfaces involves modification of the enamel surface with artificial materials or the development of a pseudo-enamel, with research focusing on bioactive and biomimetic materials. In this study, a bioactive auto-polymerizing resin (APR) was developed by adding surface-pre-reacted glass ionomer (S-PRG) fillers of different quantities to APR. Its bioactive effects were evaluated via pH neutralization, ion release, and inhibition of enamel demineralization studies. The pH and fluoride ion release were measured using ion-specific electrodes, revealing that the APR disk with the S-PRG filler immediately neutralized the lactic acid solution (pH 4.0) through ion release. Inductively coupled plasma atomic emission spectrometry revealed that the Sr ion release peaked on the first day, with the other ions following the order F > B > Si > Al > Na, exhibiting a weekly decrease in the same order. Scanning electron microscopy was used to examine the enamel block morphology of the disks after 7 d of incubation, revealing enamel demineralization in disks without the S-PRG filler, whereas no demineralization occurred in disks with the S-PRG filler. APR containing the S-PRG filler demonstrated acid buffering suppressed enamel demineralization and bioactive properties.

The formation of cariogenic plaque to contemporary adhesive restorative materials: an in vitro study

The research exploiting the ability of dental materials to induce or prevent secondary caries (SC) development still seems inconclusive. Controlling bacterial adhesion by releasing bacteriostatic ions and improving the surface structure has been suggested to reduce the occurrence of SC. This paper analyses the impact of five distinctively composed dental materials on cariogenic biofilm formation. Forty-five specimens of three composites (CeramX Spectra ST, Admira Fusion, Beautifil II) and two glass-ionomers (Fuji II LC, Caredyne Restore), respectively, were incubated in bacterial suspension composed of Streptococcus mutans, Lactobacillus acidophilus, Streptococcus mitis, Streptococcus sanguinis, and Streptococcus salivarius at pH 7.0 and 5.5. Coverslips were used as a control. Adhered bacteria were collected after 2, 4, 6, 12, 24, and 48 h and analyzed using quantitative polymerase chain reaction (qPCR). Fluoride leakage was measured at each collection. The specimens' surface topography was assessed using interferometry. In the present study, surface roughness seemed to have a partial role in bacterial adhesion and biofilm formation, together with chemical composition of the materials tested. Despite differences in fluoride leakage, biofilm accumulation was similar across materials, but the number of adhered bacteria differed significantly. A release of other ions may also affect adhesion. These variations suggest that certain materials may be more prone to initiating secondary caries.

Antimicrobial effects of surface pre-reacted glass-ionomer (S-PRG) eluate against oral microcosm biofilm

This study investigated the antimicrobial activity of surface pre-reacted glass ionomer eluate (S-PRG) against oral microcosm biofilms collected from the oral cavity of patients. Dental biofilm samples were collected from three volunteers to form microcosm biofilms in vitro. Initially, screening tests were carried out to determine the biofilm treatment conditions with S-PRG eluate. The effects of a daily treatment for 5 min using three microcosm biofilms from different patients was then evaluated. For this, biofilms were formed on tooth enamel specimens for 120 h. Biofilms treated with 100% S-PRG for 5 min per day for 5 days showed a reduction in the number of total microorganisms, streptococci and mutans streptococci. SEM images confirmed a reduction in the biofilm after treatment. Furthermore, S-PRG also reduced lactic acid production. It was concluded that S-PRG eluate reduced the microbial load and lactic acid production in oral microcosm biofilms, reinforcing its promising use as a mouthwash agent.

Analysis of color stability and degree of conversion of different types of resin composites

Resin composites containing surface pre-reacted glass (S-PRG) have been introduced to reduce demineralization and improve remineralization of the tooth structure. However, water diffusion within the material is necessary for its action, which can impair its overall physicomechanical properties over time, including color stability. This study aimed to evaluate the color stability and related degree of conversion (DC) of four resin composites. Discs (6 x 4 mm, n = 5/group) of microhybrid (MH), nanofilled (NF), nanohybrid (NH), and S-PRG-based nanohybrid (S-PRG-NH) composites with two opacities (A2/A2E and A2O/A2D) were prepared. Color (CIELab and CIEDE2000) was evaluated with a spectrophotometer after aging in grape juice (2 x 10 min/10mL/7days). The DC was analyzed by using Fourier transform infrared spectroscopy before and after light-curing. Data were statistically analyzed by using two-way analysis of variance and post-hoc least significant difference tests (p<0.05). In the color stability analysis, the interaction between filler type and opacity was significant (CIELab, p = 0.0015; CIEDE2000, p = 0.0026). NH presented the highest color stability, which did not differ from that of MH. The greatest color alteration was observed for S-PRG-NH. S-PRG fillers also influenced DC (p < 0.05). The nanohybrid resin composite presented favorable overall performance, which is likely related to its more stable organic content. Notwithstanding the benefits of using S-PRG-based nanohybrid resins, mostly in aesthetic procedures, professionals should consider the susceptibility of such resins to color alteration, probably due to the water-based bioactive mechanism of action.

In vitro analysis of durability of S-PRG filler-containing composite crowns for primary molar restoration

OBJECTIVE

To evaluate the reliability, maximum principal stress, shear stress, and crack initiation of a computer-aided design/computer-aided manufacturing (CAD/CAM) resin composite (RC) incorporating surface pre-reacted glass (S-PRG) filler for primary molar teeth.

METHODS

Mandibular primary molar crowns fabricated by experimental (EB) or commercially available CAD/CAM RCs (HC) were prepared and cemented to a resinous abutment tooth using an adhesive resin cement (Cem) or a conventional glass-ionomer cement (CX). These specimens were subjected to a single compressive test (n = 5/each) and the step-stress accelerated life testing (SSALT) (n = 12/each). Data was evaluated using Weibull analyses and reliability was calculated. Afterwards, the maximum principal stress and crack initiation point of each crown was analyzed by finite element analysis. To evaluate bonding of EB and HC to dentin, microtensile bond strength (μTBS) testing was conducted using primary molar teeth (n = 10/each).

RESULTS

There was no significant difference between the fracture loads of EB and HC for either cement (p > 0.05). The fracture loads of EB-CX and HC-CX were significantly lower than EB-Cem and HC-Cem (p < 0.05). The reliability at 600 N for EB-Cem was greater than that for EB-CX, HC-Cem, and HC-CX. The maximum principal stress concentrated on EB was lower than that on HC. The shear stress concentrated in the cement layer for EB-CX was higher than that for HC-CX. There was no significant difference among the μTBSs of EB-Cem, EB-CX, HC-Cem, and HC-CX (p > 0.05).

