Electrocatalytic oxidation of formic acid on Pd/CNTs nanocatalysts synthesized in special “non-aqueous” system

A "Special" Solvent to Prepare Alloyed Pd2Ni1 Nanoclusters on a MWCNT Catalyst for Enhanced Electrocatalytic Oxidation of Formic Acid

Herein, an electrocatalyst with Pd₂Ni₁ nanoclusters, supporting multiwalled carbon nanotubes (MWCNTs) (referred to Pd₂Ni₁/CNTs), was fabricated with deep eutectic solvents (DES), which simultaneously served as reducing agent, dispersant, and solvent. The mass activity of the catalyst for formic acid oxidation reaction (FAOR) was increased nearly four times compared to a Pd/C catalyst. The excellent catalytic activity of Pd₂Ni₁/CNTs was ascribed to the special nanocluster structure and appropriate Ni doping, which changed the electron configuration of Pd to reduce the d-band and to produce a Pd-Ni bond as a new active sites. These newly added Ni sites obtained more OH^- to release more effective active sites by interacting with the intermediate produced in the first step of FAOR. Hence, this study provides a new method for preparing a Pd-Ni catalyst with high catalytic performance.

Pd3Co1 Alloy Nanocluster on the MWCNT Catalyst for Efficient Formic Acid Electro-Oxidation

In this study, the Pd₃Co₁ alloy nanocluster from a multiwalled carbon nanotube (MWCTN) catalyst was fabricated in deep eutectic solvents (DESs) (referred to Pd₃Co₁/CNTs). The catalyst shows a better mass activity towards the formic acid oxidation reaction (FAOR) (2410.1 mA mg_Pd^-1), a better anti-CO toxicity (0.36 V) than Pd/CNTs and commercial Pd/C. The improved performance of Pd₃Co₁/CNTs is attributed to appropriate Co doping, which changed the electronic state around the Pd atom, lowered the d-band of Pd, formed a new Pd-Co bond act at the active sites, affected the adsorption of the toxic intermediates and weakened the dissolution of Pd; moreover, with the assistance of DES, the obtained ultrafine Pd₃Co₁ nanoalloy exposes more active sites to enhance the dehydrogenation process of the FAOR. The study shows a new way to construct a high-performance Pd-alloy catalyst for the direct formic acid fuel cell.

Unveiling the effect of gas treatment on the electronic structure of carbon nanotube-supported Pd catalysts for electroreduction of H2O2 and Heck reaction

This study explored the impact of gas treatments on the structures of multi-walled carbon nanotubes supported Pd (CNT-Pd) catalysts used for electrocatalytic H₂O₂ reduction and the Heck cross-coupling reaction. The CNT-Pd catalyst was prepared by anchoring Pd nanoparticles on thiolated CNTs. XPS was conducted to examine the surface composition and electronic structure changes of the CNT-Pd catalyst before and after gas treatment. The XPS results revealed that as-prepared CNT-Pd contains at least two different oxidation states on the surface, whereon their proportions depend on the gas used for treatment. Treatment with H₂ leads to Pd(0) enrichment near the surface, while O₂ treatment causes Pd(Ⅱ) enrichment of CNT-Pd. All catalysts containing both Pd(0) and Pd(Ⅱ) were active toward H₂O₂ reduction, and the Heck cross-coupling reaction of n-butyl acrylate and 4-iodotoluene; increased proportion of metallic Pd(0) boosted the catalytic reaction. However, the catalyst stability increased as the amount of Pd(II) increased.