Nanofibrous membranes with antibacterial and thermoregulatory functions fabricated by coaxial electrospinning

Preparation and Characterization of a One-Step Electrospun Poly(Lactic Acid)/Wormwood Oil Antibacterial Nanofiber Membrane

With the continuous improvement of the standard of living, people are increasingly inclined towards natural, green, and environmentally friendly products. Plant-based products that are safe, natural, non-toxic, and beneficial to human health are often more favored. Poly(lactic acid) (PLA) is a polymer obtained through lactate polymerization using renewable plant resources such as corn and has excellent biocompatibility and biodegradability. It is widely used in the field of food packaging. Wormwood oil (WO) is an oil extracted from the stems and leaves of Artemisia plants, and it has broad-spectrum antibacterial properties. In this article, through electrospinning technology, wormwood oil was directly incorporated into PLA, giving the PLA nanofiber membrane antioxidant and antibacterial functions. Various parameters such as voltage (11 KV, 13 KV, 15 KV), spinning solution concentration (8%, 10%, 12%), distance (15 cm, 17 cm, 19 cm), and feeding rate (0.4 mL/h, 0.5 mL/h, 0.6 mL/h) were explored, and the resulting spun fibers were characterized. Through SEM characterization, it was found that when the spinning voltage was 13 KV, the spinning solution concentration was 10%, the distance was 17 cm, and the feeding rate was 0.5 mL/h, the nanofiber membrane had a smooth morphology without bead formation, with an average diameter of 260 nm. The nanofiber membrane was characterized using FTIR, TG, and SEM, confirming the successful incorporation of artemisia essential oil into PLA. The prepared antimicrobial nanofilm was subjected to antimicrobial testing, and the results showed that as the concentration of the essential oil increased, the inhibition zones also increased. When wormwood oil concentration was 4%, the diameter of the inhibition zone for Staphylococcus aureus increased from 1.0 mm to 3.5 mm, while the diameter of the inhibition zone for Escherichia coli increased from 2.0 mm to 4.5 mm.

Hypericum perforatum Oil and Vitamin A Palmitate-Loaded Gelatin Nanofibers Cross-Linked by Tannic Acid as Wound Dressings

Recent studies in wound dressing applications offer new therapies to promote the wound healing process. The main strategy of this study is to combine the traditional perspective of using medicinal oils with polymeric scaffolds manufactured by an engineering approach to fabricate a potential tissue engineering product that provides both new tissue formation and wound healing. Thus, Hypericum perforatum oil (HPO) and vitamin A palmitate (VAP) incorporated gelatin (Gt) nanofibrous scaffolds were successfully prepared by the electrospinning method. Tannic acid (TA) was used as the cross-linking agent. The amounts of VAP and HPO loaded in the base Gt solution [15% w/v in 4:6 v/v acetic acid/deionized water] were 5 and 50 wt % (based on the weight of Gt), respectively. The obtained scaffolds were studied regarding their microstructure, chemical structure, thermal stability, antibacterial activity, in vitro release study, and cellular proliferation assay. In the light of these studies, it was determined that VAP and HPO were incorporated successfully in Gt nanofibers cross-linked with TA. Release kinetic tests confirmed that the patterns of TA and VAP release were consistent with the Higuchi model, whereas HPO release was consistent with the first-order kinetic model. In addition, this membrane was biocompatible with L929 fibroblast cells and had antibacterial activity and thermal stability. This preliminary study suggests potential applicability of the proposed dressing to treat skin wounds in clinics.