SIGNIFICANCE

The crowns fabricated with the experimental CAD/CAM RC incorporating S-PRG filler yielded greater fracture loads and reliability than the crowns manufactured with commercially available CAD/CAM RC regardless of the luting materials. These findings suggest that the experimental CAD/CAM RC crown may be clinically useful for the restoration of primary molars.

Antibacterial Activity of a Bioactive Tooth-Coating Material Containing Surface Pre-Reacted Glass in a Complex Multispecies Subgingival Biofilm

Bioactive materials were developed with the ability to release fluoride and provide some antimicrobial potential, to be widely used in dentistry today. However, few scientific studies have evaluated the antimicrobial activity of bioactive surface pre-reacted glass (S-PRG) coatings (PRG Barrier Coat, Shofu, Kyoto, Japan) on periodontopathogenic biofilms. This study evaluated the antibacterial activity of S-PRG fillers on the microbial profile of multispecies subgingival biofilms. A Calgary Biofilm Device (CBD) was used to grow a 33-species biofilm related to periodontitis for 7 days. The S-PRG coating was applied on CBD pins from the test group and photo-activated (PRG Barrier Coat, Shofu), while the control group received no coating. Seven days after treatment, the total bacterial counts, metabolic activity, and microbial profile of the biofilms were observed using a colorimetric assay and DNA-DNA hybridization. Statistical analyses were applied; namely, the Mann-Whitney, Kruskal-Wallis, and Dunn's post hoc tests. The bacterial activity of the test group was reduced by 25.7% compared with that of the control group. A statistically significant reduction was observed for the counts of 15 species: A. naeslundii, A. odontolyticus, V. parvula, C. ochracea, C. sputigena, E. corrodens, C. gracilis, F. nucleatum polymorphum, F. nucleatum vincentii, F. periodonticum, P. intermedia, P. gingivalis, G. morbillorum, S. anginosus, and S. noxia (p ≤ 0.05). The bioactive coating containing S-PRG modified the composition of the subgingival biofilm in vitro, thereby decreasing colonization by pathogens.

Multiple-Ion Releasing Bioactive Surface Pre-Reacted Glass-Ionomer (S-PRG) Filler: Innovative Technology for Dental Treatment and Care

Surface Pre-Reacted Glass-ionomer (S-PRG) filler, which releases strontium (Sr²⁺), borate (BO₃^3-), fluoride (F^-), sodium (Na⁺), silicate (SiO₃^2-), and aluminum (Al³⁺) ions at high concentrations, is a unique glass filler that are utilized in dentistry. Because of its multiple-ion releasing characteristics, S-PRG filler exhibits several bioactivities such as tooth strengthening, acid neutralization, promotion of mineralization, inhibition of bacteria and fungi, inhibition of matrix metalloproteinases, and enhancement of cell activity. Therefore, S-PRG filler per se and S-PRG filler-containing materials have the potential to be beneficial for various dental treatments and care. Those include restorative treatment, caries prevention/management, vital pulp therapy, endodontic treatment, prevention/treatment of periodontal disease, prevention of denture stomatitis, and perforation repair/root end filling. This review summarizes bioactive functions exhibited by S-PRG filler and its possible contribution to oral health.

Study of Streptococcus mutans in Early Biofilms at the Surfaces of Various Dental Composite Resins

BACKGROUND

Biofilm deposit on the composite restoration is a common phenomenon and bacterial growth follows the deposition. The study aims to evaluate Streptococcus mutans (S. mutans) early biofilm formation on the surfaces of various dental composite resins by using the real-time quantitative polymerase chain reaction (qPCR) technique.

MATERIALS AND METHODS

Thirty-two discs, where eight discs were in each group of Filtek Supreme Ultra (FSU; 3M, St. Paul, MN), Clearfil AP-X (APX; Kuraray Noritake Dental Inc., Tokyo, Japan), Beautifil II (BE2; Shofu, Inc., Kyoto, Japan), and Estelite Sigma Quick (ESQ; Tokuyama Dental, Tokyo, Japan), were fabricated and subjected to S. mutans biofilm formation in an oral biofilm reactor for 12 hours. Contact angles (CA) were measured on the freshly fabricated specimen. The attached biofilms underwent fluorescent microscopy (FM). S. mutans from biofilms were analyzed using a qPCR technique. Surface roughness (Sa) measurements were taken before and after biofilm formation. Scanning electron microscopy (SEM), including energy dispersive X-ray spectrometer (EDS) analysis, was also performed for detecting relative elements on biofilms.

RESULTS

The study showed that FSU demonstrated the lowest CA while APX presented the highest values. FM revealed that condensed biofilm clusters were most on FSU. The qPCR results indicated the highest S. mutans DNA copies in the biofilm were on FSU while BE2 was the lowest (p < 0.05). Sa test signified that APX was significantly the lowest among all materials while FSU was the highest (p < 0.05). SEM displayed areas with apparently glucan-free S. mutans more on BE2 compared to APX and ESQ, while FSU had the least. Small white particles detected predominantly on the biofilms of BE2 appeared to be Si, Al, and F extruded from the resin.

CONCLUSION

Differences in early biofilm formation onto various composite resins are dependent on the differences in material compositions and their surface properties. BE2 showed the lowest quantity of biofilm accumulation compared to other resin composites (APX, ESQ, and FSU). This could be attributed to BE2 proprieties as a giomer and fluoride content.

Effect of Particle Sizes and Contents of Surface Pre-Reacted Glass Ionomer Filler on Mechanical Properties of Auto-Polymerizing Resin

Herein, the mechanical properties of an auto-polymerizing resin incorporated with a surface pre-reacted glass ionomer (S-PRG) filler were evaluated. For this, S-PRG fillers with particle sizes of 1 μm (S-PRG-1) and 3 μm (S-PRG-3) were mixed at 10, 20, 30, and 40 wt% to prepare experimental resin powders. The powders and a liquid (powder/liquid ratio = 1.0 g/0.5 mL) were kneaded and filled into a silicone mold to obtain rectangular specimens. The flexural strength and modulus (n = 12) were recorded via a three-point bending test. The flexural strengths of S-PRG-1 at 10 wt% (62.14 MPa) and S-PRG-3 at 10 and 20 wt% (68.68 and 62.70 MPa, respectively) were adequate (>60 MPa). The flexural modulus of the S-PRG-3-containing specimen was significantly higher than that of the S-PRG-1-containing specimen. Scanning electron microscopy observations of the specimen fracture surfaces after bending revealed that the S-PRG fillers were tightly embedded and scattered in the resin matrix. The Vickers hardness increased with an increasing filler content and size. The Vickers hardness of S-PRG-3 (14.86–15.48 HV) was higher than that of S-PRG-1 (13.48–14.97 HV). Thus, the particle size and content of the S-PRG filler affect the mechanical properties of the experimental auto-polymerizing resin.

