Application potential of zero-valent aluminum in nitrophenols wastewater decontamination: Enhanced reactivity, electron selectivity and anti-passivation capability

Enhanced mineralization of nitrophenols by a novel C@ZVAl-PS based sequential reduction-oxidation process

Widely employed nitrophenols (NPs) are refractory and antioxidant due to their strong electron-withdrawing group (-NO2). Actually, NPs are readily reduced to aminophenols (APs). However, APs remain toxic and necessitate further treatment. Herein, we utilized a novel sequential reduction-oxidation system of carbon-modified zero-valent aluminum (C@ZVAl) combined with persulfate (PS) for the thorough removal of both NPs and APs. The results demonstrated that p-nitrophenol (PNP, up to 1000 mg/L) exhibited complete reduction to p-aminophenol (PAP), and then over 98.0 % of PAP could be effectively oxidized, in the meantime the removal rate of chemical oxygen demand (COD) was as high as 95.9 %. Based on the SEM and XPS characterizations, we found that C@ZVAl has exceptionally high reactivity that generates massive electrons and reduces PNP to PAP through accelerated electron transfer. In the subsequent oxidation step, PS can be rapidly activated by C@ZVAl to generate SO4- radicals for PAP oxidization. Meanwhile, the mineralization of COD proceeds. The temporal binding of reduction and oxidation can be regulated by varying the PS dosing time. Namely, the appropriate delay in PS dosing facilitates sufficient reduction to provide enough reactants for oxidation, favoring the mineralization of PNP and COD. More crucially, dinitrodiazophenol (DDNP) in an actual explosive wastewater without any pretreatment can be effectively mineralized by this sequential reduction-oxidation system, affirming the excellent performance of this process in practical applications. In conclusion, the C@ZVAl-PS based sequential reduction-oxidation looks very promising for enhanced mineralization of nitro-substituted organic contaminants.

Ball-milled biochar-modified zero-valent aluminum activates peroxodisulfate for phenol degradation: Enhancement of catalysis by membrane-breaking effect

Zero-valent aluminum (ZVAl) is a potential activator for peroxodisulfate (PDS), yet the dense oxide film on its surface hampers electron transfer for the O-O bond cleavage of PDS. We synthesized zero-valent aluminum-biochar (BM-ZVAl@BC) composites through ball milling, which effectively disrupted the native oxide layer on BM-ZVAl@BC. Within the BM-ZVAl@BC/PDS system, biochar (BC) not only suppressed the rapid oxidation of BM-ZVAl@BC but also enhanced the dispersion and electron transfer rate of ZVAl, thereby improving the overall catalytic efficiency. Consequently, the phenol removal efficacy in the BM-ZVAl@BC/PDS system was notably improved. Optimal catalytic performance of the prepared BM-ZVAl@BC was achieved at a charcoal-to‑aluminum mass ratio of 2:1, resulting in 95.7 % phenol removal after 180 min. Quenching experiments and electron paramagnetic resonance (EPR) analysis revealed that both free radicals (SO4•-, •OH, and O2•-) and non-radical species (1O2) contributed to phenol degradation, with SO4•- and •OH playing predominant roles. In summary, the BM-ZVAl@BC/PDS system represented an effective and promising technology for the remediation of phenolic water pollutants.

Rapid and effective removal of copper, nitrate and trichloromethane from aqueous media by aluminium alloys

Zero-valent iron (ZVI) has been extensively studied for its efficacy in removing heavy metals, nitrate, and chlorinated organic compounds from contaminated water. However, its limited effectiveness due to rapid passivation and poor selectivity is prompting for alternative solutions, such as the use of aluminium alloys. In this study, the efficacy of five distinct aluminium alloys, namely Al-Mg, Al-Fe, Al-Cu, and Al-Ni, each comprising 50 % Al by mass at a concentration of 10 g/L, was assessed using copper, nitrate and trichloromethane (TCM) as model contaminants. Results show that chemical pollutants reacted immediately with Al-Mg. On the contrary, the remaining three alloys exhibited a delay of 24 h before demonstrating significant reactivity. Remarkably, Al-Mg alloy reduced nitrate exclusively to ammonium, indicating minimal preference for nitrate reduction to N2. In contrast, the Al-Cu, Al-Ni, and Al-Fe alloys exhibited N2 selectivity of 3 %, 5 %, and 19 %, respectively. The removal efficiency of copper, nitrate and TCM reached 99 % within 24 h, 95 % within 48h and 48 % within 48h, respectively. Noteworthy findings included the correlation between Fe concentration within the Al-Fe alloy and an increased N2 selectivity from 9.3 % to 24.1 %. This resulted in an increase of Fe concentration from 10 % to 58 % albeit with a concurrent reduction in reactivity. Cu2+ removal by Al-Fe alloy occurred via direct electron transfer, while the removal of nitrate and TCM was facilitated by atomic hydrogen generated by the alloy's hydrolysis. Intriguingly, nitrate and TCM suppressed Cu2+ reduction, whereas Cu2+ improved nitrate reduction and TCM degradation. These findings demonstrate the great potential of Al-Mg and Al-Fe alloys as highly efficient agents for water remediation.