Transition metals Fe3+, Ni2+ modified titanium dioxide (TiO2) film sensors fabricated by CPT method to sense some toxic environmental pollutant gases

Sputtered Ultrathin TiO2 as Electron Transport Layer in Silicon Heterojunction Solar Cell Technology

This work presents the implementation of ultrathin TiO₂ films, deposited at room temperature by radio-frequency magnetron sputtering, as electron-selective contacts in silicon heterojunction solar cells. The effect of the working pressure on the properties of the TiO₂ layers and its subsequent impact on the main parameters of the device are studied. The material characterization revealed an amorphous structure regardless of the working pressure; a rougher surface; and a blue shift in bandgap in the TiO₂ layer deposited at the highest-pressure value of 0.89 Pa. When incorporated as part of the passivated full-area electron contact in silicon heterojunction solar cell, the chemical passivation provided by the intrinsic a-Si:H rapidly deteriorates upon the sputtering of the ultra-thin TiO₂ films, although a short anneal is shown to restore much of the passivation lost. The deposition pressure and film thicknesses proved to be critical for the efficiency of the devices. The film thicknesses below 2 nm are necessary to reach open-circuit values above 660 mV, regardless of the deposition pressure. More so, the fill-factor showed a strong dependence on deposition pressure, with the best values obtained for the highest deposition pressure, which we correlated to the porosity of the films. Overall, these results show the potential to fabricate silicon solar cells with a simple implementation of electron-selective TiO₂ contact deposited by magnetron sputtering. These results show the potential to fabricate silicon solar cells with a simple implementation of electron-selective TiO₂ contact.