Effect of a Toothpaste Containing Surface Pre-Reacted Glass-Ionomer Filler on the Remineralization of Artificial Carious Enamel Lesions in situ

This study evaluated the remineralizing effect of a toothpaste containing surface pre-reacted glass-ionomer (S-PRG) filler on demineralized enamel in situ. For this, 180 bovine enamel samples were demineralized by using a microcosm biofilm model for 3 days. Thereafter, the samples were randomly signed to 15 healthy volunteers and to 3 cross-over in situ phases corresponding to the following treatments: (1) toothpaste containing 1,500 ppm F as NaMFP (positive control, Colgate®Cavity Protection), (2) toothpaste containing 5% S-PRG filler (Shofu®), and (3) placebo toothpaste (negative control prepared by Shofu®). Four demineralized enamel blocks were fixed into each palatal appliance per phase. The volunteers wore the appliances for 5 days and were trained to brush their teeth 2 times for 2 min a day, while one drop of the toothpaste's slurry (1:3) was dripped on each sample for the same period. The surface hardness and TMR analyses were done and analyzed by ANOVA/Tukey and t test (p < 0.05). S-PRG filler and Colgate® toothpastes were equally able to improve 2-2.5× enamel remineralization by the analysis of % surface hardness recovery. However, S-PRG toothpaste was the only one able to significantly improve ΔΔZ (the integrated mineral loss recovery: 1,489 ± 503 %vol.μm) compared to placebo (1,050 ± 467 %vol.μm), while Colgate® did not differ from placebo. No differences were seen between the groups with respect to ΔLD. S-PRG filler and Colgate® toothpastes show similar potential to remineralize the lesion surface. However, S-PRG toothpaste is better to recover mineral loss at the subsurface area.

Effect of Zinc Oxide Incorporation on the Antibacterial, Physicochemical, and Mechanical Properties of Pit and Fissure Sealants

This study aimed to evaluate the antibacterial, physicochemical, and mechanical properties of pit and fissure sealants containing different weight percentages of zinc oxide nanoparticles (ZnO NPs). The following amounts of ZnO NPs were added to a commercially available pit and fissure sealant (BeautiSealant, Shofu, Japan) to prepare the experimental materials: 0 wt.% (commercial control (CC)), 0.5 wt.% (ZnO 0.5), 1 wt.% (ZnO 1.0), 2 wt.% (ZnO 2.0), and 4 wt.% (ZnO 4.0). The antibacterial effect against S. mutans was confirmed by counting the colony-forming units (CFUs) and observing live/dead bacteria. In addition, ion release, depth of cure, water sorption and solubility, and flexural strength tests were conducted. When compared with the CC, the experimental groups containing ZnO NPs showed zinc ion emission and significantly different CFUs (p < 0.05) with fewer live bacteria. ZnO NP addition reduced the depth of cure and water solubility and increased water sorption in comparison with the CC (p < 0.05). However, all groups showed similar flexural strength (p > 0.05). The pit and fissure sealants containing ZnO NPs exhibited antibacterial activity against S. mutans with no negative effects on physicochemical and mechanical properties, and thus, these sealants can be ideal secondary caries prevention material.

Effect of surface prereacted glass ionomer nanofillers on fluoride release, flexural strength, and surface characteristics of polymethylmethacrylate resin

OBJECTIVE

Dentures should have proper fluoride release and physical properties. We evaluated how surface prereacted glass ionomer (S-PRG) nanofillers influenced fluoride release, flexural strength, and surface characteristics of polymethylmethacrylate (PMMA) resin.

MATERIALS AND METHODS

PMMA resin disc (n = 14) and rectangular (n = 5) specimens containing 0, 20 wt% microparticles, and 20 wt% nanoparticles of S-PRG were prepared. Six-disc specimens were examined for surface roughness; eight-disc specimens were immersed in 5 ml of deionized water for 24 h before analyzing the fluoride levels on days 1-3, 12, and 15. They were recharged with 1000 ppm fluoride solution for 24 h and stored in deionized water for five cycles. Fluoride release was examined. The flexural strength of the rectangular specimens was determined using a three-point bending test. Data were analyzed by two-way repeated-measures ANOVA.

RESULTS

S-PRG nanofiller had the highest fluoride exchange rate and did not significantly change the surface roughness compared with the microparticle and control groups; however, the nanofillers agglomerated and reduced the flexural strength to below 65 MPa.

CONCLUSIONS

Incorporating 20 wt% nanofillers into resin enhanced the fluoride exchange property greater than microfillers at the same content, but diminished the mechanical properties of the resin.

CLINICAL SIGNIFICANCE

Incorporating 20 wt% S-PRG nanofillers in resin denture base can improve the fluoride releasing property without affecting the surface roughness.

S-PRG-based toothpastes compared to NaF toothpaste and NaF varnish on dentin permeability in vitro

Objectives

To analyze the effect of 5 toothpastes containing different percentages of S-PRG fillers compared to NaF toothpaste and NaF varnish on the dentin hydraulic conductance (Lp).

Methodology

Dentin disks (1.0±0.2 mm thickness) were cut from third molars, and their Lp values were evaluated using Flodec. The specimens were allocated into 7 groups (n=8). The minimum (smear layer) and the maximum (after acid etching) Lp values were recorded. Lp was also assessed after treatment with either a 0wt.%, 1wt.%, 5wt.%, 20wt.%, or 30wt.% S-PRG toothpaste, a NaF toothpaste, or a NaF varnish. Toothpastes were applied by brushing for 15 s, allowing it to settle for 1 min, and rinsing with deionized water. The NaF varnish was applied for 4 min and was removed with a probe. Specimens were exposed to citric acid (6%, pH 2.1, 1 min) and their final Lp was recorded. The pH of all products was recorded (n=3) and specimens from each group were analyzed by Laser Scanning Confocal Microscopy (LSCM). Data were subjected to 2-way repeated measures ANOVA and post-hoc Bonferroni (a=0.05).

Results

The highest Lp reduction was noticed for the 5wt.% S-PRG toothpaste, NaF toothpaste, and NaF varnish. However, the toothpastes containing 5wt.%, 20wt.%, and 30wt.% of S-PRG were similar to all toothpastes but differed from the NaF varnish. After erosion, all groups retrieved their maximum Lp values, except for the NaF varnish. The LSCM evidenced deposits on the surface of specimens treated with 5%, 20%, and 30% S-PRG-based toothpastes and NaF toothpaste. Even more deposits were observed for the NaF varnish. After the erosive challenge, the deposits were diminished in all groups.

