Growth of Ag/g-C3N4 nanocomposites on nickel foam to enhance photocatalytic degradation of formaldehyde under visible light

M-Encapsulated Be12O12 Nano-Cage (M = K, Mn, or Cu) for CH2O Sensing Applications: A Theoretical Study

DFT and TD-DFT studies of B3LYP/6-31 g(d,p) with the D2 version of Grimme's dispersion are used to examine the adsorption of a CH2O molecule on Be12O12 and MBe12O12 nano-cages (M = K, Mn, or Cu atom). The energy gap for Be12O12 was 8.210 eV, while the M encapsulation decreased its value to 0.685-1.568 eV, whereas the adsorption of the CH2O gas decreased the Eg values for Be12O12 and CuBe12O12 to 4.983 and 0.876 eV and increased its values for KBe12O12 and MnBe12O12 to 1.286 and 1.516 eV, respectively. The M encapsulation enhanced the chemical adsorption of CH2O gas with the surface of Be12O12. The UV-vis spectrum of the Be12O12 nano-cage was dramatically affected by the M encapsulation as well as the adsorption of the CH2O gas. In addition, the adsorption energies and the electrical sensitivity of the Be12O12 as well as the MBe12O12 nano-cages to CH2O gas could be manipulated with an external electric field. Our results may be fruitful for utilizing Be12O12 as well as MBe12O12 nano-cages as candidate materials for removing and sensing formaldehyde gas.

Silica wastes derived multifunctional coatings for formaldehyde photodegradation and autonomous indoor humidity buffering

To maintain a comfortable and healthy indoor environment without large amounts of energy consumption is of great importance. The progress of multifunctional indoor coatings with formaldehyde photodegradation and humidity buffering capability is necessary. From the viewpoints of circular economy, the preparation of effective photocatalysts (denoted as sFCC/GCN-x and ESF/GCN-y) via the decoration of recycling industrial wastes (i.e., spent fluid catalytic cracking catalysts (sFCC) and enhancement silica fume (ESF)) onto graphitic carbon nitride (GCN) by using a simple route is reported. The obtained results show that the prepared sFCC/GCN-0.15 and ESF/GCN-0.15 photocatalysts have the rate constants of formaldehyde degradation of 0.0075 and 0.0082 min-1, respectively, which are superior to that of pristine GCN (0.0044 min-1) under visible-light irradiation. The enhanced transfer kinetics of photogenerated electrons and declined recombination of electron-hole pairs may account for the surpassing photocatalytic performance. Results obtained from electron paramagnetic resonance spectra and Mott-Schottky plots indicate that the formation of ･O2- via the reaction of O2 with electrons generated on the conduction band is the major reaction pathway to photodegrade formaldehyde under visible light. To further assess the real applications of prepared photocatalysts, the sFCC/GCN-0.15 and ESF/GCN-0.15 are used to fabricate the multifunctional coatings (denoted as s- and E-coatings) with sFCC and ESF as the main compositions. Experimentally, the E-coatings could reach the formaldehyde degradation efficiency of ca. 84.5% after 3 h of visible light irradiation and excellent humidity buffering ability (293.8 g m-2) which is at least 10-folds higher than commercial coatings (28.9 g m-2). This notable progress of humidity buffering capacity on E-coatings can be attributed to their surface textural properties. Most importantly, this study exemplifies the valorization of inorganic silica wastes to produce sustainable and multifunctional coatings which may offer the practical and cost-effective applications in the indoor living space.