Novel hydrolytic resistant antibacterial monomers for dental resin adhesive

Mechanical and Antimicrobial Properties of Boron Nitride/Methacrylic Acid Quaternary Ammonium Composites Reinforced Dental Flowable Resins

Dental resin composites (DRCs) are commonly used to restore teeth affected by dental caries or defects. These materials must possess excellent properties to withstand the complex oral environment. The objective of this study was to prepare and characterize Boron nitride nanosheets (BNN)/ dimethyl amino hexadecyl methacrylate (DMAHDM) composites (BNN/DMA), and to evaluate them as functional fillers to enhance the mechanical and antimicrobial properties of dental resins. The BNN/DMA composites were successfully prepared under the theoretical guidance of molecular dynamics (MD), and then the physicochemical and morphological characterization of the BNN/DMA composites were carried out by using various test methods, such as FT-IR, XRD, UV-vis spectroscopy, SEM, TEM, and AFM. It was doped into the dental flowable resin in a certain proportion, and the results showed that the flexural strength (FS), elastic modulus (EM), compressive strength (CS), and microhardness (MH) of the modified resin composites were increased by 53.29, 47.8, 97.59, and 37.1%, respectively, with the addition of 0.8 wt % of BNN/DMA composite fillers. It has a good inhibition effect on Streptococcus mutans, with an inhibition rate as high as 90.43%. Furthermore, this effect persists even after one month of aging. In conclusion, the modification of flowable resins with low-concentration BNN/DMA composites favorably integrates the mechanical properties and long-term antimicrobial activity of dental resins. At the same time, they have good biocompatibility and do not affect the aesthetics. The BNN/DMA composite modified flowable resin has the potential to become a new type of antimicrobial dental restorative material.

Novel resin-based material containing β-tricalcium phosphate nanoparticles for the reduction of dentin permeability

OBJECTIVES

To synthesize and characterize a novel dentin adhesive containing Beta-Tricalcium Phosphate (β-TCP) nanoparticles and test its ability to reduce dentin permeability (dP).

METHODS

Experimental adhesives were prepared by mixing Bis-GMA, TEGDMA, HEMA (50/25/25 wt.%), photo-initiators, and inhibitors. The following groups were tested: Experimental adhesives without β-TCP (Exp.); with 10 wt.% β-TCP (Exp.10 wt.% β-TCP); with 15 wt.% β-TCP (Exp.15 wt.% β-TCP), Scotchbond Multi-Purpose (SBMP) and Clearfil SE Protect Bond (CFPB). Degree of conversion (DC%, 10 and 20 s); Flexural Strength (FS), Knoop Hardness (KHN), and Cell Viability (OD%) tests were performed. dP was evaluated by hydraulic conductance, using human dentin disks (n=12), at three-time intervals: post-EDTA (T0); post-treatment (T1); and post-erosion/abrasion cycling (T2). Data were statistically analyzed (α=0.05).

RESULTS

For all groups, exposure time for 20 s presented a higher DC% than for 10 s. For FS, filled adhesives did not differ from unfilled and from CFPB. Experimental adhesives did not differ among them and showed lower KHN than the commercial products. Cell viability did not differ among adhesives, except Exp. 15 wt.%, which showed lower OD% than Exp., Exp. 10% and, CFPB. For dP, only Exp.10 and 15 wt.% β-TCP did not present difference between the times T1 and T2. After cycling, Exp.10 wt.% β-TCP presented lower permeability than Exp. and CFPB.

CONCLUSIONS

The incorporation of 10 wt.% β-TCP nanoparticles into the resin-based dental material did not affect its mechanical properties and biocompatibility, and promoted the greatest reduction in dentin permeability, sustaining this effect under erosive/abrasive challenges.

CLINICAL SIGNIFICANCE

A novel resin-based dental material containing β-TCP nanoparticles was able to reduce dentin permeability, maintaining its efficacy after erosive/abrasive challenges. The synthesized material did not affect dental pulp cell viability and might be promising for other conditions that require dental remineralization, such as tooth wear and dental caries.