Conclusion

Toothpastes containing 5wt.%, 20wt.%, and 30wt.% of S-PRG fillers behaved similarly to a conventional NaF toothpaste, even after an erosive challenge. The NaF varnish promoted better reduction of the Lp, but its effect was also diminished after erosion.

Physical properties and wear behavior of CAD/CAM resin composite blocks containing S-PRG filler for restoring primary molar teeth

OBJECTIVES

This study aimed to develop computer-aided design/computer-aided manufacturing (CAD/CAM) resin composite blocks (RCBs) containing surface pre-reacted glass-ionomer (S-PRG) filler for primary molar teeth and evaluate their physical properties and wear resistance.

METHODS

Experimental CAD/CAM RCBs containing S-PRG filler for primary molar teeth (EB), a commercial CAD/CAM RCB (HC), two resin composites for primary teeth (BKP and BKZ) and one for permanent teeth (BⅡ) were used. Hardness tests, three-point bending tests, fracture toughness tests, and water absorption tests were conducted. Wear tests were conducted for these materials and stainless steel crowns (SSCs).

RESULTS

The Vickers hardness of EB was lower than that of HC (p < 0.05), and there was no significant difference among BKZ, BKP, and BⅡ (p > 0.05). After 1 week of water immersion, EB and HC showed greater flexural strength than the other materials (p < 0.05). EB showed greater fracture toughness than the other materials (p < 0.05). The water absorption of EB was lower than that of HC, BKZ, and BKP (p < 0.05), and greater than that of BⅡ (p < 0.05). Antagonist wear was significantly smaller in EB than in HC and BⅡ (p < 0.05), and significantly greater than in BKZ (p < 0.05). Antagonist wear could not be measured in SSC because of excessive wear that was out of range of the surface roughness tester.

SIGNIFICANCE

The CAD/CAM RCBs containing S-PRG filler for primary molar teeth developed in this study demonstrated adequate physical properties and wear performance, suggesting that they are suitable for restoration of primary molar teeth and could function in place of SSCs.

A novel methacrylate derivative polymer that resists bacterial cell-mediated biodegradation

This study tests biodegradation resistance of a custom synthesized novel ethylene glycol ethyl methacrylate (EGEMA) with ester bond linkages that are external to the central polymer backbone when polymerized. Ethylene glycol dimethacrylate (EGDMA) with internal ester bond linkages and EGEMA discs were prepared in a polytetrafluoroethylene (PTFE) mold using 40 μl macromer and photo/co-initiator mixture cured for 40 s at 1000 mW/cm² . The discs were stored in the constant presence of Streptococcus mutans (S. mutans) in Todd Hewitt Yeast + Glucose (THYE+G) media up to 9 weeks (n = 8 for each macromer type) and physical/mechanical properties were assessed. Initial measurements EGEMA versus EGDMA polymer discs showed equivalent degree of conversion (45.69% ± 2.38 vs. 46.79% ± 4.64), diametral tensile stress (DTS; 8.12± 2.92 MPa vs. 6.02 ± 1.48 MPa), and low subsurface optical defects (0.41% ± 0.254% vs. 0.11% ± 0.074%). The initial surface wettability (contact angle) was slightly higher (p ≤ .012) for EGEMA (62.02° ± 3.56) than EGDMA (53.86° ± 5.61°). EGDMA showed higher initial Vicker's hardness than EGEMA (8.03 ± 0.88 HV vs. 5.93 ± 0.69 HV; p ≤ .001). After 9 weeks of S. mutans exposure, EGEMA (ΔDTS-1.30 MPa) showed higher resistance to biodegradation effects with a superior DTS than EGDMA (ΔDTS-6.39 MPa) (p = .0039). Visible and scanning electron microscopy images of EGEMA show less surface cracking and defects than EGDMA. EGDMA had higher loss of material (18.9% vs. 8.5%, p = .0009), relative changes to fracture toughness (92.5% vs. 49.2%, p = .0022) and increased water sorption (6.1% vs. 1.9%, p = .0022) compared to EGEMA discs. The flipped external ester group linkage design is attributed to EGEMA showing higher resistance to bacterial degradation effects than an internal ester group linkage design methacrylate.

A water-soluble glass-based temporary restorative resin inhibited bacteria-induced pH reductions at the bacteria-material interface

This study aimed to evaluate the inhibitory effects of a water-soluble glass based temporary restorative resin (WSG-TRR) on bacteriainduced pH reductions at the bacteria-material interface. Each material (WSG-TRR, glass-ionomer cement, resin composite and conventional temporary restorative resin) was fixed to the bottom of the well of the experimental apparatus. The well was filled with pelleted cells of Streptococcus mutans, and the pH at the bacteria-material interface was monitored using a miniature pH electrode. The concentration of ions released from WSG-TRR and the effect of fluoride and zinc ions on bacteria-induced pH reduction was evaluated. The buffering capacities of WSG-TRR and WSG were also evaluated. At 90 min after the glucose addition, WSG-TRR exhibited the highest pH (5.29±0.12). Fluoride ion was detected at the interface between bacteria and WSG-TRR. Moreover, WSG were found to confer high buffering capacity. A WSG-TRR reduced bacteria-induced pH reductions at the bacteria-material interface.

Interactions of boron released from surface pre-reacted glass ionomer with enamel/dentin and its effect on pH

This study investigated the interaction of borate ions released from surface pre-reacted glass ionomer (S-PRG) fillers with the biological apatites of enamel and dentin using solid-state (SS) magic-angle spinning nuclear magnetic resonance (MAS-NMR) spectroscopy analysis. We further evaluated the effect of borate ions on the pH change. Bovine enamel and dentin powder were submerged in S-PRG eluate (with borate ion concentration of 100 mM) for 3 h, then washed with deionized water (DW). The dried enamel and dentin specimens were used for ¹¹B SS-NMR and Fourier transform infrared spectroscopy (FT-IR) analysis. Enamel and dentin blocks were treated with three solutions: DW (control), S-PRG eluent and borate solution (100 mM). The treated samples were submerged in the demineralization solution and the pH was measured using a pH meter daily for 6 days. The surfaces of the enamel and dentin blocks were then observed using field emission scanning electron microscopy (FE-SEM). SS-NMR analysis revealed the presence of adsorbed borate ions in the enamel and dentin samples in a tetra-coordinated form. The pH results demonstrated an increase in pH values in the S-PRG and borate groups. SEM images showed that the surfaces of the control group were demineralized, whereas the surfaces of the S-PRG and borate groups were intact. These results concluded that borate ions could be adsorbed to enamel and dentin in the tetra-coordinated form. Borate ions possess a buffer capacity which may help to protect the tooth structure against acid attacks and promote remineralization.

