Catalytic properties of barium modified Ru/MgZrO2 for the isomerization linoleic acid to conjugated linoleic acid

Regulating oxygen vacancies by Zn atom doping to anchor and disperse promoter Ba on MgO support to improve Ru-based catalysts activity for ammonia synthesis

In heterogeneous catalysis, surface defects are widely regarded as an effective means to enhance the catalytic performance of catalysts. In this study, the oxygen vacancy-rich Mg(1-X)ZnXO solid solution support was successfully prepared by doping a small amount of Zn into MgO nanocrystals. Based on this support, Ru/Ba-Mg(1-X)ZnXO catalyst for ammonia synthesis was prepared. Characterization using TEM, EPR, XPS, and DFT calculations confirmed the successful substitution of Zn atoms for Mg atoms leading to the formation of more oxygen vacancies (OVs). N2-TPD, SEM and TEM analyses revealed that a small amount of Zn had minimal influence on the surface morphology and the size of Ru nanoparticles. The abundance of OVs in the support was identified as the primary factor enhancing the catalytic activity. XPS, H2-TPD and kinetics experiment studies further elucidated the mechanism by which OVs promote the reaction, with OVs serving as an anchor point for the promoter Ba on the MgO support and promoted the dispersion of Ba. This anchoring effect not only enhanced the electron density on Ru, favoring the dissociation of the N[triple bond, length as m-dash]N bond, but also mitigated hydrogen poisoning. As a result,the ammonia synthesis rate reached 1.73 mmol g-1 h-1. Furthermore, the CO2-TPD and H2-TPR analyses indicated that Zn doping effectively promotes the metal-support interaction (MSI) and surface alkalinity. The findings of this study offers valuable insights for the design of defective modified catalyst supports.

Preparation of Conjugated Linoleic Acid by Ultrasound-assisted Nanonickel Catalyst Isomerization of Sunflower Oil

A homemade nanonickel catalyst was made by the ultrasonic liquid-phase reduction method, characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy, and applied to the isomerization reaction of high linoleic acid sunflower oil. Scanning electron microscopy (SEM), transmission electron microscopy (TEM) and particle size analysis showed that the homemade nickel particles were spherical, uniformly dispersed, less agglomerated, 20 to 75 nm in size, and nanoscale nickel powder. Compared with commercially available Raney nickel, the homemade nanonickel powder has a larger specific surface area, smaller pore size and higher catalytic activity. The X-ray diffraction spectrum of the homemade nanonickel powder had distinct diffraction peaks at its characteristic peaks which indicated that the powder was pure nickel. The nanometal nickel particles are fully dispersed in high oleic sunflower oil under the action of ultrasound. The results showed that it could effectively reduce the activation reaction time of nanonickel, and the conversion rate of conjugated linoleic acid could reach 86.24%. The process of activating the catalyst is omitted, the number of times of repeated uses of the nanonickel catalyst is increased, and the environmental pollution of the production is avoided. To obtain sunflower oil rich in CLA, it also provides a new idea for the preparation of conjugated linoleic acid.