Laser irradiation method to prepare polyethylene porous fiber membrane with ultrahigh xylene gas filtration capacity

Preparation of Bamboo-Based Activated Carbon via Steam Activation for Efficient Methylene Blue Dye Adsorption: Modeling and Mechanism Studies

Dye pollution has long been an ecological and human health issue. Activated carbon is considered to be the most promising material for dye adsorption. In this study, bamboo was used as a biomass precursor to produce activated carbon with a high specific surface area by the steam activation method. The physical activation reaction between water vapor and bamboo promotes the carbonization product to have a rich porous structure. The prepared activated carbon was investigated from the perspectives of surface morphology, elemental change, surface porosity, and surface functional groups using a variety of techniques. According to the Brunauer-Emmett-Teller analysis, the activated carbon has a high surface area (1273 m2/g) and a mesoporous structure (average pore size 3.1 nm). On this basis, the effect of activated carbon on the removal of methylene blue (MB) dye from aqueous environments was evaluated and optimized by response surface methodology (RSM). Key adsorption parameters include initial MB concentration (150-200 mg/L), adsorption time (5-120 min), adsorbent dosage (30-50 mg), adsorption temperature (5-50 °C), and solution pH (3-11). Box-Behnken design (BBD) was used for modeling and analysis. Kinetic and isotherm model studies show that pseudo-second-order model kinetics and Langmuir isotherm can better describe the process of MB dye adsorption. This study will provide new ideas for the preparation of bamboo-activated carbon and provide a model prediction basis for dye adsorption research.

Aramid textile with near-infrared laser-induced graphene for efficient adsorption materials

Porous carbon materials show great application potential in the field of adsorption. However, the preparation process of carbon adsorption materials relies on high temperature, high energy consumption, many steps, and long time. Most of them exist in the form of powder or block, and the practical application scenarios are limited and difficult to recycle. In this study, based on in-situ carbonization of polymer precursor, we directly generated laser-induced graphene (LIG) on the surface of commercial aramid textile using a low-energy near-infrared laser in air, and prospected the application prospect of the prepared aramid/graphene textile in the field of adsorption. Under a certain laser energy, the photothermal reaction promotes the breaking of the CO and CN bonds in the surface layer of the aramid fiber, and reorganizes into a graphene structure at an instantaneous high temperature, while the overall flexible structure of the textile was not destroyed. Further, adsorption materials based on the as-prepared aramid/graphene textiles were also designed, including VOC-adsorbing textile in air and dye-adsorbing textile in water. Using low-energy near-infrared laser to directly achieve LIG writing in commercial textiles under air condition will provide an efficient, environmentally friendly, and designable direction for the large-scale fabrication of textile adsorption products.

Preparation and Laser Marking Properties of Poly(propylene)/Molybdenum Sulfide Composite Materials

In this study, using molybdenum sulfide (MoS₂) as laser-sensitive particles and poly(propylene) (PP) as the matrix resin, laser-markable PP/MoS₂ composite materials with different MoS₂ contents ranging from 0.005 to 0.2% were prepared by melt-blending. A comprehensive analysis of the laser marking performance of PP/MoS₂ composites was carried out by controlling the content of laser additives, laser current intensity, and the scanning speed of laser marking. The color difference test shows that the best laser marking performance of the composite can be obtained at the MoS₂ content of 0.02 wt %. The surface morphology of the PP/MoS₂ composite material was observed after laser marking using a metallographic microscope, an optical microscope, and a scanning electron microscope (SEM). During the laser marking process, the laser energy was absorbed and converted into heat energy to cause high-temperature melting, pyrolysis, and carbonization of PP on the surface of the PP/MoS₂ composite material. The black marking from carbonized materials was formed in contrast to the white matrix. Using X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, and Raman spectroscopy, the composite materials before and after laser marking were tested and characterized. The PP/MoS₂ composite material was pyrolyzed to form amorphous carbonized materials. The effect of the laser-sensitive MoS₂ additive on the mechanical properties of composite materials was investigated. The results show that the PP/MoS₂ composite has the best laser marking property when the MoS₂ loading content is 0.02 wt %, the laser marking current intensity is 11 A, and the laser marking speed is 800 mm/s, leading to a clear and high-contrast marking pattern.