Novel antimicrobial denture adhesive containing S-PRG filler

The antimicrobial effects of denture adhesives containing novel surface pre-reacted glass-ionomer (S-PRG) fillers were assessed. We prepared denture adhesives containing S-PRG (particle sizes: 1 and 3 µm; quantities: 5, 7.5, and 10 wt%). We evaluated acid buffering capacity, ion release, and antimicrobial effects of denture adhesives with and without S-PRG. Significantly higher pH changes were observed in 1 µm S-PRG adhesives than in 3 µm S-PRG adhesives. Adhesives containing 7.5 and 10 wt% S-PRG exhibited significantly higher ion release than adhesives with 5 wt% S-PRG. The 1µm-10wt% S-PRG denture adhesive exhibited significantly lower colony-forming units on the denture adhesive contact surface than in the control group; additionally, it exhibited excellent acid buffering capacity, ion release properties, and antimicrobial effect against C. albicans, C. glabrata, S. mutans, and A. naeslundii. Longer contact periods resulted in significantly lower adhesion of Candida albicans to the denture base resin treated with denture adhesive.

S-PRG Filler Eluate Induces Oxidative Stress in Oral Microorganism: Suppression of Growth and Pathogenicity, and Possible Clinical Application

Controlling the oral microbial flora is putatively thought to prevent not only oral diseases, but also systemic diseases caused by oral diseases. This study establishes the antibacterial effect of the novel bioactive substance “S-PRG filler” on oral bacteria. We examined the state of oxidative stress caused by the six types of ions released in eluate from the S-PRG filler in oral bacterial cells. Moreover, we investigated the effects of these ions on the growth and pathogenicity of Gram-positive and Gram-negative bacteria. We found that the released ions affected SOD amount and hydrogen peroxide in bacterial cells insinuating oxidative stress occurrence. In bacterial culture, growth inhibition was observed depending on the ion concentration in the medium. Additionally, released ions suppressed Streptococcus mutans adhesion to hydroxyapatite, S. oralis neuraminidase activity, and Porphyromonas gingivalis hemagglutination and gingipain activity in a concentration-dependent manner. From these results, it was suggested that the ions released from the S-PRG filler may suppress the growth and pathogenicity of the oral bacterial flora. This bioactive material is potentially useful to prevent the onset of diseases inside and outside of the oral cavity, which in turn may have possible applications for oral care and QOL improvement.

Effect of the S-PRG filler content in the multi-ion releasing paste on the acid resistance of the enamel surface after polishing with the paste

This study aimed to investigate the effect of the multi-ion releasing paste (MP) on the acid resistance of the enamel surface of an extracted human tooth. Five kinds of MP were prepared according to the content (wt%) of S-PRG fillers: 0 wt% (MP0, control), 1 wt% (MP1), 5 wt% (MP5), 20 wt% (MP20), and 30 wt% (MP30). The buccal coronal surfaces of the extracted anterior teeth were polished with each kind of MP for 1 min. After removing radicular parts, the coronal parts underwent a pH cycling, and then sliced to make thin sections. The lesion depth of each section was measured using a polarization microscope. Each lesion's depth of enamel polished with MP5, MP20, and MP30 was significantly shallower than that polished with MP0.

Recent Progress in Antimicrobial Strategies for Resin-Based Restoratives

Repairing tooth defects with dental resin composites is currently the most commonly used method due to their tooth-colored esthetics and photocuring properties. However, the higher than desirable failure rate and moderate service life are the biggest challenges the composites currently face. Secondary caries is one of the most common reasons leading to repair failure. Therefore, many attempts have been carried out on the development of a new generation of antimicrobial and therapeutic dental polymer composite materials to inhibit dental caries and prolong the lifespan of restorations. These new antimicrobial materials can inhibit the formation of biofilms, reduce acid production from bacteria and the occurrence of secondary caries. These results are encouraging and open the doors to future clinical studies on the therapeutic value of antimicrobial dental resin-based restoratives. However, antimicrobial resins still face challenges such as biocompatibility, drug resistance and uncontrolled release of antimicrobial agents. In the future, we should focus on the development of more efficient, durable and smart antimicrobial dental resins. This article focuses on the most recent 5 years of research, reviews the current antimicrobial strategies of composite resins, and introduces representative antimicrobial agents and their antimicrobial mechanisms.

Fabrication and characterization of remineralizing dental composites containing calcium type pre-reacted glass-ionomer (PRG-Ca) fillers

OBJECTIVE

To fabricate and characterize dental composites with calcium type pre-reacted glass-ionomer (PRG-Ca) fillers.

METHODS

PRG-Ca fillers were prepared by the reaction of calcium fluoroaluminosilicate glass with polyacrylic acid. Seven dental composites were produced from the same organic matrix (70/30wt% Bis-GMA/TEGDMA), with partial replacement of barium borosilicate (BaBSi) fillers (60wt%) by PRG-Ca fillers (wt%): E0 (0) - control, E1 (10), E2 (20), E3 (30), E4 (40), E5 (50) and E6 (60). Enamel remineralization was evaluated in caries-like enamel lesions induced by S. mutans biofilm using micro-CT. The following properties were characterized: degree of conversion (DC%), roughness (Ra), Knoop hardness (KHN), flexural strength (FS), flexural modulus (FM), water sorption (W_sp), water solubility (W_sl), and translucency (TP). Data were analyzed to one-way ANOVA and Tukey's HSD test (α=0.05).

RESULTS

All composites with PRG-Ca induced enamel remineralization. E0 and E1 presented similar and highest DC% than E2=E3=E4=E5=E6. Ra and KHN were not influenced by PRG-Ca fillers (p<0.05). The higher the content of PRG-Ca, the lower FS, FM and TP (p<0.05). W_sp increased linearly with the content of PRG-Ca fillers (p<0.05). E6 presented the highest W_sl (p<0.05), while the W_sl of the other composites were not different from each other (p>0.05).

SIGNIFICANCE

Incorporation of 10-40wt.% of PRG-Ca fillers endowed remineralizing potential to dental composites without jeopardizing the overall behavior of their physicochemical properties. Dental composites with PRG-Ca fillers seems to be a good alternative for reinforcing the enamel against caries development.

Evaluation of surface characteristic and bacterial adhesion of low-shrinkage resin composites

This study aimed to examine the surface characteristics of low shrinkage composites and adhesion of Streptococcus mutans and Streptococcus mitis to these materials. Control material (glass) and three low shrinkage composites (Charisma Diamond, Kalore GC, Beatiful II LS) were used. After polishing procedure was applied to composite specimens, surface roughness (SR), surface free energy (SFE), and contact angle measurements were performed. Surfaces of composite were analyzed using scanning electron microscope and energy-dispersive X-ray spectroscopy. After pellicle formation with artificial saliva, S. mutans and S. mitis biofilms were incubated in 5% CO₂ for 24 h at 37°C and were analyzed using confocal laser scanning microscopy. The lowest SR and highest SFE values were found in the control group. While the contact angle of control was statistically lower than composites, statistically difference was not found between composite groups. S. mutans adhesion of composites was significantly lower than control group, but there was no significant difference between composites. S. mitis adhesion of all groups was statistically similar. SR did not affect the S. mutans and S. mitis adhesion. Less adherence of S. mutans to low shrinkage composites was associated with low SFE and high contact angle values. Even though the highest SR was observed in the Charisma Diamond, no difference was found between the composites in terms of bacterial adhesion.

[Evaluation of wear property of Giomer and universal composite in vivo]

OBJECTIVE

To observe the wear performance of Giomer and universal composite for posterior restorations by 3D laser scan method, in order to guide the material selection in clinic.

METHODS

In this study, 48 patients (108 teeth) were selected according to the inclusion and exclusion criteria. All the patients in need of a minimum of 2 Class Ⅰ and/or Class Ⅱ restorations were invited to join the study. The teeth were restored with Giomer (Beautifil Ⅱ, BF) and universal composite (Filtek Z350, Z350) randomly. The restorations were evaluated at baseline and after 6-, 18-, 48-month using the modified United States Public Health Service (USPHS) criteria for clinical performance. The in vivo images and gypsum replicas were taken at each recall. A 3D-laser scanner and Geomagic Studio 12 were used to analyze the wear depth quantitatively. Statistical analysis was performed with SPSS 20.0.

RESULTS

After 4 years, 89.6% patients were recalled. The survival rate of both materials was 95.8% (Kaplan-Meier survival analysis). Seven restorations of the two materials failed due to loss of restoration, bulk fracture, secondary caries and pulp necrosis. The wear patterns of restorations were divided into 2 classes. Pattern Ⅰ: occlusal contact areas showed the deepest and fastest wear depth; pattern Ⅱ: the wear depth was slow and uniform. Both materials showed a rapid wear in the first 6 months. Then the wear rate was decreased. The occlusal wear depth after 4 years were (58±22) μm and (54±16) μm for BF group and Z350 group respectively, which were in accordance with the American Dental Association (ADA) guidelines (wear depth for 3 years < 100 μm). No significant differences (P>0.05) were observed between the two groups. Regarding the restorations with wear pattern Ⅰ, the wear depth of BF group was higher than Z350 group at 6- and 48-month (P < 0.05), while there was no significant difference between restorations with wear pattern Ⅱ (P>0.05).

CONCLUSION

Within the limitation of the study, after 4 years, the survival rate and wear resistance of Giomer met ADA guidelines for tooth-colored restorative materials for posterior teeth. When the two materials were applied in occlusal contact areas, wear resistance of Giomer was slightly lower than universal composite resin. No significant difference was found when they were applied in none of the occlusal contact areas.

Effects of a surface prereacted glass-ionomer filler coating material on biofilm formation and inhibition of dentin demineralization

OBJECTIVES

This study investigated the ability of a surface prereacted glass-ionomer (S-PRG) coating material to inhibit the biofilm formation and demineralization of dentin.

METHODS AND MATERIALS

Dentin specimens were randomly divided into three groups: (1) no coating (control), (2) S-PRG filler-containing coat, and (3) a nonS-PRG filler-containing coat. Streptococcus mutans biofilms were grown on the dentin surfaces in a microcosm for 20 h. Then, the quantity of bacteria and water-insoluble glucan in the retained biofilm on the dentin surface were measured. Regarding demineralization inhibition test, specimens were demineralized for 5 days then sectioned into halves and observed under confocal laser scanning microscope (CLSM). One-way ANOVA and Tukey's HSD were used for statistical analysis.

RESULTS

The estimated mean surface roughness for specimens in the S-PRG group was statistically significantly higher than the estimates for both the nonS-PRG and the control group specimens. The quantity of bacteria and water-insoluble glucan/mm² revealed that the S-PRG group prevented biofilm formation and bacterial adhesion to the dentin surface compared with the control and nonS-PRG groups. The S-PRG group recorded the highest acid-resistance ability with no surface loss.

CONCLUSION

Application of S-PRG barrier coat on dentin surfaces can inhibit biofilm formation as well as protecting the dentin surface against demineralization.

CLINICAL SIGNIFICANCE

Coating material containing S-PRG fillers might be used for caries prevention, through inhibiting biofilm formation, enhancing mineralization, and reducing acidic attack by cariogenic bacteria.

Opportunities for caries prevention using an ion-releasing coating material: a randomised clinical study

Ion-releasing materials (containing fluoride and boron, for example) have shown caries-preventive effects in vitro. The purpose of the present study was to investigate the impact of multi-ion-releasing coating material on pH stabilisation, plaque accumulation and the bacterial composition of dental plaque during a time period of 90 days. The null hypothesis tested here was that the evaluated material would not show any differences in pH stabilisation, plaque accumulation or bacterial composition compared with control material.

The study was carried out as a double-blind, split-mouth, randomised, controlled clinical trial in 28 volunteers. Over the evaluation period (days 4, 30, 60 and 90), pH measurements, plaque index and plaque sampling for bacterial analyses were conducted in a calibrated, standardized manner. The study received ethical permission and was carried out in accordance with the Helsinki Declaration.

A significant difference was observed, with less plaque accumulation over time in the subjects in whom the ion-releasing material was applied in comparison to the non-active group. No significant difference was evident in terms of either pH stabilisation or plaque levels of mutans streptococci.

The null hypothesis relating to plaque accumulation was rejected, with a lower plaque index shown for the test group up to 60–90 days. No adverse effects during the observation period were observed. Since the studied cohort was healthy from a caries perspective, more clinical studies are needed to further evaluate the caries-prevention potential of the ion-releasing material in other patient groups.

In vivo Microbial Diversity Analysis on Different Surfaces of Dental Restorative Materials via 16S rDNA Sequencing

Background

This study aimed to provide precise material selection guidance for proper clinical restoration and treatment of plaque-related oral diseases, such as dental caries and periodontal diseases.

Material/Methods

Four groups (n=24) of restorative material sheets (n=24) were prepared using 3M Z350 composite resin (ZR), zinc phosphate cement (ZPC), glass-ionomer (GI), and ICON permeable resin (IPR). Six volunteers wore a plaque-collection device equipped with the 4 restorative material sheets for 48 hours. Plaque samples were collected, and Miseq sequencing was applied to obtain template DNA fragments for microbial diversity analysis. The data were analyzed with nonparametric tests.

Results

The microbial diversity on the ZPC surface was significantly lower than that on GI and IPR surfaces. The abundance of Firmicutes and Streptococcus on the ZPC surface was significantly higher than on the surfaces of GI and IPR. In contrast, the abundance of Porphyromonas on the surface of ZPC was significantly lower than that on GI and IPR surfaces. (P<0.05).

Conclusions

The results of the present study might serve as a basis for material selection under different oral microbial conditions to provide more accurate treatments and restorative procedures in the oral cavity.

Basic properties of novel S-PRG filler-containing cement

This study was aimed to evaluate the effect of a novel surface pre-reacted glass-ionomer (S-PRG) filler-containing cement for root caries. We prepared the cements using five different S-PRG filler amounts (0, 10, 20, 30, and 40 wt%). Compressive strength, ion release, acid buffering capacity, and microstructure of the as-prepared cements were evaluated. The compressive strength was statistically significant; it was highest for 0 wt% S-PRG cement. Ion release in 0 wt% S-PRG was highest for F^- and Al, whereas in 40 wt% S-PRG it was highest for B. For 20, 30, and 40 wt% S-PRG cements, Na and Sr release was higher compared to the other ions. The acid buffering capacity was significantly higher in the 40 wt% S-PRG cement than in the others. In the microstructural analysis, no difference of surface structure was observed among each of the S-PRG filler contents (0-40 wt% S-PRG).

Protective Effects of GIC and S-PRG Filler Restoratives on Demineralization of Bovine Enamel in Lactic Acid Solution

This study was aimed at investigating the protective effects of glass ionomer cement (GIC) and surface pre-reacted glass ionomer (S-PRG) fillers used as dental restorative materials on demineralization of bovine enamel. GlasIonomer FX ULTRA (FXU), Fuji IX GP Extra (FIXE), CAREDYNE RESTORE (CDR) were used as GICs. PRG Barrier Coat (BC) was used as the S-PRG filler. They were incubated in a lactic acid solution (pH = 4.0) for six days at a temperature of 37 °C. The mineral was etched from the enamel surface, and a large number of Ca and P ions were detected in solution. The Al, F, Na, Sr, and Sr ions were released in GICs and S-RPG fillers. The Zn ion was released only in CDR and the B ion was released only in BC. The presence of apparent enamel prism peripheries was observed after six days of treatment for the group containing only enamel blocks. pH values for the FXU, FIXE, CDR, BC, and enamel block groups after six days were 6.5, 6.6, 6.7, 5.9, and 5.1, respectively. Therefore, the observed pH neutralization effect suppressed progression of caries due to the release of several ions from the restoratives.

Acidity-induced release of zinc ion from BioUnionTM filler and its inhibitory effects against Streptococcus mutans

BioUnion filler incorporated into restorative/coating materials is a new bio-functional glass powder. The most unique function of BioUnion filler is its ability to release Zn²⁺ in acidic environments. In this study, the ion release profile of BioUnion filler under acidic conditions and its antibacterial effects against Streptococcus mutans were evaluated. The concentrations of Zn²⁺ released from BioUnion fillers into acetic acids were greater than those released into water. S. mutans inhibition by BioUnion fillers was greater with sucrose than without sucrose, reflecting a decrease in suspension pH in response to the addition of sucrose. Exposure to acids increased Zn²⁺ release from BioUnion fillers, and the fillers after repeated exposure to acids demonstrated inhibitory effects against S. mutans. These findings suggest that BioUnion filler accelerated the release of Zn²⁺ under acidic conditions, which induced bactericidal/inhibitory effects against S. mutans.

Cutting-edge filler technologies to release bio-active components for restorative and preventive dentistry

Advancements in materials used for restorative and preventive treatment is being directed toward "bio-active" functionality. Incorporation of filler particles that release active components is a popular method to create bio-active materials, and many approaches are available to develop fillers with the ability to release components that provide "bio-protective" or "bio-promoting" properties; e.g. metal/calcium phosphate nanoparticles, multiple ion-releasing glass fillers, and non-biodegradable polymer particles. In this review paper, recent developments in cutting-edge filler technologies to release bio-active components are addressed and summarized according to their usefulness and functions, including control of bacterial infection, tooth strengthening, and promotion of tissue regeneration.

Polymeric and inorganic nanoscopical antimicrobial fillers in dentistry

Failure of dental treatments is mainly due to the biofilm accumulated on the dental materials. Many investigations have been conducted on the advancements of antimicrobial dental materials. Polymeric and inorganic nanoscopical agents are capable of inhibiting microorganism proliferation. Applying them as fillers in dental materials can achieve enhanced microbicidal ability. The present review provides a broad overview on the state-of-the-art research in the field of antimicrobial fillers which have been adopted for incorporation into dental materials over the last 5 years. The antibacterial agents and applications are described, with the aim of providing information for future investigations. STATEMENT OF SIGNIFICANCE: Microbial infection is the primary cause of dental treatment failure. The present review provides an overview on the state-of-art in the field of antimicrobial nanoscopical or polymeric fillers that have been applied in dental materials. Trends in the biotechnological development of these antimicrobial fillers over the last 5 years are reviewed to provide a backdrop for further advancement in this field of research.

Bioactive resin-based composite with surface pre-reacted glass-ionomer filler and zwitterionic material to prevent the formation of multi-species biofilm

OBJECTIVE

This study evaluated the synergetic effect between surface pre-reacted glass-ionomer (SPRG) filler and 2-methacryloyloxyethyl phosphorylcholine (MPC), for inhibiting multi-species biofilm formation, while maintaining or even improving the original beneficial features of SPRG-filled resin-based composite (RBC).

METHODS

MPC (1.5-10wt%) was incorporated into commercial SPRG-filled RBC. Then, the inherent properties of RBC, and ion release and acid-neutralising properties associated with SPRG were investigated. Further, protein adsorptions and bacterial adhesion and viability on the SPRG-filled RBC surfaces were studied using four kinds of oral bacteria; Streptococcus mutans, Actinomyces naeslundii, Veillonella parvula, and Porphyromonas gingivalis. Finally, the thickness and biomass of the human saliva-derived biofilm model cultured on test and control samples were analysed.

RESULTS

Addition of MPC content resulted in decreased flexural strength and wettability of SPRG-filled RBC. SPRG-filled RBC released significantly higher amounts of multiple ions as contents of MPC increased. Meanwhile, SPRG-filled RBC with 5-wt% MPC significantly improved acid-neutralising properties than those of other test and control samples (P<0.001). SPRG-filled RBC with 3wt% MPC significantly reduced the amount of adsorbed bovine serum albumin and proteins from the brain heart infusion medium as compared to the control (P<0.01). A similar trend was observed in the attachment of four types of bacteria and multi-species biofilm (P<0.01).

SIGNIFICANCE

Despite limitation in terms of deteriorations of some physical properties, addition of 3% MPC to SPRG-filled RBC leads to inhibition of the attachment of multi-species bacteria on its surface, as well as inhibition of biofilm growth. Moreover, the original important bioactive features of SPRG-filled RBC such as ion release and acid neutralisations are either maintained or improved upon adding MPC.

Time dependence of multi-ion absorption into human enamel from surface prereacted glass-ionomer (S-PRG) filler eluate

Ion incorporation into the tooth is expected to be effective for caries prevention. Time-dependent ion incorporation released from surface pre-reacted glass-ionomer (S-PRG) filler eluate into tooth enamel was estimated by using inductively coupled plasma atomic emission spectroscopy (ICP-AES). Al, B, and Sr contents in enamel were increased in a time-dependent manner with immersion in S-PRG eluate. Clear ion incorporation was observed after 1 h of immersion in S-PRG filler eluate. Sr showed remarkable incorporation in enamel -up to 7,900 ppm- after 28 days of immersion. Sr and B incorporation rapidly occurred in S-PRG filler eluate, compared with their single component solutions. Simultaneous incorporation of cations and anions from S-PRG eluate occurred under balanced charge and may assist in rapid ion incorporation. Thus, various useful ions could be effectively incorporated into tooth enamel by applying S-PRG filler or its eluate; a bioactive effect can be expected.

Novel Bioactive and Therapeutic Dental Polymeric Materials to Inhibit Periodontal Pathogens and Biofilms

Periodontitis is a common infectious disease characterized by loss of tooth-supporting structures, which eventually leads to tooth loss. The heavy burden of periodontal disease and its negative consequence on the patient's quality of life indicate a strong need for developing effective therapies. According to the World Health Organization, 10⁻15% of the global population suffers from severe periodontitis. Advances in understanding the etiology, epidemiology and microbiology of periodontal pocket flora have called for antibacterial therapeutic strategies for periodontitis treatment. Currently, antimicrobial strategies combining with polymer science have attracted tremendous interest in the last decade. This review focuses on the state of the art of antibacterial polymer application against periodontal pathogens and biofilms. The first part focuses on the different polymeric materials serving as antibacterial agents, drug carriers and periodontal barrier membranes to inhibit periodontal pathogens. The second part reviews cutting-edge research on the synthesis and evaluation of a new generation of bioactive dental polymers for Class-V restorations with therapeutic effects. They possess antibacterial, acid-reduction, protein-repellent, and remineralization capabilities. In addition, the antibacterial photodynamic therapy with polymeric materials against periodontal pathogens and biofilms is also briefly described in the third part. These novel bioactive and therapeutic polymeric materials and treatment methods have great potential to inhibit periodontitis and protect tooth structures.

Developing a New Generation of Therapeutic Dental Polymers to Inhibit Oral Biofilms and Protect Teeth

Polymeric tooth-colored restorations are increasingly popular in dentistry. However, restoration failures remain a major challenge, and more than 50% of all operative work was devoted to removing and replacing the failed restorations. This is a heavy burden, with the expense for restoring dental cavities in the U.S. exceeding $46 billion annually. In addition, the need is increasing dramatically as the population ages with increasing tooth retention in seniors. Traditional materials for cavity restorations are usually bioinert and replace the decayed tooth volumes. This article reviews cutting-edge research on the synthesis and evaluation of a new generation of bioactive dental polymers that not only restore the decayed tooth structures, but also have therapeutic functions. These materials include polymeric composites and bonding agents for tooth cavity restorations that inhibit saliva-based microcosm biofilms, bioactive resins for tooth root caries treatments, polymers that can suppress periodontal pathogens, and root canal sealers that can kill endodontic biofilms. These novel compositions substantially inhibit biofilm growth, greatly reduce acid production and polysaccharide synthesis of biofilms, and reduce biofilm colony-forming units by three to four orders of magnitude. This new class of bioactive and therapeutic polymeric materials is promising to inhibit tooth decay, suppress recurrent caries, control oral biofilms and acid production, protect the periodontium, and heal endodontic infections.

Nanostructured Polymeric Materials with Protein-Repellent and Anti-Caries Properties for Dental Applications

Dental caries is prevalent worldwide. Tooth cavity restorations cost more than $46 billion annually in the United States alone. The current generation of esthetic polymeric restorations have unsatisfactory failure rates. Replacing the failed restorations accounts for 50–70% of all the restorations. This article reviewed developments in producing a new generation of bioactive and therapeutic restorations. This includes: Protein-repellent and anti-caries polymeric dental composites, especially the use of 2-methacryloyloxyethyl phosphorylcholine (MPC) and dimethylaminododecyl methacrylate (DMAHDM); protein-repellent adhesives to greatly reduce biofilm acids; bioactive cements to inhibit tooth lesions; combining protein-repellency with antibacterial nanoparticles of silver; tooth surface coatings containing calcium phosphate nanoparticles for remineralization; therapeutic restorations to suppress periodontal pathogens; and long-term durability of bioactive and therapeutic dental polymers. MPC was chosen due to its strong ability to repel proteins. DMAHDM was selected because it had the most potent antibacterial activity when compared to a series of antibacterial monomers. The new generation of materials possessed potent antibacterial functions against cariogenic and periodontal pathogens, and reduced biofilm colony-forming units by up to 4 logs, provided calcium phosphate ions for remineralization and strengthening of tooth structures, and raised biofilm pH from a cariogenic pH 4.5 to a safe pH 6.5. The new materials achieved a long-term durability that was significantly beyond current commercial control materials. This new generation of bioactive and nanostructured polymers is promising for wide applications to provide therapeutic healing effects and greater longevity for dental restorations.